Effect of pressure on the low-temperature reaction of ethylene with N2O4

Calorimetric monitoring of the autoclave reaction N₂O₄ + C₂H₄ at –85 to +10 °C under argon pressure 10–30 bar revealed that the exothermic chemical reaction started at temperatures above –52 °C at 10 bar, whereas an intensive exothermic reaction started at –85 °C and pressure of 30 bar. IR study showed that oligo/polynitroethylene was formed at 30 bar, while carbonyl and hydroxy compound as well as nitrate R–ONO₂ formation occurred upon processing at 10 bar.     

Crystallization of Poly(ethylene adipate) within γ-Phase Poly(vinylidene fluoride) Matrix

The effects of PEA on the γ-phase PVDF crystal structure and the crystallization of PEA within the pre-existing γ-phase PVDF spherulites have been investigated by optical microscopy(OM), infrared spectroscopy(IR) and scanning electron microscopy(SEM). The results demonstrate that the γ-phase PVDF spherulites consist of the lamellae exhibiting a highly curved scroll-like morphology and develop preferentially in PEA-rich blend. With increasing PEA concentration, the scroll diameter increases and the scrolls are better separated from each other. PEA crystallizes first in the interspherulitic region and transcrystalline layer develops. Subsequently, the transcrystalline layer of PEA continues to grow within the γ-phase PVDF spherulites, e.g., in the region between the scrolls, until impinging on other PEA transcrystalline layers or spherulites. The crystallization kinetics results indicate that the growth rate of PEA crystals in the intraspherulitic region of γ-phase PVDF shows a positive correlation with content of PEA, but a negative one with the crystallization temperature of γ-phase PVDF.     

Crosslinked poly(ethylene oxide) containing siloxanes fabricated through thiol‐ene photochemistry

Homogenous amphiphilic crosslinked polymer films comprising of poly(ethylene oxide) and polysiloxane were synthesized utilizing thiol‐ene “ click ” photochemistry. A systematic variation in polymer composition was Carried out to obtain high quality films with varied amount of siloxane and poly(ethylene oxide). These films showed improved gas separation performance with high gas permeabilities with good CO₂/N₂ selectivity. Furthermore, the resulting films were also tested for its biocompatibility, as a carrier media which allow human adult mesenchymal stem cells to retain their capacity for osteoblastic differentiation after transplantation. The obtained crosslinked films were characterized using differential scanning calorimetry, dynamic mechanical analysis, thermogravimetric analysis, FTIR, Raman‐IR , and small angle X‐ray scattering. The synthesis ease and commercial availability of the starting materials suggests that these new crosslinked polymer networks could find applications in wide range of applications. © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2015 , 53, 1548–1557     

Amphiphilic thermoset elastomers from metal‐free,click crosslinking of PEG‐grafted silicone surfactants

The hydrophobicity of silicone elastomers can compromise their utility in some biomaterials applications. Few effective processes exist to introduce hydrophilic groups onto a polysiloxane backbone and subsequently crosslink the material into elastomers. This problem can be overcome through the utilization of metal‐free click reactions between azidoalkylsilicones and alkynyl‐modified silicones and/or PEGs to both functionalize and crosslink silicone elastomers. Alkynyl‐functional PEG was clicked onto a fraction of the available azido groups of a functional polysiloxane, yielding azido reactive PDMS‐g‐PEG rake surfactants. The reactive polymers were then used to crosslink alkynyl‐terminated PDMS of different molecular weights. Using simple starting materials, this generic yet versatile method permits the preparation and characterization of a library of amphiphilic thermoset elastomers that vary in their composition, crosslink density, elasticity, hydrogel formation, and wettability. An appropriate balance of PEG length and crosslink density leads to a permanently highly wettable silicone elastomer that demonstrated very low levels of protein adsorption. © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2015 , 53, 1082–1093     

o-Trityl phenoxy-imino vanadium (III) complexes: synthesis,characterization, and catalysis on ethylene (co)polymerization

