Synthesis of Small‐Sized,Porous, and Low‐Toxic Magnetite Nanoparticles by Thin POSS Silica Coating

In this communication, we report the synthesis of small‐sized (<10 nm), water‐soluble, magnetic nanoparticles (MNPs) coated with polyhedral oligomeric silsesquioxanes (POSS), which contain either polyethylene glycol (PEG) or octa(tetramethylammonium) (OctaTMA) as functional groups. The POSS‐coated MNPs exhibit superparamagnetic behavior with saturation magnetic moments (51–53 emu g^?1) comparable to silica‐coated MNPs. They also provide good colloidal stability at different pH and salt concentrations, and low cytotoxicity to MCF‐7 human breast epithelial cells. The relaxivity data and magnetic resonance (MR) phantom images demonstrate the potential application of these MNPs in bioimaging.     

A model for crack formation during active solid pyrolysis of a char-forming solid: crack patterns; surface area generation; volatile mass efflux

A model is developed for the formation and propagation of cracks in a material sample that is heated at its top surface, pyrolyses, and then thermally degrades to form char. In this work the sample is heated uniformly over its entire top surface by a hypothetical flame (a heat source). The pyrolysis mechanism is described by a one-step overall reaction that is dependent nonlinearly on the temperature (Arrhenius form). Stresses develop in response to the thermal degradation of the material by means of a shrinkage strain caused by local mass loss during pyrolysis. When the principal stress exceeds a prescribed threshold value, the material forms a local crack. Cracks are found to generally originate at the surface in response to heating, but occasionally they form in the bulk, away from ever-changing material boundaries. The resulting cracks evolve and form patterns whose characteristics are described. Quantities examined in detail are: the crack spacing in the pyrolysis zone; the crack length evolution; the formation and nature of crack loops which are defined as individual cracks that have joined to form loops that are disconnected from the remaining material; the formation of enhanced pyrolysis area; and the impact of all of the former quantities on mass flux. It is determined that the mass flux from the sample can be greatly enhanced over its nominal (non-cracking) counterpart. The mass efflux profile qualitatively resembles those observed in Cone Calorimeter tests.     

Influence of solvents on the formation of ultrathin uniform poly(vinyl pyrrolidone) nanofibers with electrospinning

Although there have been many reports on the preparation and applications of various polymer nanofibers with the electrospinning technique, the understanding of synthetic parameters in electrospinning remains limited. In this article, we investigate experimentally the influence of solvents on the morphology of the poly(vinyl pyrrolidone) (PVP) micro/nanofibers prepared by electrospinning PVP solution in different solvents, including ethanol, dichloromethane (MC) and N,N‐dimethylformamide (DMF). Using 4 wt % PVP solutions, the PVP fibers prepared from MC and DMF solvents had a shape like a bead‐on‐a‐string. In contrast, smooth PVP nanofibers were obtained with ethanol as a solvent although the size distribution of the fibers was somewhat broadened. In an effort to prepare PVP nanofibers with small diameters and narrow size distributions, we developed a strategy of using mixed solvents. The experimental results showed that when the ratio of DMF to ethanol was 50:50 (w/w), regular cylindrical PVP nanofibers with a diameter of 20 nm were successfully prepared. The formation of these thinnest nanofibers could be attributed to the combined effects of ethanol and DMF solvents that optimize the solution viscosity and charge density of the polymer jet. In addition, an interesting helical‐shaped fiber was obtained from 20 wt % PVP solution in a 50:50 (w/w) mixed ethanol/DMF solvent. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 3721–3726, 2004     

Continuity of the Solution Map in Parametric Affine Variational Inequalities

A systematic study of the upper semicontinuity and the lower semicontinuity of the solution map in parametric affine variational inequalities is given in this paper. Several examples are constructed to analyze the results. This work was supported by Korea Research Foundation Grant (KRF 2001-015-DP0049), the APEC Postdoctoral Fellowships Program, and the KOSEF Brain Pool Program.     

