聚苯胺膜的磁学性能

本文讨论聚苯胺自支撑膜的电子自旋共振(ESR)和磁学性能与成膜、拉伸处理以及质子掺杂等因素的影响,实验结果表明,聚苯胺膜的磁学性能与它的粉末样品相似,其磁化率表现为与温度无关的泡利型顺磁性和符合居里定律的顺磁性之和,质子掺杂后,其磁学性能也随绝缘体-半导体-金属态相变而变化,并且质子掺杂后自旋密度的增加符合“质子化导致自旋不成对”的机理,拉伸后的聚苯胺的泡利自旋和居里自旋均比其粉末和薄膜样品明显提高,这可能是由于拉伸取向增强了聚苯胺链上醌环上氮原子上弧对电子间的相互作用所致。 关键词：     

FREE STANDING FILM OF POLYANILINE

A free standing film of polyaniline as large as 18 cm×18cm×0.002 cm can be obtained by evaporation of a solution of the chemically synthesized base in NMP. Its structure was examined by the elemental analysis, IR, U.V.-visible spectra, XPS, DSC, SEM and X-ray scattering and its conducting behavior as well as electrochemical properties were studied. Results show that the composition, structure of main chain, physical properties of the free standing film of polyanilme is similar to that of the powder. However, some differences in its electronic structure, conductivity at room temperature and potential of redox couple between the flee standing film and powder are observed, which may be due to cross-linking of the film of polyaniline.     

STUDIES ON THE ELECTRICAL CONDUCTIVITY OF FREE-STANDING FILMS OF POLYANILINE

An insulate to metal transition was investigated based on the measurements of the dependence of the conductivity, activation energy on the protonation state of polyaniline (PANI). An isotropy in conductivity for stretched salt form of PANI was observed.For salt film of PANI, the Ⅰ-Ⅴcurve obeys Ohm's law, which shows a typical metal behavior, however, for base film or film with low protonation state, it can be explained by Space Charge Limited Current (SCLC). It is also found that the Ⅰ-Ⅴcurve of base film of PANI is independent of the work function of electrodes and the polymerization temperature.     

TS单晶体及其聚合物PTS的介电和动态力学行为

<正> 聚丁二炔类宏观单晶体以其极大的尺寸,完整性和立体规整的共轭主链,为我们提供了一个准一维体系模型化合物。它们的电性能,非线性光学性能及形成聚合LB膜的能力等具有潜在的应用前景,近年来研究工作非常活跃。丁二炔类化合物中最能培养咸大晶体,从而研究得最多的是双(对甲苯磺酸)-2,4-己二炔-1,6-二醇酯(TS)及其聚合物PTS。我们先后测量过它们的热电势率、电导、膨胀系数、介电性能、光声效