MgO(111)衬底MgB2 超薄膜的制备和性质研究

利用混合物理化学气相沉积法(HPCVD)在MgO(111)衬底上制备了干净的MgB₂超导超薄膜. 在背景气体压强, 载气氢气流量以及沉积时间一定的情况下, 改变B₂H₆的流量, 制备得到不同厚度系列的MgB₂超导薄膜样品, 并测量了其超导转变温度 T_c, 临界电流密度J_c等临界参量. 该系列超导薄膜沿c轴外延生长, 表面具有良好的连接性, 且有很高的超导转变温度T_c(0) ≈ 35-38 K和很小的剩余电阻率ρ(42 K) ≈ 1.8-20.3 μΩ·cm^-1. 随着膜厚的减小而减小, 临界温度变低, 而剩余电阻率变大. 其中20 nm的样品在零磁场, 5K时的临界电流密度J_c ≈ 2.3×10⁷ A/cm². 表明了利用HPCVD在MgO(111)衬底上制备的MgB₂超薄膜有很好的性能, 预示了其在超导电子器件中广阔的应用前景. 关键词： MgO(111)衬底 2超薄膜')" href="#">MgB₂超薄膜 混合物理化学气相沉积     

Magnetic property improvement of niobium doped with rare earth elements

A new idea is proposed by the PKU group to improve the magnetic properties of the Type-II superconductor niobium.Rare earth elements like scandium and yttrium are doped into ingot niobium during the smelting processes. A series of experiments have been done since 2010. The preliminary testing results show that the magnetic properties of niobium materials have changed with different doping elements and proportions while the superconductive transition temperature does not change very much. This method may increase the superheating magnetic field of niobium so as to improve the performance of the niobium cavity, which is a key component of SRF accelerators. A Tesla-type single-cell cavity made of scandium-doped niobium is being fabricated.     

MgB2超导膜的厚度与其Jc(5K,0T)的关系

通过混合物理化学气相沉积法 (hybrid physical-chemical vapor deposition, HPCVD), 在(000l) SiC 衬底上制得一系列从10 nm到8 μm的MgB₂超导膜样品, 并对它们的形貌、超导转变温度T_c 和临界电流密度J_c与膜厚度的关系进行了研究. 观察到T_c随膜厚度增加上升到最大值后, 尽管膜继续增厚, 但T_c值保持近乎平稳, 而J_c则先随膜厚度增加上升到最高值后, 继而则随膜的厚度的增加而下降. MgB₂膜的T_c(0)和T_c(onset)值与膜厚的关系基本一致, T_c(0)在膜厚为230 nm处达到最大值T_c(0)=41.4 K, 而J_c(5K,0T)在膜厚为100 nm时达到最大值, J_c (5 K, 0 T)=2.3×10⁸A·cm^-2, 这也说明了我们能用HPCVD方法制备出高质量干净MgB₂超导膜. 本文研究的超导膜厚度变化跨度非常大, 从10 nm级的超薄膜到100 nm级的薄膜, 再到几微米的厚膜, 如此T_c和J_c对膜厚度变化的依赖就有了较完整、成体系的研究. 并且本文的工作对MgB₂超导薄膜制备的厚度选取具有实际应用意义. 关键词： 2超导膜')" href="#">MgB₂超导膜 混合物理化学气相沉积法 厚度 临界电流密度