Er~(3+)/Tm~(3+)共掺铋硅酸盐玻璃2.0μm光谱性质（英文）

用高温熔融法制备了Er~(3+)/Tm~(3+)共掺杂无铅铋硅酸盐玻璃.测试了玻璃的吸收光谱和荧光光谱,分析和表征了Er~(3+)、Tm~(3+)离子之间的能量传递机制和传递效率,结果表明:在800 nm和1 550 nm光源泵浦下,Er~(3+)的掺入能够增强Tm~(3+)离子1.8μm发光,相应的最大发射截面分别为6.7×10~(-21)cm~2和7.3×10~(-21)cm~2,荧光带宽达到250 nm.根据Dexter-Foster模型,得到Er~(3+):~4I_(13/2)能级到Tm~(3+):~3F_4能级的直接能量传递系数为16.8×10~(-40)cm~6/s,为1 550 nm泵浦下获得较强的1.8μm发光奠定了基础.     

Polarization manipulation of bright-dark vector bisolitons

We simulate the polarization manipulation of bright-dark vector bisolitons at 1-μm wavelength regime.Through changing the pulse parameters,different kinds of pulse shapes and optical spectra are generated in output orthogonal polarization directions.When the input vector bisoliton is polarization-locked with 1064 nm central wavelength,“1+1”fundamental dark-dark and“2+1”pseudo-high-order bright-dark group-velocity-locked vector solitons can be achieved through changing the projection angle.When the input vector bisoliton is group-velocity-locked with 1063 nm and 1065 nm central wavelengths,“2+1”and“2+2”pseudo-high-order bright-dark group-velocity-locked vector solitons,bright-dark group-velocity-locked vector solitons with chirp-like temporal oscillations are generated.Our simulation results can provide beneficial conduct for polarization manipulation of vector multi-solitons,and have promising applications in quantum information register,optical communications,nanophotonics,and all-optical switching.     

掺铥氟磷玻璃的结构、热学性质和光谱性质

制备了不同Al(PO3)3含量的掺铥系列氟磷玻璃,研究了其结构、热稳定性和光谱性质。随着Al(PO3)3含量的增加,该系列玻璃的密度降低,折射率增加,差热分析表明,转变温度、析晶起始温度、析晶峰温度和熔化温度增加。Al(PO3)3摩尔浓度在7%~9%时析晶稳定性最佳。采用归一化的拉曼光谱分析了材料的结构和声子状况,对于该系列氟磷玻璃,Al(PO3)3含量的增加不会影响声子能量,但使声子密度增大。测试了样品的吸收光谱,Tm3 的3H6→3F4在第三通信窗口的L波段有明显吸收。与在其它玻璃基质中相比,Tm3 的3F4能级对应能量偏高,3H4能级对应能量偏低,使得3H4→3F4跃迁波长较大,接近于增益迁移光纤放大器的放大波长。扎得奥菲而特(Judd-Ofelt)理论分析表明随着Al(PO3)3含量增加,离子强度参量Ω2增大,Ω6保持相对稳定,Tm3 的能级寿命降低。     

Effect of lithium-potassium mixed alkali on spectroscopic properties of Er^3＋-doped aluminophosphate glasses

Er^3＋-doped lithium-potassium mixed alkali aluminophosphate glasses belonging to the oxide system xK2O-（15-x）Li2O-4B2O3-11Al2O3-5BaO-65P2O5 are obtained in a semi-continuous melting quenching process. Spectroscopic properties of Er^3＋-doped glass matrix have been analysed by fitting the experimental data with the standard Judd-Ofelt theory. It is observed that Judd-Ofelt intensity parameters Ωt（t = 2, 4 and 6） of Er^3＋ change when the second alkali is introduced into glass matrix. The variation of line strength Sed[^4I13/2,^4I15/2] follows the same trend as that of the/26 parameter. The effect of mixed alkali on the spectroscopic properties of the aluminophosphate glasses, such as absorption cross-section, stimulated emission cross-section, spontaneous emission probability, branching ratio and the radiative lifetime, has also been investigated in this paper.     