Several phenoxy-imine ligands bearing o-trityl group in phenoxy moiety RN=CHArOH (Ar = C₆H₂(CPh₃)^tBu, R = 2,6-Me₂C₆H₃ ( L ₁ H ); 2,6-ⁱPr₂C₆H₃ ( L ₂ H ); 3,5-(CF₃)₂C₆H₃ ( L ₃ H ); 3,5-(OMe)₂C₆H₃ ( L ₄ H ); CHPh₂ ( L ₅ H ); CPh₃ ( L ₆ H )) were synthesized and characterized by¹H NMR and ¹³C NMR spectroscopy. The vanadium complexes based on these ligands LVCl₂(THF)₂ ( 1–6 ) were synthesized via conventional transmetalation reaction in moderate to high yields. Complexes 1–6 were fully characterized by FT-IR, elemental analyses and the molecular structures of 1 , 2 ·H₂O, (2 ·H₂O ) ₂ (μ-Cl) ₂ , 4 , and 5 were confirmed by X-ray crystallographic analysis in which the six-coordinated vanadium centers are in a typical octahedral geometry. Upon activation with Et₂AlCl in toluene, complexes 1–6 showed high activities in ethylene polymerization affording polymers with moderate molecular weight (5.9–11.8 × 10⁴ Da). Moreover, in hexane or CH₂Cl₂, 1–6 /Et₂AlCl exhibited enhanced activities. When activated with MAO or MMAO in toluene, these complexes showed relatively low activities but afforded polymers with ultra-high molecular weight (up to 3.30 × 10⁶ Da). 1–6 /Et₂AlCl also showed high activities in ethylene/1-hexene copolymerization at room temperature giving moderate molecular-weight polymers (6.5–11.4 × 10⁴ Da) with co-monomer incorporation being of 6.0 ~ 7.8%.     

高压结晶PET/PC共混体系中大尺寸聚合物伸直链晶体的形态观察

 大尺寸聚合物伸直链晶体在低维体系物理学的研究中具有不可替代的重要作用。但以往高压合成的聚合物伸直链晶体，尺寸较小且合成时间过长，使其作用至今未能显现。加入10%（质量分数）聚碳酸酯（PC）于聚对苯二甲酸乙二醇酯（PET）中，在研究PET/PC共混体系高压结晶行为的过程中快速合成了大量生长厚度超过100 μm 的聚合物伸直链晶体，并采用扫描电子显微镜对其进行了深入研究。研究表明，高压结晶PET/PC共混体系中存在不同类型的大尺寸伸直链晶体：完善的伸直链晶体、沿平行或垂直于C轴方向发生断裂的伸直链晶体、内聚能密度较大而发生内聚破裂的伸直链晶体、不同断裂方式下呈不同形态的楔形状伸直链晶体以及弯曲的伸直链晶体。同时对不同形态伸直链晶体的形成机理作了阐述。     

Biodegradable/biocompatible ABC triblock copolymer bearing hydroxyl groups in the middle block

New biodegradable/biocompatible ABC block copolymers, poly(ethylene oxide)‐b‐poly(glycidol)‐b‐poly(L ,L ‐lactide) (PEO‐PGly‐PLLA), were synthesized. First, PEO‐b‐poly(1‐ethoxyethylglycidol)‐b‐PLLA was synthesized by a successive anionic ring‐opening copolymerization of ethylene oxide, 1‐ethoxyethylglycidyl ether, and L ,L ‐lactide initiated with potassium 2‐methoxyethanolate. In the second step, the 1‐ethoxyethyl blocking groups of 1‐ethoxyethylglycidyl ether were removed at weakly acidic conditions leaving other blocks intact. The resulting copolymers were composed of hydrophilic and hydrophobic segments joined by short polyglycidol blocks with one hydroxyl group in each monomeric unit. These hydroxyl groups may be used for further copolymer transformations. The PEO‐PGly‐PLLA copolymers with a molecular weight of PLLA blocks below 5000 were water‐soluble. Above the critical micellar concentration (ranging from 0.05 to1.0 g/L, depending on the composition of copolymer), copolymers formed macromolecular micelles with a hydrophobic PLLA core and hydrophilic PEO shell. The diameters of the micelles were about 25 nm. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 3750–3760, 2003     