Preparation and characterization of rigid poly(vinyl chloride)/MMT nanocomposites. II. XRD,morphological and mechanical characteristics

A Haake torque rheometer equipped with an internal mixer is used to study the influence of the amount of sodium montmorillonite (Na⁺‐MMT) and organically modified MMT (O‐MMT) on X‐ray diffraction (XRD), morphology, and mechanical characteristics of rigid poly (vinyl chloride) (PVC)/Na⁺‐MMT and PVC/O‐MMT nanocomposites, respectively. Results of XRD and transmission electron microscopy (TEM) indicate that MMT is partially encapsulated and intercalated in the rigid PVC/Na⁺‐MMT nanocomposites. However, results of XRD and TEM show MMT is partially intercalated and exfoliated in the rigid PVC/O‐MMT nanocomposites. Tensile strength, yield strength, and elongation at break of the rigid PVC/MMT nanocomposites were improved simultaneously with adding 1–3 wt % Na⁺‐MMT or O‐MMT with respect to that of pristine PVC. However, the addition of Na⁺‐MMT or O‐MMT should be kept as not more than 3 wt % to optimize the mechanical properties and the processing stability of the rigid PVC/MMT nanocomposites. SEM micrographs of the fractured surfaces of the rigid PVC/Na⁺‐MMT and PVC/O‐MMT nanocomposites both before and after tensile tests were also illustrated and compared. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 2145–2154, 2006     

Hydrothermal Synthesis and X‐Ray Structural Characterization of Manganese,Nickel, and Cadmium Coordination Polymers Containing 2,3‐Pyridinedicarboxylate as Multidentate Ligands

Three divalent transiton‐metal complexes of 2,3‐pyridinedicarboxylate (2,3‐pda²), [Mn(2,3‐pda)‐(H₂O)3]_∞ ( 7 ), [Ni(2,3‐pda)(H₂O)3]_∞ ( 8 ), and [Cd2(2,3‐pda)₂(H₂O)]_∞ ( 9 ) have been hydrothermally synthesized and structurally characterized. X‐ray diffraction analyses reveal that compounds 7 and 8 are zigzag‐ and linear‐type one‐dimension (1D) coordination polymers, respectively, whereas compound 9 is a three‐dimension (3D) coordination polymer. A simple comparison of the coordination geometries with the available neutral analogues {M_x(2,3‐pda)_x(H₂O)_y}_∞ containing one or two divalent transition‐metal atoms and equal ligands in the presence or absence of coordinated water molecules is also presented.     

Detailed Structural Characterizations of SBA‐15 and MCM‐41 Mesoporous Silicas on a High‐Resolution Transmission Electron Microscope

Using high‐resolution transmission electronic micrograph (HR‐TEM) observation, one can clearly see the pore geometry of the MCM‐41 and SBA‐15 mesoporous silicas to determine that their pore shapes are hexagonal and round, respectively. With the perpendicular orientations of the nanochannels to the electron beam, parallel line images of the (100) and (110) repeating spacings were observed. In the SBA‐15 mesoporous silicas, there are byproducts of the granular silica and disordered mesostructures, attributed to the weak hydrogen interactions between Pluronic 123 blockcopolymer and the silica species. There are also many different and significant +π disclination defects in SBA‐15 and MCM‐41 surfactant‐silica composites. The SBA‐15 with a thicker silica wall is more stable under irradiation by high‐energy electron beams compared to MCM‐41, which has thinner wall thickness. Some carbon nanostructure impurities were found in some carbon films on the metal grids.     

Efficient synthesis of N-benzyl-3-aminopyrrolidine-2,5-dione and N-benzyl-3-aminopyrrolidin-2-one

Reaction of N-tert-butyloxycarbonylasparagine (Boc-Asn) with 2 equiv of benzyl bromide in presence of cesium carbonate led to N-benzyl-3-Boc-amino-pyrrolidin-2,5-dione 1a (N-benzyl-3-Boc-aminosuccinimide). Borane dimethylsulfide reduced 3-Boc-aminopyrrolidine-2,5-dione 1a into 3-Boc-aminopyrrolidin-2-one 2a. The same procedure could also be used to prepare derivatives 1 and 2 substituted on the aromatic ring.     

SYNTHESIS OF MESOPOROUS POLY(STYRENE-co-MALEIC ANHYDRIDE)/SILICA HYBRID MATERIALS VIA A NONSURFACTANT-TEMPLATED SOL-GEL PROCESS*

Mesoporous poly (styrene-co-maleic anhydride)/silica hybrid materials have been prepared. The synthesis wasachieved by the HCl-catalyzed sol-gel reactions of tetraethyl orthosilicate (TEOS) and styrene-maleic anhydride copolymerin the presence of 3-aminopropyl triethoxysilane (APTES) as a coupling agent and citric acid as a nonsurfactant template orpore-forming agent, followed by ethanol extraction. Characterization results from nitrogen sorption isotherms and powder X-ray diffraction indicate that polymer-modified mesoporous materials with large specific surface areas (e.g. 900 m~2/g) andpore volumes (e.g. 0.6 cm~3/g) could be prepared. As the citric acid concentration is increased, the specific surface areas, porevolumes and pore diameters of the hybrid materials increase.