Nano-tribological study on a super-hydrophobic film formed on rough aluminium substrates

A novel super-hydrophobic stearic acid (STA) film with a water contact angle of 166^o was prepared by chemical adsorption on aluminum wafer coated with polyethyleneimine (PEI) film. The micro-tribological behavior of the super-hydrophobic STA monolayer was compared with that of the polished and PEI-coated Al surfaces. The effect of relative humidity on the adhesion and friction was investigated as well. It was found that the STA monolayer showed decreased friction, while the adhesive force was greatly decreased by increasing the surface roughness of the Al wafer to reduce the contact area between the atomic force microscope (AFM) tip and the sample surface to be tested. Thus the friction and adhesion of the Al wafer was effectively decreased by generating the STA monolayer, which indicated that it could be feasible and rational to prepare a surface with good adhesion resistance and lubricity by properly controlling the surface morphology and the chemical composition. Both the adhesion and friction decreased as the relative humidity was lowered from 65% to 10%, though the decrease extent became insignificant for the STA monolayer. The project supported by the National Natural Science Foundation of China (50375151, 50323007, 10225209) and the Chinese Academy of Sciences (KJCX-SW-L2)     

不同阴离子插层双金属氢氧化物的制备及摩擦学性能研究

本研究中利用尿素分解法、盐酸–氯化钠混合溶液法及离子交换法得到了一系列不同阴离子插层的层状双金属氢氧化物(Co-Al LDH)材料,利用傅立叶变换红外光谱仪、X射线衍射仪及扫描电子显微镜对它们的化学组成、晶体结构及颗粒形貌进行了分析表征.利用SRV-1型微动摩擦试验机对含有不同阴离子插层LDH的PAO-8润滑油(质量分数为0.1%)的摩擦学性能进行了研究,证明LDH材料的少量添加即可显著提高PAO-8在高载荷(150 N)下的摩擦学性能,同时也发现插层阴离子的种类对LDH摩擦学性能的影响具有明显差异性.     

尖晶石型NiCr2O4的燃烧法合成及表征

通过溶胶-凝胶燃烧法制备了具有立方相的尖晶石型NiCr2O4颜料,并采用TG/DSC、XRD、FTIR和SEM等手段对其进行表征和研究。结果表明:将燃烧后的粉末于900℃下煅烧2 h可以得到单一相的NiCr2O4,温度达不到900℃时所得粉末(包括燃烧后粉末和500和700℃煅烧得到的粉末)为NiO和Cr2O3组成的混合物。利用紫外/可见/近红外分光光度计仔细研究了燃烧后粉末和煅烧后粉末的颜色参数。尽管具有相同的成分,500和700℃下煅烧得到的粉末与燃烧后粉末却具有明显不同的颜色,这可从一氧化镍为非整比化合物的角度加以解释。此外,900和1 000℃下煅烧得到的NiCr2O4粉末呈现出随温度变化的绿色。     

MOSi2及其复合材料摩擦学性能研究

通过热压烧结制备了MoSi2及3种MoSi2基复合材料，考察了其相组成和结构，测定了其硬度和断裂韧性，评价了其摩擦磨损行为，并探讨了力学性能、摩擦界面特性和偶件材料特性等对MoSi2及其复合材料摩擦学行为的影响．结果表明：MoSi2同GCrl5钢和WC-Co硬质合金配副时表现出较高的摩擦系数，其磨损强烈依赖于偶件材料特性；第二相的引入对MoSi2的磨损行为具有显著影响，其中SiC第二相可以改善MoSi2的摩擦磨损性能；摩擦界面特性和偶件材料特性则对MoSi2及其复合材料的摩擦磨损性能具有决定性影响．     

绿色润滑油的发展概况

概述了绿色润滑油的发展状况,阐述了绿色润滑油的含义,阐述了绿色润滑油的含义,介绍了生物降解试验方法,通过对绿色润滑油基础油及基适用的添加剂的综述,提出了绿色润滑油发展过程中存在的主要问题,并对将来的发展趋势进行了展望。     

