Properties of ITO films prepared by reactive magnetron sputtering

Indium tin oxide (ITO) thin films were deposited by mid frequency pulsed dual magnetron sputtering using a metallic alloy target with 10 wt.% tin in an atmosphere of argon and oxygen. The aim of the work was to study the interdependence of structural, electrical and optical properties of ITO films deposited in the reactive and transition target mode, respectively. The deposition rate in the transition mode exceeds the deposition rate in the reactive mode by a factor of six, a maximum value of 100 nm·m min⁻¹ could be achieved. This corresponds to a static deposition rate of 200 nm min⁻¹. The lowest electrical resistivity of 1.1·10⁻³ Ω cm was measured at samples deposited in the high oxygen flow range in the transition mode. The samples show a good transparency in the visible range corresponding to extinction coefficients being below 10⁻². X-ray diffraction was used to characterise crystalline structure as well as film stress. ITO films prepared in the transition mode show a slightly preferred orientation in (211) direction, whereas films deposited in the reactive mode are strongly (222) oriented. Compared to undoped In₂O₃ all samples have an enlarged lattice. The lattice strain perpendicular to the surface is about 0.8% and 2.0% for films grown in the transition and the reactive mode, respectively. Deposition in the transition mode introduces a biaxial film stress in the range of −300 MPa, while stress in reactive mode samples is −1500 MPa.     

Preparation and Characterization of Compositions Based on PbO-MgO-Nb2O5 Using the Sol-Gel Method

Lead Magnesium Niobate, Pb(Mg_1/3Nb_2/3)O₃ (PMN), is an important relaxor ferroelectric material. A significant problem exists, however, in the preparation of this material: it is very difficult to prepare pure phase, without the presence of a pyrochlore impurity phase which degrades the dielectric properties. Depending on the processing conditions, the amount of pyrochlore phase varies.Considering the ternary diagram PbO-MgO-Nb₂O₅, different compositions have been prepared by a simple sol-gel method at room temperature using Pb(CH₃COO)₂, Mg(CH₃COO)₂, Nb(OC₂H₅)₅ as precursors. After the heat treatment, the samples obtained were analyzed by XRD and EPMA with the purpose of studying the compositions formed.From the analysis of these results, it seems to be that the appearance of pyrochlore can be related to the reactivity of the MgO and/or the presence of other phases of the binary system PbO-Nb₂O₅. An excess of Pb and Mg is necessary for compositions to be formed near the PMN. The control of the amount of these two elements is very important because an excess of MgO would lead to rich compositions in Mg as a secondary phase.     

Effect of pressure on the proton transfer rate from a photoacid to a solvent. 4. Photoacids in methanol

The pressure dependence of the excited-state proton dissociation rate constant of four photoacids, 2-naphthol-6,8-disulfonate (2N68DS), 10-hydroxycamptothecin (10-CPT), 5-cyano-2-naphthol (5CN2), and 5,8-dicyano-2-naphthol (DCN2), are studied in methanol. The results are compared with the results of the pressure dependence study we recently conducted for several photoacids in water, ethanol, and propanol. The pressure dependence is explained using an approximate stepwise two-coordinate proton transfer model. The increase in rate, as a function of pressure, manifests a strong dependence of proton tunneling on the distance which decreases with an increase of pressure between the two oxygen atoms involved in the process. The decrease in the proton transfer rate with increasing pressure reflects the dependence of the reaction on the solvent relaxation rate. We found that, for the relatively weak photoacids 2N68DS, 10-CPT, and 5CN2, the proton transfer rate constant increases by a factor of about 5-8 at a pressure of about 1.5 GPa. For a strong photoacid like DCN2, the rate increase was only by a factor of 2.     

Highly efficient recycling of a "sandwich" type polyoxometalate oxidation catalyst using solvent resistant nanofiltration

A "sandwich" type polyoxometalate catalyst ([MeN(n-C8H17)3]12[WZn3(ZnW9O34)2]) was very efficiently recycled by nanofiltration with almost quantitative retention, using an alpha-alumina supported mesoporous gamma-alumina membrane.     

