Measurement and Analysis of Composition and Depth Profile of H in Amorphous Si1-xCx:H Films

Composition in amorphous Si1-xCx：H heteroepitaxial thin films on Si （100） by plasma enhanced chemical vapour deposition （PECVD） is analysed. The unknown x （0.45-3.57） and the depth profile of hydrogen in the thin films are characterized by Rutherford backscattering spectrum （RBS）, resonance-nuclear reaction analysis （R-NRA） and elastic recoil detection （ERD）, respectively. In addition, the depth profile of hydrogen in the unannealed thin films is compared to that of the annealed thin films with rapid thermal annealing （RTA） or laser spike annealing （LSA） in nitrogen atmosphere. The results indicate that the stoichiometric amorphous SiC can be produced by PECVD when the ratio of CH4/SiH4 is approximately equal to 25. The content of hydrogen decreases suddenly from 35% to 1% after 1150℃ annealing. RTA can reduce hydrogen in SiC films effectively than LSA.     

氧气氛中p-GaN/Ni/Au电极在相同温度不同合金时间下的欧姆接触形成机制和扩散行为

用卢瑟福背散射/沟道技术研究了p-GaN上的Ni/Au电极在氧气氛下相同合金温度(500℃)不同合金时间后的微结构演化,以揭示欧姆接触的形成机制.利用背散射随机谱和RUMP模拟程序研究了电极金属之间的互扩散,用沟道谱探测了电极金属中的氧分布.结合不同合金时间下比接触电阻ρ_c的变化,发现随着合金时间的延长比接触电阻持续降低,在合金时间60 s后降低的速度减慢, Au扩散到GaN的表面,在p-GaN上形成外延结构,O向电极内部扩散反应生成NiO对降低ρ_{关键词： GaN 卢瑟福背散射/沟道 欧姆接触}     

Structure Characterization of Modified Polyimide Films Irradiated by 2MeV Si Ions

Structures of polyimide （6051） films modified by irradiation of 2.0 MeV Si ions with different fluences are studied in detail. Variations of the functional groups in polyimide are investigated by attenuated total reflection Fourier transform infrared spectroscopy （ATR-FTIR） and Raman spectroscopy. The results indicate that the functional groups can be destroyed gradually with the increasing ion fluenee. The variations of structure and element contents are characterized by x-ray diffraction （XRD）, Rutherford backscattering spectrometry （RBS） and x- ray photoelectron spectroscopy （XPS）. The results indicate that the contents of N and O decrease significantly compared with the original samples, some graphite-like and carbon-rich phases are formed in the process of irradiation.     

Depth Dependence of Tetragonal Distortion of a ZnO/Mg0.1Zn0.90/ZnO Heterostructure Studied by Rutherford Backscattering/Channeling

Rutherford backscattering and channeling are used to characterize the structure of a ZnO/Mg0.1Zn0.90/ZnO heterostructare grown on a sapphire （0001） substrate by rf plasma-assisted molecular beam epitaxy. The results show that the Mg0.1Zn0.90 layer has the same hexagonal wurtzite structure as the underlying ZnO layer, and the heterostructure has a good crystalline quality with xmin = 5%, which is the ratio of the backscattering yields of aligned and random spectra in the near-surface region. Using the channeling angular scan around an off-normal （1213） axis in the {1010} plane of both ZnO and MgZnO layer, the tetragonal distortion εT, which is caused by the elastic strain in the epilayer, is determined. The depth dependence of εT is obtained by using this technique. It can clearly be seen that the elastic strain rapidly decreases with the increase in thickness of the ZnO film in the early growth stage and becomes slightly larger in the region of the Mg0.1Zn0.9O layer.     

Mg+注入对GaN晶体辐射损伤的研究

在蓝宝石衬底上通过金属有机物化学气相沉积(metal-organic chemical vapor deposition,MOCVD)方法外延生长的GaN薄膜具有良好的结晶品质,xmin达到2.00%.结合卢瑟福背散射/沟道(Rutherford backscattering/channeling,RBS/C)和高分辨X射线衍射(high-resolution X-ray diffraction,HXRD)的实验测量,研究了不同剂量和不同角度Mg+注入GaN所造成的辐射损伤.实验结果表明,随注入剂量的增大,晶体的辐射损伤也增大,注入剂量在1×1015atom/cm2以下,xmix小于4.78%,1×1016atom/cm2是Mg+注入GaN的剂量阈值,超过这个阈值,结晶品质急剧变差,xmin达到29.5%;随机注入比沟道注入的辐射损伤大,且在一定范围内随注入角度的增大,损伤也增大,在4×1015atom/cm2剂量下偏离〈0001〉沟道0°,4°,6°,9°时的xmin(%)分别为6.28,8.46,10.06,10.85;经过700℃/10min+1050℃/20s两步退火和1000℃/30s高温快速退火后,晶体的辐射损伤都有一定程度的恢复,而且1000℃/30s高温快速退火的效果更好,晶体的辐射损伤可以得到更好的恢复.     

