35kJ直接冷却高温超导储能磁体

介绍了直接冷却高温超导储能磁体的基本结构,分析了磁体的电磁特性,分析结果表明,磁体电磁设计中采用端部两对饼并联的方式,削弱了磁体端部磁场径向分量,提高临界电流,磁体表现了较好的电磁特性;仿真了磁体与电力系统进行功率交换时的热特性,仿真结果与实验结果两者温度变化总体趋势是一致的;介绍了磁体的冷却实验和磁体系统的动态模拟实验结果.实验结果表明磁体的冷却措施和低温系统的冷却方案是可行的,磁体具有较好的热稳定性.     

Magnetization study of ITER-type internal-Sn Nb3Sn superconducting wire

Through magnetization measurement with a SQUID magnetometer the heat treatment optimization of an international thermonuclear experimental reactor （ITER）-type internal-Sn Nb3Sn superconducting wire has been investigated. The irreversibility temperature T^＊ （H）, which is mainly dependent on A15 phase composition, was obtained by a warming and cooling cycle at a fixed field. The hysteresis width △M（H） which reflects the flux pinning situation of the A15 phase is determined by the sweeping of magnetic field at a constant temperature. The results obtained from differently heat-treated samples show that the combination of T^＊ （H） with AM（H） measurement is very effective for optimizing the heat reaction process. The heat treatment condition of the ITER-type wire is optimized at 675℃/128 h, which results in a composition closer to stoichiometric Nb3Sn and a state with best flux pinning.     

ITER用内锡法Nb3Sn超导线材的不可逆温度研究

本文采用超导量子干涉仪(SQUID)测定了一种国际热核聚变实验堆(ITER)项目用内锡法Nb3Sn超导线材的不可逆温度,测量方法是在恒定磁场下循环温度,即将温度以一定间隔从10K上升到20K,然后再返回到10K,测定磁矩的偏离温度.所得结果可用于从生成最佳Nb-Sn相组成方面来优化A15相成相热处理制度.本研究得出的结论是,对于像ITER使用的高场磁体超导线来说,鉴于其需要在较高磁场下有高的临界电流密度,就需要将超导线的热处理温度适当提高一些.本实验所用Nb3Sn超导线材的最适宜热处理制度为675°C/128小时,这样可以得到最佳不可逆温度特性,即最佳的A15相组成.     

内锡法Nb_3 Sn超导线材的A15相成相动力学研究(英文)

为研究Nb3Sn超导材料的A15相成相动力学,设计并制备了四组单组元内锡法(MEIT)超导线.这四组MEIT导线设计了不同的Sn/Cu比,并在一组导线中合金化掺杂了1at%Zr,,所有导线样品先经历210℃/50hr+340℃/25kr的Cu-Sn合金化热处理,然后进行A15相成相热处理.选择四种反应温度:650℃,675℃,700℃和725℃,以研究成相热处理温度和时间的影响.用SEM技术测定所有热处理样品的A15相层厚,然后对不同温度下的热处理时间作图,并进行非线性拟合.所得结果表明四种因素促进了A15相的增长:增加反应温度,延长反应时间,增大Sn/Cu比率和合金化掺杂zr;内锡法Nb,sn超导线材的成相动力学服从Yn=K(T)t变化关系,A15相生长指数n值受热处理温度和Zr掺杂的影响.