牙科用抗菌性义齿基托材料的摩擦磨损性能研究

在UMT-2MT型摩擦磨损试验机上,采用往复运动形式考察了牙科用抗菌性义齿基托材料的摩擦磨损性能,探讨在干摩擦和人工唾液润滑状态下抗菌性义齿基托材料的摩擦磨损性能.结果表明:在干摩擦条件下,随着抗菌剂含量的增加,义齿基托的摩擦系数逐渐升高,磨损深度逐渐减小,其磨损机制由粘着磨损和疲劳磨损共存转变为以疲劳磨损为主;在人工唾液环境中,抗菌剂含量对于义齿基托摩擦系数的影响并不明显,磨损深度随抗菌剂含量的增加明显减小,这可能与聚合物表面吸附水并形成保护膜有关,其磨损机制与干摩擦情况下基本一致.综合考虑不同比例抗菌剂对其摩擦磨损性能的影响,结合以前的抗菌性试验,抗菌剂的最佳添加量为2%.     

单晶硅滑动磨损性能及其相变研究

考察了单晶硅在室温和低接触应力条件下的摩擦磨损行为随速度的变化情况．结果表明，单晶硅的摩擦系数和磨损率随滑动速度的提高而呈现降低趋势；单品硅在低速、短滑动时间下的磨损表面形貌特征以微断裂为主，并伴有一定程度的塑性变形;随着滑动时间的延长，塑性变形特征逐渐减弱，塑性变形同具有金属延性特征的p—Sn(简称si—II)相密切相关，Si—II在滑动过程中可转变为体心立方结构(简称Si-III)、斜方六面体结构(简称Si—XII)和非晶硅相;在高速条件下，单晶硅磨损表面呈现微断裂和较弱的塑性变形特征；尽管通过Raman分析证实磨损表面存在si—III相，但其对磨损机制的影响有待于进一步研究．     

离子注入聚酰亚胺的摩擦磨损性能研究

用Ｎ＋和Ｆｅ＋分别对芳香聚酰亚胺薄膜进行了离子注入处理，考察了注入前后聚酰亚胺与５２１００钢对摩时的摩擦磨损性能．结果表明，这２种离子注入都可以降低聚酰亚胺与钢对摩时的摩擦系数和磨损，而且高剂量（１０１６ｉｏｎｓ／ｃｍ２量级）离子注入的效果比低剂量（１０１４ｉｏｎｓ／ｃｍ２量级）离子注入的好，尤以３×１０１６ｉｏｎｓ／ｃｍ２的Ｆｅ＋注入改性作用更好     

摩擦偶件对单晶硅宏观摩擦磨损行为的影响

研究了单晶硅分别与Si3N4、红宝石及GCr15钢对摩时的摩擦磨损性能.结果表明:单晶硅与不同偶件对摩时的摩擦系数均随着滑动速度的提高而降低;在相同试验条件下,单晶硅与GCr15钢对摩时的摩擦系数最高,这主要是由于单晶硅与GCr15钢中的过渡金属元素Fe具有很强的化学亲合势所致;而单晶硅与红宝石对摩时的磨损体积损失最大,与GCr15钢对摩时的磨损体积损失最小;低速下Si3N4和红宝石陶瓷偶件与单晶硅对摩时磨损表面存在大量的微断裂,随着滑动速度的增加其磨损表面逐渐变得较为光滑;GCr15钢与单晶硅对摩初期向单晶硅表面转移,在随后的摩擦过程中转移层因磨损而被去除,故单晶硅/GCr15钢磨损表面比其他2种摩擦副的磨损表面光滑.     

ZrO_2/rGO多层复合薄膜的构筑及其摩擦学性能研究

将层层自组装(LBL)技术与原位还原过程相结合在单晶硅片表面成功构筑了与基底结合牢固、性能优异的氧化锆/还原氧化石墨烯(ZrO2/rGO)多层纳米复合薄膜.试验中,引入了具有强附着性和还原性的物质-多巴胺,使得氧化石墨烯(GO)片的表面锚固和原位还原可以一步完成.另外,ZrO2粒子的表面组装通过简单、温和的溶液沉积过程来实现.结果证明:复合薄膜中rGO和ZrO2的引入以及多层结构的构筑赋予复合薄膜许多优异的性能.在不进行热处理的情况下,所构筑的ZrO2/rGO多层薄膜表现出优异的力学性能(硬度:11.54 GPa)和摩擦学性能(摩擦系数:0.12~0.17),可作为减摩抗磨涂层被用于微/纳机电系统(MEMS/NEMS)的表面保护和其他领域.