不同工艺和原料对Mn_(1.2)Fe_(0.8)P_(0.48)Si_(0.52)化合物磁热效应的影响

用不同的工艺和原料制备了3个名义成分相同的Mn1.2Fe0.8P0.48S i0.52化合物。X射线衍射结果表明,3个化合物均为Fe2P型六角结构(空间群为P-62m),并且存在少量的(Fe,Mn)3S i相。通过磁性测量发现,3个样品的居里温度有所不同,但是都在室温附近(270~290 K)。以Fe2P为原料制备的化合物具有较大的磁熵变,在1.5 T的磁场变化下其最大磁熵变为13.6 J.(kg.K)-1。以行星样品球磨机制备的化合物具有较小的热滞,最小热滞为6.7 K。这些表明不同的制备工艺和原料对化合物的居里温度、热滞和磁熵变都具有一定的影响。同时低成本的原料、简单的制备工艺、较小的热滞和较大的磁熵变使得Mn1.2Fe0.8P0.48S i0.52化合物成为一种理想的室温磁致冷候选材料。     

Magnetocaloric effects in Mn1.35Feo.65P1-xSix compounds

The structural and magnetocaloric properties of Mn1.35Fe0.65P1-xSix compounds are investigated.The Sisubstituted compounds,Mn1.35Fe0.65P1-xSix with x = 0.52,0.54,0.55,0.56,and 0.57,are prepared by high-energy ball milling and the solid-state reaction.The X-ray diffraction shows that the compounds crystallize into the Fe 2 P-type hexagonal structure with space group P■2m.The magnetic measurements show that the Curie temperature of the compound increases from 253 K for x = 0.52 to 296 K for x = 0.56.The isothermal magnetic-entropy change of the Mn1.35Fe0.65P1-xSix compound decreases with the Si content increasing.The maximal value of the magnetic-entropy change is about 7.0 J/kg·K in the Mn1.35Fe0.65P0.48Si0.52 compound with a field change of 1.5 T.The compound quenched in water possesses a larger magnetic entropy change and a smaller thermal hysteresis than the non-quenched samples.The thermal hysteresis of the compound is less than 3.5 K.The maximum adiabatic temperature change is about 1.4 K in the Mn1.35Fe0.65P0.45Si0.55 compound with a field change of 1.48 T.     

面心立方固溶体合金的团簇加连接原子几何模型及典型工业合金成分解析

工业合金牌号的成分选择体现了固溶体合金的化学短程有序结构,满足由最近邻两层原子组成的"团簇加连接原子"模型,例如对于置换型面心立方固溶体Cu-Zn,其合金牌号成分可以表述为[Zn-Cu_(12)]Zn_(1-6)和[Zn-Cu_(12)](Cu,Zn)_6,其中方括号内为第一近邻配位多面体团簇.基于此,本文赋予团簇式以具体原子结构的含义,对置换型面心立方固溶体结构中团簇的可能存在形式进行了穷尽,得出团簇式所对应的所有"团簇加连接原子"结构单元模型,给出团簇和连接原子之间的比例和空间排列的所有可能,并对Cu-Zn和Cu-Ni合金常用牌号对应的团簇式给出了三维结构模型,进一步验证了前期关于合金团簇式解析的正确性.用这些模型中原子化学序描述合金的成分,赋予团簇式以具体的原子结构意义,为进一步开发新的合金提供了理论依据.     

Magnetocaloric effects in Mn1.35Fe0.65P1-xSix compounds

The structural and magnetocaloric properties of Mn_1.35Fe_0.65P_1-xSi_x compounds are investigated. The Si-substituted compounds, Mn_1.35Fe_0.65P_1-xSi_x with x = 0.52, 0.54, 0.55, 0.56, and 0.57, are prepared by high-energy ball milling and the solid-state reaction. The X-ray diffraction shows that the compounds crystallize into the Fe₂P-type hexagonal structure with space group P62m. The magnetic measurements show that the Curie temperature of the compound increases from 253 K for x = 0.52 to 296 K for x = 0.56. The isothermal magnetic-entropy change of the Mn_1.35Fe_0.65P_1-xSi_x compound decreases with the Si content increasing. The maximal value of the magnetic-entropy change is about 7.0 J/kg稫 in the Mn_1.35Fe_0.65P_0.48Si_0.52 compound with a field change of 1.5 T. The compound quenched in water possesses a larger magnetic entropy change and a smaller thermal hysteresis than the non-quenched samples. The thermal hysteresis of the compound is less than 3.5 K. The maximum adiabatic temperature change is about 1.4 K in the Mn_1.35Fe_0.65P_0.45Si_0.55 compound with a field change of 1.48 T.