Chemical diffusion in calcium titanate

This work reports the gas/solid equilibration kinetics for the O₂/CaTiO₃ system. The electrical conductivity measurement was applied for monitoring the kinetics in the ranges of temperature 973-1323 K and oxygen partial pressure 10 Pa-72 kPa. It was found that the gas/solid equilibration kinetics for the polycrystalline CaTiO₃ specimen in the above experimental conditions is determined by bulk diffusion rather than by grain boundary conditions. The obtained data of the electrical conductivity vs. time were used for the determination of the chemical diffusion coefficient as a function of temperature at low and high p(O₂), respectively:

(1)     

Charge Transfer Between Oxygen and Zirconia

The extent of the surface charge, that develops during oxidation of zirconia, is determined using work function measurements for both bulk specimen and thin films. The bulk specimen of yttria-doped zirconia (10 mol%) exhibits maxima of the surface electrical effect at 373 and 973 K (130 and 280 mV, respectively) that can be considered in terms of oxygen chemisorption and oxygen non-stoichiometry. Thin film of undoped zirconia exhibits a maximum at 473 K (260 eV). Addition of yttria (10 mol%) to the thin film results in a substantial reduction of the maximum, to about 140 eV, that is shifted up to 600 K.This revised version was published online in November 2005 with corrections to the Cover Date.