Cobalt promoted Ni/MgAl2O4 catalyst in lean methane catalytic oxidation

In the present research, magnesium aluminate spinel was prepared as catalyst support using a novel, facile, and efficient mechanochemical method. The Co-promoted catalysts with 20 wt.% of Ni were fabricated using an impregnation route and the samples were analyzed by the X-ray diffraction (XRD), N₂ adsorption/desorption (BET), temperature-programmed reduction and desorption (H₂-TPR and O₂-TPD), and field emission scanning electron microscopy (FESEM) tests. The results confirmed that all samples have a mesoporous structure with a high specific surface area and the presence of cobalt caused complete CH₄ oxidation at low temperatures, and no side reactions were observed. The results indicated that the 3%Co-20%Ni/MgAl₂O₄ catalyst was the optimal sample among the prepared catalysts, owing to the improvement of reduction features and oxygen mobility. The 50 and 90% of methane conversion was obtained at 530 and 600 °C, respectively. Also, the influence of calcination temperature, GHSV, and feed ratio was determined on the catalytic activity. The obtained outcomes revealed that the calcination temperature has a significant effect on the textural properties and catalytic efficiency. The sample calcined at 700 °C showed the weakest performance, which was related to the sintering of particles at high temperatures. The catalytic stability showed that the 3%Co-20%Ni/MgAl₂O₄ has acceptable stability during 600 min time of reaction.

Graphical abstract

     

One Way Traffic: Base-to-Backbone Hole Transfer in Nucleoside Phosphorodithioate

The directionality of the hole-transfer processes between DNA backbone and base was investigated by using phosphorodithioate [P(S⁻)=S] components. ESR spectroscopy in homogeneous frozen aqueous solutions and pulse radiolysis in aqueous solution at ambient temperature confirmed initial formation of G^.+-P(S⁻)=S. The ionization potential of G-P(S⁻)=S was calculated to be slightly lower than that of guanine in 5′-dGMP. Subsequent thermally activated hole transfer from G^.+ to P(S⁻)=S led to dithiyl radical (P-2S^.) formation on the μs timescale. In parallel, ESR spectroscopy, pulse radiolysis, and density functional theory (DFT) calculations confirmed P-2S^. formation in an abasic phosphorodithioate model compound. ESR investigations at low temperatures and higher G-P(S⁻)=S concentrations showed a bimolecular conversion of P-2S^. to the σ²-σ*¹-bonded dimer anion radical [-P-2S 2S-P-]⁻ [ΔG (150 K, DFT)=−7.2 kcal mol⁻¹]. However, [-P-2S 2S-P-]⁻ formation was not observed by pulse radiolysis [ΔG° (298 K, DFT)=−1.4 kcal mol⁻¹]. Neither P-2S^. nor [-P-2S 2S-P-]⁻ oxidized guanine base; only base-to-backbone hole transfer occurs in phosphorodithioate.     

CH_4 reforming with CO_2 for syngas production over La_2O_3 promoted Ni catalysts supported on mesoporous nanostructured γ-Al_2O_3

Nanostructured γ-Al2O3 with high surface area and mesoporous structure was synthesized by sol-gel method and employed as catalyst support for nickel catalysts in methane reforming with carbon dioxide. The prepared samples were characterized by XRD, N2adsorption-desorption,TPR, TPO, TPH, NH3-TPD and SEM techniques. The BET analysis showed a high surface area of 204 m2 g-1and a narrow pore-size distribution centered at a diameter of 5.5 nm for catalyst support. The BET results revealed that addition of lanthanum oxide to aluminum oxide decreased the specific surface area. In addition, TPR results showed that addition of lanthanum oxide increased the reducibility of nickel catalyst. The catalytic evaluation results showed an increase in methane conversion with increasing lanthanum oxide to 3 mol% and further increase in lanthanum content decreased the catalytic activity. TPO analysis revealed that the coke deposition decreased with increasing lanthanum oxide to 3 mol%. SEM and TPH analyses confirmed the formation of whisker type carbon over the spent catalysts. Addition of steam and O2 to dry reforming feed increased the methane conversion and led to carbon free operation in combined processes.     

Mechanistic insight into the hydrogenation of acetylene on the Pd2/g-C3N4 catalyst: effect of Pd clustering on the barrier energy and selectivity

Structural Chemistry - In this work, the hydrogenation of acetylene on the Pd2/g-C3N4 catalyst is investigated by the density functional theory (DFT) and quantum theory of atoms in molecules...     

Antibacterial and wound healing activities of silver nanoparticles embedded in cellulose compared to other polysaccharides and protein polymers

Cellulose - The aggregation of silver nanoparticles (AgNPs) in colloidal solution and the oxidative cytotoxicity towards human cells are two major hindrances for their thriving medicinal...