掺杂Y2O3和BaCeO3提高MOD-YBCO超导性能的研究

本文通过在前驱液中添加过量钇盐和铈的有机盐,采用三氟乙酸盐-金属有机沉积法(TFA-MOD) 在铝酸镧单晶基体上制备了含有纳米氧化钇和纳米铈酸钡的YBCO薄膜. 与纯YBCO薄膜相比,掺杂Y₂O₃/BaCeO₃的YBCO膜的临界转变温度几乎保持不变,为91 K左右. 而掺杂Y₂O₃/BaCeO₃的YBCO膜的临界电流密度达到5.0 MA/cm² (77 K, 0T), 是纯YBCO膜临界电流密度的1.5倍.薄膜中的Y₂O₃和BaCeO₃可能在YBCO内部起到了 有效的钉扎磁通作用. 关键词： 钇钡铜氧薄膜 2O₃和纳米BaCeO₃')" href="#">纳米Y₂O₃和纳米BaCeO₃ 磁通钉扎 三氟乙酸盐-金属有机沉积     

YBa2Cu3O7-x高温超导涂层导体磁通钉扎的研究进展

以YBa2Cu3O7-x(YBCO)超导涂层为导体的第二代高温超导带材由于其优异的本征性能,吸引着人们不断探索和研究其实用成材技术.现在,近千米长带的研制成功,使其已经或即将应用于电缆、马达和其他电力器件.为了更好地使YBCO涂层导体能够在高温高磁场下应用.最近在YBCO中引入钉扎中心以提高它的电磁性能的研究是一个热点.综述了近年来二代超导带材的发展状况,并对目前高温超导体中提高电学性能的研究做了较为系统的介绍.     

Influence of oxygen pressure on critical current density and magnetic flux pinning structures in YBa2Cu3O7-x fabricated by chemical solution deposition

This paper studies the effect of oxygen partial pressure on the fabrication of YBa 2 Cu 3 O 7 x films on (00l) LaAlO 3 substrates by metalorganic deposition using trifluoroacetates (TFA-MOD).As the oxygen partial pressure increases to 1500 Pa,a great increase in the superconducting properties is observed at high magnetic fields parallel to the YBCO c axis.The cross-sectional transmission electron microscope images show that a high density of stacking faults in the size range of 10-15 nm may act as flux pinning centres to enhance the critical current density of the YBCO films     

国产MOCVD-YBCO带材高温超导线圈研制与磁场温度特性研究

超导磁体的场强与超导材料的载流能力、磁体口径和低温环境有密切关系.为了在中高温区域实现高磁场强度的超导磁体,采用国产第二代高温超导带材,成功绕制出内直径为100 mm的高温超导线圈.该超导线圈在77,65,55和46 K不同温区下进行了性能测试,其最大运行电流分别为65,147,257和338 A,对应的中心磁场强度分别为0.78,1.77,3.1和4.08 T.所研制的超导线圈的中平面上磁场基本一致.     

Precursor evolution and growth mechanism of BTO/YBCO films by TFA–MOD process

In this study, BaTiO3 （BTO）-doped YBCO films are prepared on LaA103 （100） single-crystal substrates by metal- organic decomposition （MOD） using trifluoroacetate （TFA） precursor solutions. The critical current density （Jc） of BTO/YBCO film is as high as 10 MA/cm2 （77 K, 0 T）. The BTO peak is found in the X-ray diffraction （XRD） pattern of a final YBCO superconductivity film. Moreover, a comprehensive study of the precursor evolution is conducted mainly by X-ray analysis and μ-Raman spectroscopy. It is found that the TFA begins to decompose at the beginning of the thermal process, and then further decomposes as temperature increases, and at 700 ℃ BTO nanoparticles begin to appear. It sug- gests that the YBCO film embedded with BTO nanoparticles, whose critical current density （Jc） is enhanced, is successfully prepared by an easily scalable chemical solution deposition technique.     