Direct aerobic epoxidation of alkenes catalyzed by metal nanoparticles stabilized by the H5PV2Mo10O40 polyoxometalate

Ag and Ru nanoparticles stabilized by H5PV2Mo10O40, prepared by a sequence of redox reactions and supported on alpha-alumina, were effective catalysts for the direct aerobic epoxidation of alkenes in the liquid phase.     

Chiral hydroperoxides as oxygen source in the catalytic stereoselective epoxidation of allylic alcohols by sandwich-type polyoxometalates: control of enantioselectivity through a metal-coordinated template

The epoxidation of allylic alcohols is shown to be efficiently and selectively catalyzed by the oxidatively resistant sandwich-type polyoxometalates, POMs, namely [WZnM(2)(ZnW(9)O(34))(2)](q)(-) [M = OV(IV), Mn(II), Ru(III), Fe(III), Pd(II), Pt(II), Zn(II); q = 10-12], with organic hydroperoxides as oxygen source. Conspicuous is the fact that the nature of the transition metal M in the central ring of polyoxometalate affects significantly the reactivity, chemoselectivity, regioselectivity, and stereoselectivity of the allylic alcohol epoxidation. For the first time, it is demonstrated that the oxovanadium(IV)-substituted POM, namely [ZnW(VO)(2)(ZnW(9)O(34))(2)](12-), is a highly chemoselective, regioselective, and also stereoselective catalyst for the clean epoxidation of allylic alcohols. A high enantioselectivity (er values up to 95:5) has been achieved with [ZnW(VO)(2)(ZnW(9)O(34))(2)](12)(-) and the sterically demanding TADOOL-derived hydroperoxide TADOOH as regenerative chiral oxygen source. Thus, a POM-catalyzed asymmetric epoxidation of excellent catalytic efficiency (up to 42 000 TON) has been made available for the development of sustainable oxidation processes. The high reactivity and selectivity of this unprecedented oxygen-transfer process are mechanistically rationalized in terms of a peroxy-type vanadium(V) template.     

An efficient, catalytic, aerobic, oxidative iodination of arenes using the H5PV2Mo10O40 polyoxometalate as catalyst

Iodination of arenes was carried out by reacting 1 equiv of arene substrate with 0.5 equiv of iodine under an oxygen atmosphere with H5PV2Mo10O40 as oxidation catalyst. The synthesis is an inherently waste-free method for the preparation of iodoarenes.     

Mild, aqueous, aerobic, catalytic oxidation of methane to methanol and acetaldehyde catalyzed by a supported bipyrimidinylplatinum-polyoxometalate hybrid compound

We have demonstrated that a bipyrimidinylplatinum-polyoxometalate, [Pt(Mebipym)Cl2]+[H4PV2Mo10O40]-, supported on silica is an active catalyst for the aerobic oxidation of methane to methanol in water under mild reaction conditions. Further oxidation of methanol yields acetaldehyde. The presence of the polyoxometalate is presumed to allow the facile oxidation of a Pt(II) intermediate to a Pt(IV) intermediate and to aid in the addition of methane to the Pt catalytic center.     

Phenanthroline-polyoxometalate hybrid compounds and the observation of intramolecular charge transfer

A phenanthroline ligand has been covalently modified at the 2 and 9 positions by an aminophenylhexamolybdate substituent. The 1H NMR spectrum indicated a strong electron-withdrawing effect of the hexamolybdate (Mo6O19(2-)) moiety on the phenanthroline ligand. UV-vis and cyclic voltammetry showed extended conjugation of the hybrid phenanthroline-polyoxometalate compound and the possibility of easy oxidation of the extended phenanathroline ligand. Further EPR experiments provided strong evidence for an intramolecular charge-transfer process with the formation of a phenanthroline cation radical and a reduced hexamolybdate.