含氟CaO-P2O5-SiO2-Na2O-B2O3玻璃陶瓷的制备及性能表征

采用溶胶-凝胶法制备CaO-P₂O₅-SiO₂-Na₂O-B₂O₃体系前驱体粉末,用CaF₂替代部分CaO再次制备前驱体粉末。 通过TG-DSC分析确定结晶温度为865 ℃,经过热处理获得主晶相为Na₆Ca₃Si₆O₁₈的玻璃陶瓷。 通过X射线衍射(XRD)、傅里叶红外光谱(FTIR)、扫描电子显微镜(SEM)等技术手段及体外生物活性实验分析玻璃陶瓷的显微结构及性能。 结果表明,CaF₂的加入能提高玻璃陶瓷的体积密度、抗折强度和弹性模量,并且不会破坏玻璃陶瓷的生物活性。     

VITRIFICATION OF LIGNITE FLY ASH AND METAL SLAGS FOR THE PRODUCTION OF GLASS AND GLASS CERAMICS

This work focuses on the production of glass and glass-ceramics by using industrial wastes or by-products, e.g., two fly ashes from the combustion of lignite, a slag from the production of Fe-Ni and a slag from the making of steel. Vitrification took place at 1 350°-1450℃ and crystallization was achieved by heat treatment at 900, 950 and 1 000℃. The capability of the waste to be vitrified and subsequently devitrified was determined by XRD techniques. The crystalline phase depends greatly on the structure of the by-product and the heat treatment. The final products showed low leachability and good hardness.     

微波加热制备含稀土(La2O3)矿渣微晶玻璃研究

利用矿渣制备微晶玻璃是提高矿产资源利用率的主要形式之一。本文以白云鄂博尾矿为原料,采用微波一步法制备了CaO-MgO-Al₂O₃-SiO₂(CMAS)系辉石相矿渣微晶玻璃。选择835 ℃作为晶化温度,研究了微波加热对微晶玻璃析晶行为和微观组织的影响。以La₂O₃作为研究变量探讨了La₂O₃添加对矿渣微晶玻璃析晶行为的作用。与传统的热处理制度相比,微波加热可以在较短的时间内达到较高的析晶效果。同时La₂O₃的添加促进了晶粒细化。由拉曼光谱分析,La离子添加会导致玻璃网络中桥氧的增多,促进了辉石相析晶。在La的添加量为4%(质量分数)时硬度最高,达到了829.22 MPa。     

Cr4+掺杂Li1.14Zn1.43SiO4透明微晶玻璃近红外宽带光谱特性

采用高温熔融法和热处理制备了Cr⁴⁺掺杂Li_1.14Zn_1.43SiO₄微晶玻璃, 探讨了不同热处理温度下样品的物相、微观形貌及发光性能. 结果表明: 580℃热处理2h得到的微晶玻璃, Li_1.14Zn_1.43SiO₄微晶的粒径约为5nm, 在808nm的二极管激发下, 可观察到中心波长位于1226nm, 半高宽为230nm的近红外宽带发射峰, 荧光寿命约为200.73±1.71μs. 随着热处理温度的升高, Cr⁴⁺离子所处的晶体场环境发生了变化, 且可以观察到样品吸收光谱发生微弱的蓝移, 而荧光光谱发生少量的红移, 分析了晶体场环境变化对样品发光性能的影响. 关键词： 铬离子 微晶玻璃 超宽带发光 晶体场     

Influence of Nucleation Agents Concentration on Crystallization Structure and Properties of Glass-ceramics

Deep color glass-ceramics is prepared by using gold tailings as the main raw material, and Cr2O3 is added as nucleation agent. Influence of different Cr2O3 additions on crystallization structure and properties of CaO-MgO-Al2O3-SiO2 glass-ceramics has been discussed so as to select optimum additions. DTA is employed to determine optimum crystallization and nucleation temperatures; XRD and SEM are used to characterize microstructure of each sample; and performance indexes, such as water absorption, bulk density, flexural strength and so on, are also determined. Experimental results show that when 3wt% Cr2O3 is introduced, fine glass-ceramics with diopside as the main crystal and Ca-Fe diopside as the second-crystal is obtained, and its corresponding performance indexes are as follows: water absorption 0.12%, bulk density 2.56 g/cm3, and flexural strength 70.01 Mpa.     

The role of alkali content in the devitrification mechanisms of SiO2–Fe2O3–Na2O–PbO SYSTEM

Three batch compositions of pure oxides (SiO₂, Fe₂O₃, PbO, Na₂O) with equivalent SiO₂, Fe₂O₃ and PbO contents and a gradually increased Na₂O content were vitrified through heating in a high temperature electric furnace and subsequent quenching. The resulting vitreous products were thermally treated in order to study the devitrification behaviour, under conditions designated from differential thermal analysis experiments. Depending on the Na₂O content, crystal phase separation gave rise to the growth of acmite and hematite or maghemite. A uniformly phase separated glass-ceramic material, with crystallites of similar size and population density, was produced from devitrification of the vitreous product with the higher Na₂O content.     

Er3+和Yb3+共掺氟氧化物微晶玻璃的研究

制备了Er3 、Yb3 共掺的SiO2-A12O3-PbF2-CdF2系统玻璃,并进行相应的微晶化热处理,研究了氟氧化物微晶玻璃中Er3 离子的上转换发光特性.研究结果表明:原始玻璃经热处理后得到的β-PbF2相氟氧化物微晶玻璃,Er3 和Yb3 所在局域基质声子能量的降低,使微晶玻璃中Er3 上转换发光强度显著提高,而微晶化后Er3 、Yb3 离子局域环境发生变化,导致微晶玻璃中Er3 离子的绿光上转换荧光强度较强,而红光上转换荧光强度相对较弱.     

New developments in X-ray storage phosphors

We found a significant PSL effect in Eu²⁺-doped fluorozirconate glasses (ZBLAN) which were additionally doped with Br⁻ or Cl⁻ ions. The PSL is attributed to the characteristic emission of Eu²⁺ present in nano-crystallites of BaBr₂ or BaCl₂, which form in the glass upon annealing. The metastable hexagonal form of BaX₂ (X=Br,Cl) is always formed first before it is converted into the stable orthorhombic form. The particle size increases upon annealing and so does the PSL efficiency of the glass ceramic. However, there is a saturation of the PSL efficiency, which is for Br⁻ doping about 9% and for Cl⁻-doping about 80% of the Eu-doped BaFBr standard. The particle size was determined by transmission electron microscopy (TEM). The TEM results show a clear tendency for bigger particles for longer annealing at the expense of its number. The particle size for the most efficient phosphor is about 100 nm.     

高炉熔渣微晶玻璃的结构与性能研究

高温熔渣具有大量显热与渣体.采用熔融法制备微晶玻璃可以更好地利用其热和渣,达到高效利用的目的.通过高温条件下混熔的方式制备性能稳定的基础玻璃.利用差示扫描量热仪(DSC)确定基础玻璃的热处理工艺制度.结合高分辨透射电子显微镜(TEM)、X射线衍射分析(XRD)、场发射扫描式电子显微镜(FE-SEM)对微晶玻璃的结构进行了研究.研究表明:基础玻璃中氟含量的增加,有利于促进微晶玻璃成核和晶体长大,降低微晶玻璃的形核结晶温度.在低温热处理得到微晶玻璃的主晶相为萤石,高温热处理得到的微晶玻璃析出了霞石和萤石两个微晶相.高炉渣微晶玻璃中,微晶相的出现可有效提高微晶玻璃的力学性能,试样的显微硬度最高可达585.68 MPa,抗折强度最高可达126.21 MPa.