Wet thermal annealing effect on TaN/HfO2/Ge metal-oxide-semiconductor capacitors with and without a GeO2 passivation layer

Wet thermal annealing effects on the properties of TaN/HfO2/Ge metal-oxide-semiconductor(MOS) structures with and without a GeO2 passivation layer are investigated.The physical and the electrical properties are characterized by X-ray photoemission spectroscopy,high-resolution transmission electron microscopy,capacitance-voltage(C-V) and current-voltage characteristics.It is demonstrated that wet thermal annealing at relatively higher temperature such as 550℃ can lead to Ge incorporation in HfO2 and the partial crystallization of HfO2,which should be responsible for the serious degradation of the electrical characteristics of the TaN/HfO2/Ge MOS capacitors.However,wet thermal annealing at 400℃ can decrease the GeO x interlayer thickness at the HfO2/Ge interface,resulting in a significant reduction of the interface states and a smaller effective oxide thickness,along with the introduction of a positive charge in the dielectrics due to the hydrolyzable property of GeO x in the wet ambient.The pre-growth of a thin GeO2 passivation layer can effectively suppress the interface states and improve the C-V characteristics for the as-prepared HfO2 gated Ge MOS capacitors,but it also dissembles the benefits of wet thermal annealing to a certain extent.     

金属与半导体Ge欧姆接触制备、性质及其机理分析

金属与Ge材料接触时界面处存在着强烈的费米钉扎效应, 尤其与n型Ge形成的欧姆接触的比接触电阻率高, 是制约Si基Ge器件性能的关键因素之一. 本文对比了分别采用金属Al和Ni 与Si衬底上外延生长的p型Ge和n型Ge材料的接触特性. 发现在相同的较高掺杂条件下, NiGe与n型Ge可形成良好的欧姆接触, 其比接触电阻率 较 Al接触降低了一个数量级, 掺P浓度为2×10¹⁹ cm^-3时达到1.43×10^-5 Ω·cm². NiGe与p型Ge接触和Al接触的比接触电阻率相当, 掺B浓度为4.2×10¹⁸ cm^-3时达到1.68×10^-5 Ω·cm². NiGe与n型Ge接触和Al电极相比较, 在形成NiGe过程中, P杂质在界面处的偏析是其接触电阻率降低的主要原因. 采用NiGe作为Ge的接触电极在目前是合适的选择. 关键词： 金属与Ge接触性质 NiGe 比接触电阻率