Evaluation of tailored magnetic composite films for near-field electromagnetic noise suppression

The effects of permeability and permittivity of the magnetic nanorods filled in composite films have been studied in the broadband radio-frequency range from 0.5 to 10 GHz on a microstrip line. The transmission power absorption of the composite film on a microstrip line was simulated using 3D FEM HFSS program. The model of microstrip line was designed based on IEC standard (IEC 62333-2). The permeability of composite film with magnetic nanorods could be controlled by the aspect ratio of nanorods. The ferromagnetic resonance frequency and the relative complex permeability with the change of aspect ratio were calculated by the Landau–Lifshitz–Gilbert equation. Given the bulk magnetization of 5 kG, the power loss frequency region has exhibited the 2.5–7 GHz broadband frequency by mixing of nanorods with various aspect ratios from 2 to 10. The permittivity effects have been evaluated by changing the real part of permittivity with a fixed imaginary part value and vice versa. The power losses were increased with the proportional to the imaginary part of permittivity and did not show any significant change with the increment of the real part of permittivity. The conduction electromagnetic noise in near field can be suppressed by controlling complex permeability with various aspect ratios of the magnetic nanorods in the composite.

     

Fine tuning of gadolinium doped ceria electrolyte nanoparticles via reverse microemulsion process

Gadolinium doped ceria (Gd–CeO₂) nanoparticles have been synthesized by an reverse microemulsion system using cyclohexane as the oil phase, a non-ionic surfactant Igepal CO 520 and their mixed aqueous solutions of gadolinium III nitrate hexahydrate and cerium III nitrate hexahydrate as the water phase. The control of particle size was achieved by varying the water to surfactant molar ratio. The synthesized and calcined powders were characterized by thermogravimetry-differential thermal analysis (TGA-DTA), X-ray diffraction analysis (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy dispersive spectroscopy (EDS), Fourier transform infrared spectroscopy (FTIR) and Raman spectroscopy. The XRD results show that all the samples calcined at 700 °C were single phase cubic fluorite structure. The average size of the particle was found to increase with increase in water to surfactant molar ratio (R). The mean diameter of the particle for various value of R varies between 8–15 nm (SEM) and 7.5–11 nm (TEM), respectively. EDS confirm the presence of gadolinia and ceria phase in the nanopowder calcined at 700 °C. FTIR analysis was carried to monitor the elimination of residual oil and surfactant phases from the microemulsion-derived precursor and calcined powder. Raman spectroscopy and DTA evidenced the formation of a solid solution of gadolinium doped ceria at room temperature.