Tetragonal Distortion of InN Thin Films by RBS/Channeling

Rutherford backscattering and channeling spectrometry （RBS/C） are used to identify the crystalline quality （Xmin = 4.87%） Of an InN thin film as a function of depth, and make a non-destructive quantitative analysis of the structure, in order to analyze the tetragonal distortion of the InN thin film at the depth determined.     

A Comparison of GaN Epilayers with Multiple Buffer Layers and with a Single Buffer Layer Grown on Si（111） Studied by HRXRD and RBS/Channeling

Two hexagonal GaN epilayers （samples A and B） with multiple buffer layers and single buffer layer are grown on Si （111） by metal-organic vapour phase epitaxy （MOVPE）. From the results of Rutherford backscattering （RBS）/channeling and high resolution x-ray diffraction （HRXRD）, we obtain the lattice constant （a and c） of two GaN epilayers （aA = 0.3190 nm, cA = 0.5184 nm and aB = 0.3192 nm, CB = 0.5179 nm）, the crystal quality of two GaN epilayers （ ХminA=4.87%, ХminB =7.35% along 〈1-↑213〉 axis） and the tetragonal distortion eT of the two samples along depth （sample A is nearly fully relaxed, sample B is not relaxed enough）. Comparing the results with the two samples, it is indicated that sample A with multiple buffer layers have better crystal quality than sample B with a single buffer layer, and it is a good way to grow GaN epilayer on Si （111） substrates using multiple buffer layers to improve crystal quality and to reduce lattice mismatch.     

Tetragonal Distortion of GaN Epilayer with Multiple Buffer Layers on Si （111） Studied by RBS/Channelling and HRXRD

Rutherford backscattering （RBS）/channelling and high resolution x-ray diffraction （HRXRD） have been used to characterize the tetragonal distortion of a GaN epilayer with four Alx Ga1-xN and single AIN buffer layers grown on a Si （111） substrate by metal-organic vapour phase epitaxy （MOVPE）. The results show that a 1000nm GaN epilayer with a perfect crystal quality （Xmin = 1.54%） can be grown on the Si （111） substrate in virtue of multiple buffer layers. Using the RBS/channelling angular scan around an off-normal （1213） axis in the （1010） plane and the conventional HRXRD θ - 20 scans normal to GaN （0002） and （1122） planes at the 0° and 180° azimuth angles, the tetragonal distortion eT, which is caused by the elastic strain in the epilayer and different buffer layers, can be obtained respectively. The two experiments are testified at one result, the tetragonal distortion of GaN epilayer is nearly to a fully relaxed （eT = 0）.     

Si(111)衬底上生长有多缓冲层的六方GaN晶格常数计算和应变分析

利用卢瑟福背散射/沟道技术和高分辨率X射线衍射技术对在Si(111)衬底上利用金属有机化合物气相外延技术(MOVPE)生长有多缓冲层的六方GaN外延膜进行结晶品质计算、晶格常数计算和应变分析. 实验结果表明：GaN外延膜的结晶品质为χ_min=1.54%，已达到完美晶体的结晶品质(χ_min=1%—2%)；GaN外延膜的水平方向和垂直方向晶格常数分别为：a_epi＝0.31903nm，c_epi=0.51837nm，基本达到G 关键词： GaN 高分辨X射线衍射 卢瑟福背散射/沟道 弹性应变     

用卢瑟福背散射/沟道技术研究ZnO/Zn0.9Mg0.1O/ZnO异质结的弹性应变

利用卢瑟福背散射/沟道技术对射频等离子体辅助分子束外延法生长在蓝宝石衬底上的ZnO/Zn_0.9Mg_0.1O/ZnO异质结进行了组分分析，并得到了异质结弹性应变随深度的变化，应变由界面向表面逐渐释放，并由负变正，且在ZnO与Zn_0.9Mg_0.1O界面处轻微增大.负的应变是由于ZnO与衬底的晶格失配和热失配，而逐渐变为正值是Zn_0.9Mg_0.1O与ZnO的晶格常数差异及弹性应变的 关键词： 异质结 卢瑟福背散射/沟道 弹性应变 ZnMgO