前驱液成分对TFA-MOD法制备YBa2Cu3O7-x薄膜超导性能的影响

采用三氟乙酸盐-金属有机沉积法(TFA-MOD)在铝酸镧单晶基体上制备了YBa₂Cu₃O_7-x (YBCO)超导薄膜.通过改变前驱液的成分,研究了金属元素的不同化学计量比对YBCO薄膜的结构和性能的影响.结果表明,按照钇盐Y(CH₃COO)₃与钡盐Ba(CH₃COO)₂的比例为Y ∶Ba=1 ∶1.5时所制备的YBCO薄膜的临界电流密度比严 关键词： 三氟乙酸盐-金属有机沉积 钇钡铜氧薄膜 前驱液成分 磁通钉扎     

Study on reaction mechanism of YBa2Cu3O7-x film by TFA-MOD process

This paper systematically investigates the intermediate phases of YBa2Cu3O7-x (YBCO) film prepared by metalorganic deposition method using trifluoroacetates (TFA-MOD). According to x-ray diffraction and Raman analyses, the precursor film decomposed in a mixture of BaF2, Y2O3 and CuO after the pyrolysis process. Then these intermediate phases converted into tetragonal YBa2Cu3O6.5 at about 725°C. The influence of water vapour pressure on the YBa2Cu3O7-x film growth on LaAlO3 single-crystal substrates was also studied. The films prepared at low water vapour pressures (40-140 hPa) showed poor electrical performance due to the a-axis grain structure and impurity phases. However, the films prepared at 190 hPa exhibited the highest critical temperature of 90 K and the highest Jc of 3.8 MA/cm2, which was attributed to the formation of a purer YBCO phase and stronger biaxial texture.     

插入二氧化铈薄膜提高MOD-YBa2Cu3O7-x厚膜超导性能的研究

YBa₂Cu₃O_7-x(YBCO)膜存在“厚度效应”: 随着厚度增加, YBCO薄膜的临界电流密度下降, 尤其是YBCO薄膜的厚度超过1 μm时, 它的临界电流密度急剧下降. 本文在YBCO薄膜之间引入极薄的二氧化铈(CeO₂)薄膜, 成功制备出结构为YBCO/YBCO/CeO₂/YBCO的超导厚膜. 所制备的厚度为2 μm的YBCO膜临界电流密度为1.36 MA/cm² (77 K, 自场), 其性能比相同厚度的纯YBCO膜有了较大幅度的提升. 研究表明CeO₂薄膜起到了传递织构、松弛应力的作用.     

阳离子交换法制备稳定的近红外区核/壳型PbS/CdS量子点

硫化铅量子点(PbS QDs)的光氧化稳定性差是其应用于太阳能电池等领域的主要限制因素之一. 采用阳离子交换法在合成的PbS量子点表面包裹一层具有更稳定、更大禁带宽度的硫化镉(CdS)壳层, 制备出稳定的核/壳型PbS/CdS量子点; 同时, 研究了反应温度和反应时间对阳离子交换过程的影响规律. 通过透射电子显微镜和高分辨透射电子显微镜(TEM/HRTEM)、X射线衍射仪(XRD)、吸收光谱和荧光光谱考察了所制备PbS/CdS量子点的结构、光学特性和光氧化稳定性．结果表明: 阳离子交换过程中, 离子交换反应程度有限、仅发生在量子点的表面层, 但极薄的CdS壳层已能有效钝化PbS量子点的表面缺陷、显著提高其光氧化稳定性.     

Strong flux pinning enhancement in YBa2Cu3O7-x films by embedded BaZrO3 and BaTiO3 nanoparticles

YBa2Cu3O7-x (YBCO) films with embedded BaZrO3 and BaTiO3 nanoparticles were fabricated by metalorganic deposition using trifluoroacetates (TFA-MOD). Both X-ray diffraction and transmission electron microscopy revealed that these BaZrO3 and BaTiO3 nanoparticles had random orientations and were distributed stochastically in the YBCO matrix. The unique combined microstructure enhances the critical current density (Jc) of the BaZrO3/BaTiO3 doped-YBCO films, while keeping the critical transition temperature (Tc) close to that in the pure YBCO films. These results indicate that BaZrO3 and BaTiO3 nanoparticles provide strong flux pinning in YBCO films.