Synthesis,characterization, and biological activity of [2‐oxo‐2‐(4‐acetyl) phenyl amino] ethylene methacrylate and its derivatives

A new type of methacrylate monomer, [2‐oxo‐2‐(4‐acetyl) phenyl amino] ethylene methacrylate (APEMA), was synthesized. The oxime, 2,4‐dinitrophenylhydrazone, and thiosemicarbazone derivatives of poly{[2‐oxo‐2‐(4‐acetyl) phenyl amino] ethylene methacrylate} [poly(APEMA)] were prepared with hydroxylamine hydrochloride, 2,4‐dinitrophenylhydrazine, and thiosemicarbazone hydrochloride, respectively. The radical homopolymerization of APEMA was performed at 65 °C in a 1,4‐dioxane solution with benzoyl peroxide as an initiator. The monomer and its homopolymer were characterized with Fourier transform infrared and NMR techniques. The thermal stabilities of poly(APEMA) and its derivatives were investigated with thermogravimetric analysis and differential scanning calorimetry. The ultraviolet stability of the polymers were compared. The solubility and inherent viscosity of the polymers were also determined. The number‐average and weight‐average molecular weights and polydispersity index of the polymers were determined with gel permeation chromatography. The antibacterial and antifungal effects of the monomer and the polymer and its derivatives were also investigated on various bacteria and fungi. The activation energies of the thermal degradation of the polymers were calculated with the Ozawa method. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 3157–3169, 2004     

Synthesis and characterization of well‐defined diblock and triblock copolymers of poly(N‐isopropylacrylamide) and poly(ethylene oxide)

Well‐defined diblock and triblock copolymers composed of poly(N‐isopropylacrylamide) (PNIPAM) and poly(ethylene oxide) (PEO) were successfully synthesized through the reversible addition–fragmentation chain transfer polymerization of N‐isopropylacrylamide (NIPAM) with PEO capped with one or two dithiobenzoyl groups as a macrotransfer agent. ¹H NMR, Fourier transform infrared, and gel permeation chromatography instruments were used to characterize the block copolymers obtained. The results showed that the diblock and triblock copolymers had well‐defined structures and narrow molecular weight distributions (weight‐average molecular weight/number‐average molecular weight < 1.2), and the molecular weight of the PNIPAM block in the diblock and triblock copolymers could be controlled by the initial molar ratio of NIPAM to dithiobenzoate‐terminated PEO and the NIPAM conversion. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 4873–4881, 2004     

Studies of photooxidative degradation of poly(vinyl chloride)/poly(ethylene oxide) blends

The photooxidative degradation of blends (in a full range of compositions) of amorphous poly(vinyl chloride) (PVC) with semicrystalline poly(ethylene oxide) (PEO) in the form of thin films is investigated using absorption spectroscopy (UV–visible and Fourier transform infrared) and atomic force microscopy (AFM). The amount of insoluble gel formed as a result of photocrosslinking is estimated gravimetrically. It is found that the PVC/PEO blendsí susceptibility to photooxidative degradation differs from that pure of the components and depends on the blend composition and morphology. Photoreactions such as degradation and oxidation are accelerated whereas dehydrochlorination is retarded in blends. The photocrosslinking efficiency in PVC/PEO blends is higher than in PVC; moreover, PEO is also involved in this process. AFM images showing the lamellar structure of semicrystalline PEO in the blend lead to the conclusion that the presence of PVC does not disturb the crystallization process of PEO. The changes induced by UV irradiation allow the observation of more of the distinct PEO crystallites. This is probably caused by recrystallization of short, more mobile chains in degraded PEO or by partial removal of the less stable amorphous phase from the film surface. These results confirm previous information on the miscibility of PVC with PEO. The mechanism of the interactions between the components and the blend photodegradation are discussed. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 585–602, 2004