Fabrication of highly porous interconnected three-dimensional scaffolds with micro-channels

A novel highly porous 3-D poly(ε-caprolactone)(PCL) scaffold with micro-channels was fabricated by injection molding and diluent acetic acids leaching technologies. In this study, the chitosan fiber was employed to form the microchannel in PCL matrix. The morphology, porosity and mechanical properties of the scaffolds were studied and calculated. It was found that the larger the content of chitosan fiber is, the higher the porosity would be, due to the volumetric expansion of chitosan fiber in PCL matrix during it being leached. In addition, the less the content of chitosan fiber is, the higher the compressive modulus would be.     

Nanofibrillated cellulose (NFC) reinforced polyvinyl alcohol (PVOH) nanocomposites: properties, solubility of carbon dioxide, and foaming

Polyvinyl alcohol (PVOH) and its nanofibrillated cellulose (NFC) reinforced nanocomposites were produced and foamed and its properties—such as the dynamic mechanical properties, crystallization behavior, and solubility of carbon dioxide (CO₂)—were evaluated. PVOH was mixed with an NFC fiber suspension in water followed by casting. Transmission electron microscopy (TEM) images, as well as the optical transparency of the films, revealed that the NFC fibers dispersed well in the resulting PVOH/NFC nanocomposites. Adding NFC increased the tensile modulus of the PVOH/NFC nanocomposites nearly threefold. Differential scanning calorimetry (DSC) analysis showed that the NFC served as a nucleating agent, promoting the early onset of crystallization. However, high NFC content also led to greater thermal degradation of the PVOH matrix. PVOH/NFC nanocomposites were sensitive to moisture content and dynamic mechanical analysis (DMA) tests showed that, at room temperature, the storage modulus increased with decreasing moisture content. The solubility of CO₂ in the PVOH/NFC nanocomposites depended on their moisture content and decreased with the addition of NFC. Moreover, the desorption diffusivity increased as more NFC was added. Finally, the foaming behavior of the PVOH/NFC nanocomposites was studied using CO₂ and/or water as the physical foaming agent(s) in a batch foaming process. Only samples with a high moisture content were able to foam with CO₂. Furthermore, the PVOH/NFC nanocomposites exhibited finer and more anisotropic cell morphologies than the neat PVOH films. In the absence of moisture, no foaming was observed in the CO₂-saturated neat PVOH or PVOH/NFC nanocomposite samples.