ABSTRACT

Copolymers of 1,5-dioxepan-2-one (DXO) and e-caprolactone (?-CL), δ-valerolactone (δ-VL) or L-lactide (LLA) have been synthesized and characterized. High molecular weight copolymers were obtained using stannous-2-ethyl hexanoate as catalyst in bulk. Reactivity ratios for the copolymerization of DXO and δ-VL were determined at 110°C as r_VL=0.5 and r_DXO=2.3. At high conversion, depolymerization of δ-VL occurred, resulting in lower molecular weight and variations in the copolymer composition.

Physical properties, such as crystallinity and melting temperature of the DXO-copolymers proved to be strongly dependent on the choice of comonomer and on the molar composition of the copolymers. DXO appears to be incorporated into the poly-?-caprolactone (PCL) crystals and to some extent into the poly-δ-valerolactone (PVL) crystals, resulting in a more gradual decrease in crystallinity with increasing amount of DXO.     

Secondary ion yields produced by keV atomic and polyatomic ion impacts on a self-assembled monolayer surface

A suite of keV polyatomic or 'cluster' projectiles was used to bombard unoxidized and oxidized self-assembled monolayer surfaces. Negative secondary ion yields, collected at the limit of single ion impacts, were measured and compared for both molecular and fragment ions. In contrast to targets that are orders of magnitude thicker than the penetration range of the primary ions, secondary ion yields from polyatomic projectile impacts on self-assembled monolayers show little to no enhancement when compared with monatomic projectiles at the same velocity. This unusual trend is most likely due to the structural arrangement and bonding characteristics of the monolayer molecules with the Au(111). Copyright 1999 John Wiley & Sons, Ltd.     

Fusion around the barrier for 7Li+12C

Fusion cross-sections for the ⁷Li + ¹²C reaction have been measured at energies above the Coulomb barrier by the direct detection of evaporation residues. The heavy evaporation residues with energies below 3 MeV could not be separated out from the α-particles in the spectrum and hence their contribution was estimated using statistical model calculations. The present work indicates that suppression of fusion cross-sections due to the breakup of ⁷Li may not be significant for ⁷Li + ¹²C reaction at energies around the barrier.     

Real meromorphic functions and linear differential polynomials

We determine all real meromorphic functions f in the plane such that f has finitely many zeros, the poles of f have bounded multiplicities, and f and F have finitely many non-real zeros, where F is a linear differential polynomial given by F = f (k) +Σk-1j=0ajf(j) , in which k≥2 and the coefficients aj are real numbers with a0≠0.     

Sorption of inorganic nanoparticles in woven cellulose fabrics

Titanium dioxide was deposited from aqueous suspension onto cellulosic surfaces.Titania was sourced from Degussa (P25TM,70:30 anatase:rutile).Dry uptake of particles was shown to be rapid and dominant with one-third of the deposition occurring in less than 30 s and over one-half in the first minute.Isotherms were recorded to compare the rate of titanium deposition on dry and pre-wetted cotton.In the dry case uptake reached a maximum in 30 min whereas in the pre-wetted case the uptake was seen to continue beyond 180 min.A broad trend of higher deposition occurring at lower pH was seen,corresponding to the region where surface charges were opposite and thus attractive.Dry pickup was less significant at high pH.The response to varying ionic strength was complex and was attributed to the combined effect of charge screening,particle aggregation and consequent particle entrapment or occlusion.Titania deposition into the interstices of woven cotton sheets resulted in the formation of inorganic,nanoparticulate skeletons which could be isolated by controlled combustion of the cellulose and thus cotton was suggested to have potential for the templated synthesis of high surface area semiconductor materials.     

Annealing effect of NiO/Co90Fe10 thin films: From bilayer to nanocomposite

Exchange-biased bilayers are widely used in the pinned layers of spintronic devices. While magnetic field annealing (MFA) was routinely engaged during the fabrication of these devices, the annealing effect of NiO/CoFe bilayers is not yet reported. In this paper, the transition from NiO/Co₉₀Fe₁₀ bilayer to nanocomposite single layer was observed through rapid thermal annealing at different temperatures under magnetic field. The as-deposited and low-temperature (<623 K) annealed samples had rock salt (NiO) and face center cubic (Co₉₀Fe₁₀) structures. On the other hand, annealing at 623 K and 673 K resulted in nanocomposite single layers composed of oxides (matrix) and alloys (precipitate), due to grain boundary oxidization and strong interdiffusion in the NiO/CoFe and CoFe/SiO₂ interfaces. The structural transition was accompanied by the reduction of grain sizes, re-ordering of crystallites, incensement of roughness, and reduction of Ni²⁺. When measured at room temperature, the bilayers exhibited soft magnetism with small room-temperature coercivity. The nanocomposite layers exhibited an enhanced coercivity due to the changes in the magnetization reversal mechanism by pinning from the oxides. At 10 K, the increased antiferromagnetic anisotropy in the NiO resulted in enhanced coercivity and exchange bias in the bilayers. The nanocomposites exhibited weaker exchange bias compared with the bilayers due to frustrated interfacial spins. This investigation on how the magnetic properties of exchange-biased bilayers are influenced by magnetic RTA provides insights into controlling the magnetization reversal properties of thin films.     

Syntheses and reactions of some fluorinated dienes,cyclobutenes and furans

There are many reports¹ of the pyrolysis of fluorinated organic compounds, including the defluorination of cyclic fluorocarbons over iron to give aromatic compounds. Extending this technique we have investigated the flow pyrolysis of some readily accessible unsaturated fluorocarbons, such as I, II, and III, and found these to be synthetically

useful routes to fluorinated dienes, cyclobutenes, and furans. Pyrolyses were carried out using a nitrogen flow over platinum, iron or caesium fluoride heated at 430–700°. The various products can all be rationalized in terms of intermediate allylic radicals, and the solid substrate influences which allylic radicals are formed.We are also investigating the chemistry of those now accessible compounds, such as IV, V, and VI, and some of the preliminary results are described.

For example the fluoride ion induced dimerisation of IV gave two major products VII and VIII via a particular interesting mechanism.

     

Increased surface spin stability in γ-Fe2O3 nanoparticles with a Cu shell

γ-Fe(2)O(3) nanoparticles were coated with a Cu shell in situ during synthesis. An interfacial monolayer of CuO in the Cu-coated γ-Fe(2)O(3) nanoparticles was discovered that stabilized the disordered surface spins of γ-Fe(2)O(3) nanoparticles. Element-specific x-ray absorption spectroscopy at the L-edges for Cu and Fe indicated the magnetic moment of the Cu in the shell interacted with the γ-Fe(2)O(3) nanoparticle's surface magnetic moments. This exchange interaction between the Fe and Cu at the interface permitted an overall Cu moment in CuO (an antiferromagnet typically) that altered the γ-Fe(2)O(3) nanomagnetism. Increasing the Cu shell thickness also increased the total Fe magnetism of the nanoparticles.