下电极对ZnO薄膜电阻开关特性的影响

本文采用直流磁控溅射法在三种不同的下电极(BEs)上制备了ZnO薄膜, 获得了W/ZnO/BEs存储器结构. 研究了不同的下电极材料对器件电阻开关特性的影响. 研究结果表明, 以不同下电极所制备的器件都具有单极性电阻开关特性. 在低阻态时, ZnO薄膜的导电机理为欧姆传导, 而高阻态时薄膜的导电机理为空间电荷限制电流. 不同下电极与ZnO薄膜之间的肖特基势垒高度对电阻开关过程中的操作电压有较大的影响, 并基于导电细丝模型对不同下电极上ZnO薄膜的低阻态阻值及reset电流的变化进行了解释. 关键词： ZnO薄膜 电阻开关 下电极     

Centimetre-Long Single Crystalline ZnO Fibres Prepared by Vapour Transportation

Centimetre-long ZnO fibres are synthesized by vapour transportation via thermal evaporation of ZnO powders. The growth process is carried out in a graphite crucible, in which ZnO powder is loaded as the source material, and a silicon wafer is positioned on the top of the crucible as the growth substrate. During the growth process, the source temperature is kept at 800℃ and the substrate temperature is kept at 600℃. Typical growth time to obtain centimetre-long ZnO fibres is 5-10 hours. Scanning electron microscopy （SEM）, x-ray diffraction （XRD）, transmission electron microscopy （TEM）, and selected area electron diffraction （SAED） measurement results show that ZnO fibres are single crystalline with high crystalline quality and very low defects concentration.     

衬底温度对直流反应磁控溅射法制备的N掺杂p型ZnO薄膜性能的影响

利用直流反应磁控溅射法(纯金属锌作为靶材,Ar-N2-O2混合气体作为溅射气体)在石英玻璃衬底上制备了N掺杂p型ZnO薄膜.通过XRD、Hall和紫外可见透射谱分别研究了衬底温度对ZnO薄膜结构性能、电学性能和光学性能的影响.XRD结果显示所有制备的薄膜都具有垂直于衬底的c轴择优取向,并且随着衬底温度的增加,薄膜的晶体质量得到了提高.Hall测试表明衬底温度对p型ZnO薄膜的电阻率具有较大影响,400℃下生长的p型ZnO薄膜由于具有较高的迁移率(1.32 cm2/Vs)和载流子浓度(5.58×1017cm-3),因此表现出了最小的电阻率(8.44Ω·cm).