In order to solve the problem that single median filtering and gaussian filtering algorithm is not effective in suppressing impulse noise and poisson noise simultaneously in low illumination image, and the edge detail protection is insufficient, an open and close mix-median-gaussian (OCMMG) filtering algorithm based on field programmable gate array (FPGA) was proposed. Firstly, the minimum four-direction difference was used to detect the anomaly degree of each pixel point, the weight was allocated according to the threshold of pulse noise discrimination, and the first step was filtering. Then, the four-direction edge detection algorithm was used to extract image edges, and the second step was filtered according to the set edge confidence characterization value. Finally, the images collected by electron bombarded active pixel sensor (EBAPS) under the condition of 1×10−3 lx illumination were processed by FPGA in real time. The experimental results show that the FPGA processing results are consistent with the software simulation processing results. Compared with the median filtering and gaussian filtering algorithm, the peak signal-to-noise ratio (PSNR) of the algorithm is improved by 3.23% and 16.34%, the structural similarity is improved by 14.66% and 33.86%, and the edge retention index is improved by 0.49% and 4.21%, respectively, which can effectively remove the mixed noise of EBAPS image and meet the real-time requirements. © 2022 Editorial office of Journal of Applied Optics. All rights reserved.     

Pr含量对Bi_5Fe_(0.5)Co_(0.5)Ti_3O_(15)室温多铁性的影响

采用改良的固相烧结工艺制备了Bi5-xPrxFe0.5Co0.5Ti3O15(BPFCT-x,x=0.25,0.50,0.75,0.80)陶瓷样品.X射线衍射结构分析表明:镨(Pr)含量对样品微观结构产生了影响,但所有样品均为层状钙钛矿结构;BPFCT-x样品的剩余极化强度(2Pr)随着掺杂量的增加呈现出先增大后减小的变化趋势,当Pr含量为0.75时,样品的2Pr达到最大值,为6.43μC/cm2.样品的磁性与铁电性能具有相同的变化规律,室温下样品的剩余磁化强度(2Mr)也呈现出先增大后减小的趋势,并且也在x=0.75时达到最大为0.097 emu/g.随着Pr掺杂量增大,样品的室温下铁电和铁磁性能得到明显改善,并且当掺杂量为0.75时,样品室温多铁性最好.Pr掺杂降低了样品中的缺陷浓度,从而提高了样品铁电畴动性,这有助于提高样品铁电性能.而样品铁磁性能的改善可能与Pr对样品晶格畸变产生的影响有关.