Synthesis and refractive‐index control of fluoropolymers by the polyaddition of bis(epoxide)s and triazine di(aryl ether)s

The polyaddition of fluorine‐containing bis(epoxide)s and fluorine‐containing triazine di(aryl ether)s were examined to give the corresponding fluorine‐containing poly(cyanurate)s. It was observed that the synthesized fluoropolymers had good thermal stabilities and good film‐forming properties. The glass transition temperatures (T_g's) and refractive‐indices (n_D's) of synthesized polymers were determined by differential scanning calorimetry and ellipsometry, respectively, and it was found that the values of T_g's and n_D's were supported by their fluorine containing ratios and skeletons. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 4421–4429, 2007     

New poly(butylene succinate)/layered silicate nanocomposites. II. Effect of organically modified layered silicates on structure,properties, melt rheology,and biodegradability

A series of new poly(butylene succinate) (PBS)/layered silicate nanocomposites were prepared successfully by simple melt extrusion of PBS and organically modified layered silicates (OMLS). Three different types of OMLS were used for the preparation of nanocomposites: two functionalized ammonium salts modified montmorillonite and a phosphonium salt modified saponite. The structure of the nanocomposites in the nanometer scale was characterized with wide-angle X-ray diffraction and transmission electron microscopic observations. With three different types of layered silicates modified with three different types of surfactants, the effect of OMLS in nanocomposites was investigated by focusing on four major aspects: structural analysis, materials properties, melt rheological behavior, and biodegradability. Interestingly, all these nanocomposites exhibited concurrent improvements of material properties when compared with pure PBS. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 41: 3160–3172, 2003     

Characterization and determination of linear alkylbenzenesulfonates in environmental water samples by high-performance liquid chromatography with a hydrophilic polymer column and electrospray ionization mass spectrometric detection.

A liquid chromatography-mass spectrometry (LC/MS) method was developed for the separation and determination of linear alkylbenzenesulfonates (C10-C14 LAS) in environmental water samples using a hydrophilic polymer column (Shodex Mspak GF-310 4D). This method involves a solid-phase extraction of the LAS samples with a Sep-Pak PS-2 cartridge. The LAS components were separated on the column with a mobile phase of 29% (w/v) acetonitrile-water containing 0.8 mM di-n-butylammonium acetate and 0.2 M acetic acid, and were detected by mass spectrometry with electrospray ionization. Detection limits of the developed method based on selected ion monitoring (SIM) technique for the C10-C14 LAS standards were 13-47 ng L(-1). The concentrations of the C10-C14 LAS in the environmental water samples ranged between 5-317 microg L(-1) for a river water sample and 0.4-6.4 microg L(-1) for a seawater sample. Linear relationships between the logarithms of retention factors and the alkyl chain lengths for each phenyl positional isomer of LAS could successfully be used for the identification of the isomer peaks.     

Fabrication and transport properties of multiwall carbon nanotube crossroads

A multiwall carbon nanotube crossroads has been fabricated by a manipulation technique using a glass microcapillary, and the low temperature transport properties investigated. The two-terminal conductance of an individual tube shows Tomonaga–Luttinger liquid behavior G∝T^α at high temperature and dI/dV ∝V ^α at low temperature. However, no evidence of such a power-law behavior is obtained in the four-terminal conductance at the junction, where the conductance shows an almost metallic behavior ‘corrected’ by weak localization. Weak localization would essentially appear in electron states at the junctions of MWNTs.     

Ring‐opening grafting polymerization of cyclic monomers onto human hair

Natural human hair was successfully modified by the graft polymerization of trimethylene carbonate, β‐propiolactone, ε‐caprolactone, glycidol, ε‐caprolactam, and 5,5‐dimethyl‐1,3‐dioxane‐2‐thione. In contrast, we could not modify natural human hair by the graft polymerization of oxetane under similar conditions. The model reaction suggested that the main initiating species in these polymerizations were the amino, thiol, and hydroxyl groups in hair, which could induce ring‐opening polymerization. Among the tested monomers, β‐propiolactone was most effective for hair modification with its graft polymer, whose concentration was as high as 0.5 g/g of hair though polymerization under mild conditions. The effects of the hair pretreatment and polymerization temperature on the weight ratio of the grafted polymers were also investigated. Hair modified by grafted polymers was characterized with scanning electron microscopy and Fourier transform infrared measurements. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 736–744, 2007     

Sulfur Concentration in Nanoporous Alumina Membrane

Nanoporous alumina membrane prepared by anodic oxidation using sulfuric acid electrolyte was subjected to TG-DTA and X-ray Photoelectron Spectroscopy (XPS or ESCA) to further study the distribution of sulfur. In XPS study, Ar⁺ ion bombardment was performed on the sample to etch the surface at a rate of 3 nm min^-1. As a result, sulfur was found to be concentrated within a depth of 3nm from the surface. The S content of the surface was found to be 2.7±0.5 wt%, and that at a depth of ca. 3 nm and ca. 10 nm was found to be as low as about 0.6±0.11 wt% (5.37±1.0 wt%→ 1.26±0.2wt% SO₂). In TG-DTA, the mass loss of 7.3% was in fair agreement with that calculated on XPS results (7.1±1.2%). This revised version was published online in July 2006 with corrections to the Cover Date.     