铋掺杂砷化镓晶体的坩埚下降法生长研究

使用<511>取向GaAs籽晶,在直径2英寸的pBN坩埚中生长了2.5;Bi掺杂的GaAs晶体.能量分散谱仪(EDS)和透过光谱均有Bi相关谱峰的存在,说明Bi原子已掺杂到GaAs晶体中.X射线双摇摆曲线测得半高峰宽值为42".与未掺杂GaAs晶体相比,所得晶体的禁带宽度出现红移,从1.43 eV移至近1.39 eV.扫面式电子显微镜(SEM)显示晶体中存在少量富Bi包裹物,晶体质量有待进一步改进.     

Effects of Yb^3＋ in Er^3＋/Yb^3＋ Codoped Fluorophosphate Glasses

For the Er^3＋ /Yb^3＋ codoped fluorophosphate glasses, Judd-Ofelt theory is used to analyse the influence of YbF3 as not a sensitizer but an average component on the spectroscopic properties around 1530nm emission. The double roles of Yb^3＋, as a sensitizer and as an average component, are discussed. It is found that Yb^3＋ as an average component contributes to the increase of fluorescence lifetime, and Yb^3＋ as a sensitizer has the best sensitization when its concentration is 2.4 mol%.     

GaAs晶体坩埚下降法生长及掺杂效应

作为第二代半导体材料,GaAs晶体自60年前被发现以来已广泛应用于激光、通讯和显示等领域,并发展出液封提拉法、水平布里奇曼法、垂直梯度凝固法等多种生长工艺.本文总结了GaAs晶体的最新研究进展,探讨了各种生长方法的特点及其应用,重点报道了GaAs晶体坩埚下降法生长的研究成果.坩埚下降法具有一炉多产、易操作、低成本等优点,已成为GaAs晶体产业化的重要途径.掺杂不仅能调节GaAs晶体的性能,还会对晶体生长产生重要影响.本文还给出了Bi、Si、Zn等掺杂GaAs晶体生长结果,探讨了它们的性能、缺陷以及在不同领域里的应用.     

LED用硅掺杂GaAs晶体的生长与表征

采用坩埚下降法生长了LED用硅掺杂<511>取向的GaAs晶体.选用带籽最槽的PBN坩埚作为生长容器,密封在石英安瓶中以防止生长过程中As蒸汽挥发.研究了掺杂工艺、固液界面形貌和生长缺陷.结果表明:孪晶化是硅掺杂GaAs晶体生长的主要问题.探讨了孪晶形成机理,优化了生长工艺,成功获得了直径2英寸高质量的硅掺杂GaAs晶体,双摇摆曲线显示所得晶体的FWHM为40 arcsec.     

Eu2+、Mn2+、Sr2+掺杂BaMgAl10O17的燃烧法合成及光致发光性能研究

在600℃温度下,采用液相燃烧法合成了Sr²⁺、Eu²⁺和Mn²⁺三掺的BaMgAl₁₀O₁₇（BAM）蓝绿荧光粉。用XRD、SEM和荧光光谱仪分别分析和表征该荧光粉的物相、形貌和光致发光性能。结果表明,液相燃烧法合成BAM的温度明显低于传统的高温固相合成法;合成的纳米棒均匀、无团聚现象;荧光光谱仪分析表明Eu²⁺、Mn²⁺离子间存在能量传递,且Sr²⁺能有效提高BAM的发光强度,约为固相法制备荧光强度的1.8倍。BAM：0.1Eu²⁺,0.04Mn²⁺,0.05Sr²⁺色坐标为（0.146,0.250）,属于蓝绿光。     

Eu2+、Mn2+、Sr2+掺杂BaMgAl10O17的燃烧法合成及光致发光性能

在600℃温度下,采用液相燃烧法合成了Sr²⁺、Eu²⁺和Mn²⁺三掺的BaMgAl₁₀O₁₇（BAM）蓝绿荧光粉。用XRD、SEM和荧光光谱仪分别分析和表征该荧光粉的物相、形貌和光致发光性能。结果表明,液相燃烧法合成BAM的温度明显低于传统的高温固相合成法;合成的纳米棒均匀、无团聚现象;荧光光谱仪分析表明Eu²⁺、Mn²⁺离子间存在能量传递,且Sr²⁺能有效提高BAM的发光强度,约为固相法制备荧光强度的1.8倍。BAM：0.1Eu²⁺,0.04Mn²⁺,0.05Sr²⁺色坐标为（0.146,0.250）,属于蓝绿光。