Photoluminescence of green nanophosphors Sr2MgSi2O7 doped with Tb3+ under 374-nm excitation

A series of Sr₂MgSi₂O₇:Tb³⁺ nanophosphors is prepared using a high-temperature solid-state reaction. The x-ray diffraction patterns show that the crystal structure of the sample is not significantly affected by Tb³⁺ ions. However, the images of the scanning electron microscope illustrate that the average size of nanoparticles becomes larger with the increase of Tb³⁺ concentration. Unlike earlier investigations on down-conversion emission of Tb³⁺ ion excited by deep ultraviolet light, in this work, the photoluminescence characteristics of Sr₂MgSi₂O₇ nanophosphors doped with different Tb³⁺ concentrations are analyzed under 374-nm excitations. The intense green emission at 545 nm is observed at an optimal doping concentration of 1.6 mol%. The main reason for the concentration quenching is due to the electric dipole-electric dipole interaction among Tb³⁺ ions.     

Zn2 GeO4:Mn2+绿色磷光粉的制备和长余辉性能

采用高温固相反应法合成了Zn_2GeO_4∶xMn~(2+)系列绿色长余辉磷光粉。XRD分析结果表明,掺锰磷光粉的主要衍射峰位与锗酸锌晶体标准卡基本一致,但略有红移。SEM照片显示,相对于Zn_2GeO_4基质平均粒径而言,掺锰磷光粉的颗粒尺寸均增大。在325 nm紫外光激发下,Zn_2GeO_4∶Mn~(2+)发射出强的530 nm绿光,优化掺锰离子浓度为0.5%。同时发现Zn_2GeO_4∶0.2Mn~(2+)磷光粉暗场条件下的余辉时间超过180 min,详细讨论了Zn_2GeO_4∶Mn~(2+)长余辉发光的内在机理。     

PS-b-PNIPAM/Ag复合微粒的制备与表征

采用原子转移自由基聚合(ATRP)法合成了聚苯乙烯-b-聚(N-异丙基丙烯酰胺)(PS-b-PNIPAM)两亲性嵌段共聚物, 并以其为模板, 聚乙烯亚胺(PEI)作为银离子和嵌段共聚物PS-b-PNIPAM的交联剂以及还原剂, 制备了PS-b-PNIPAM/Ag复合纳米微粒. 利用透射电子显微镜(TEM)、X射线衍射(XRD)和傅里叶变换红外(FTIR)光谱对复合纳米微粒的形貌及其成分进行了表征. X射线衍射和电子衍射证明银纳米微粒具有良好的面心立方体单晶结构. 研究结果表明, 不同浓度的两亲性嵌段共聚物PS-b-PNIPAM在丙酮中形成的胶束模板对银纳米粒子的尺寸及其分布有重要的影响.