Copolymers containing a spiro orthoester moiety that undergo no shrinkage during cationic crosslinking

A spiro orthoester with an exomethylene group (exoSOE) was radically copolymerized with acrylonitrile or vinyl acetate at several feed ratios to obtain the corresponding copolymers having spiro orthoester moieties in the side chain. The obtained copolymers could be crosslinked via the double ring‐opening polymerization of the spiro orthoester moieties in their side chain by a treatment with BF₃OEt₂. The volume changes upon the crosslinking of the copolymers were evaluated by density measurements with a micromeritics gas pycnometer. The copolymers experienced less than 1% volume expansion instead of volume shrinkage during typical cationic crosslinking, regardless of the copolymer compositions. Negligible shrinkage was observed during the thermal cationic crosslinking of a film cast from a nitrobenzene solution of the copolymers containing a benzylthiophenium salt as a thermally latent cationic initiator. The constantly low volume changes during the crosslinking of the copolymers from exoSOE probably depended on the almost zero volume change during the cationic polymerizations of spiro orthoester derivatives. This indicates that exoSOE is an effective monomer for crosslinkable polymers without volume changes. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 3666–3673, 2006     

Anionic grafting polymerization of propylene sulfide onto human hair in water

Natural human hair was modified by the graft polymerization of propylene sulfide in an aqueous medium. The amount of the polymer grafted onto the reduced hair was 0.15–0.19 g on 1.0 g of hair. The grafted polymer was isolated by the hydrolysis of the hair in the polymer‐grafted hair under basic conditions and was confirmed to be poly(propylene sulfide) by ¹H NMR, ¹³C NMR, and Fourier transform infrared spectra. The number‐average molecular weights of the isolated polymers from the grafted products were 10,000–12,000. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 3778–3786, 2006     

Synthesis of copolymers containing a spiro orthocarbonate moiety and evaluation of the volume change during their cationic crosslinking

Spiro orthocarbonate (SOC) monomers having either an exomethylene group {3,3‐dimethyl‐9‐methylene‐1,5,7,11‐tetraoxaspiro[5.5]undecane (ExoSOC)} or an allyl group {9‐allyl‐3,3‐dimethyl‐1,5,7,11‐tetraoxaspiro[5.5]undecane (AllylSOC)} were radically copolymerized with vinyl monomers at several feed ratios to obtain the corresponding copolymers having SOC moieties in the side chain. The obtained copolymers were crosslinked via the double ring‐opening polymerization of the SOC moieties by a treatment with boron trifluoride etherate. The volume changes during the crosslinking of the copolymers were evaluated by density measurements with a gas pycnometer. As the SOC moiety composition increased, the volume shrinkage during the crosslinking was suppressed, and that finally changed into volume expansion. The volume changes during the crosslinking of the copolymers from AllylSOC were slightly larger than those of the copolymers from ExoSOC. The higher volume expansions in the crosslinking of AllylSOC‐based copolymers were ascribable to the lower steric hindrance around the SOC moieties. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 7040–7053, 2006     

Separation of fulvic acid from soil extracts based on ion-pair formation with a cationic surfactant.

A novel method for separating fulvic acid (FA) from soil extracts is proposed. The FA, defined as the acid-soluble fraction of an alkaline extract of soil, was separated based on the precipitation of an ion-pair with a cationic surfactant, such as domiphen bromide. The precipitate was dissolved in aqueous HCl to produce H+ -type FA and a surfactant chloride (SUR-Cl). SUR-Cl, in the aqueous solution, was removed by extraction with CHCl3. After the aqueous phase was passed through a cation-exchanger (H+ -type), H+ -type FA (FA-SUR) was obtained as a powder by lyophylization. The chemical characteristics of FA-SUR were compared with an FA sample separated according to the method of the International Humic Substances Society using a DAX-8 resin (FA-DAX). The oxygen content, O/C atomic ratio and total acidity of the FA-SUR were significantly larger than the corresponding values for FA-DAX. The solid-state CPMS 13C NMR spectra indicated that the higher oxygen content of the FA-SUR could be due to alcoholic hydroxyl groups and polysaccharides as well as carboxylic groups. These results show that FA-SUR is more polar and hydrophilic than FA-DAX.