γ-LiAlO2晶体生长、改性和热学性质研究

采用快速提拉法生长出了透明、完整的γ-LiAlO2晶体,但是晶体的高熔点和易挥发性限制了γ-LiAlO2晶体质量.采用气相传输平衡法(vapor transport equilibration technique,VTE)工艺对晶体改性,半高宽(FWHM)值从116.9arcsec降至44.2arcsec,继续升高VTE处理温度至1300℃,FWHM值反而升高至55.2arcsec.快速提拉法生长出来晶体,[100]方向和[001]方向的热膨胀系数分别为17.2398×10-6/K,10.7664×10-6/K.经过三步VTE处理后[100]和[001]方向热膨胀系数降至16.6539×10-6/K和10.1784×10-6/K.     

Coherence-Like States of Two Coulomb-Correlated Ions Confined in a Paul Trap

We report the n x n＇ coherence-like state solutions in the cases of n, n＇ = 1, 2,... for the system including two Coulomb-correlated ions confined in a one-dimensional Paul trap with a time-dependent harmonic potential. One of the n＇ exact solutions of the centre-of-mass motion describes a generalized coherent state. For a small driving strength the n approximate solutions of relative motion are constructed, which describe the coherent oscillations of the two ions around the classical equilibrium position.     

Yb∶YAG晶体的晶胞参量及Yb~(3+)分凝系数的研究

应用提拉法生长出不同Yb3+ 浓度的Yb3xY3( 1-x) Al5O12 晶体 Yb3+ 离子的分凝系数 1是 1 .0 8±0 .0 1 ,与Yb3+ 离子掺杂浓度无关 研究了Yb3xY3( 1-x) Al5O12 晶体的晶胞参量 ,推导出联系晶胞参量、密度与Yb3+ 离子掺杂浓度的关系方程式     

Annealing effect on Cr,Yb:YAG laser crystal

The absorption spectra, fluorescence spectra, and lifetimes of as-grown and annealed Cr,Yb:YAG crystal grown by Czochralski technique have been measured. The broad absorption bands in the visible region increase in intensity and shift to long wavelength after annealing, and the additional absorption around 482 nm may be possibly due to new octahedral Cr4+ center in the crystal, and the increase in the infrared (IR) region is due to the increase of Cra+. The increase of Cr4+ also results in the groud state absorption and the concentration quenching of Ybs+ in Cr,Yb:YAG crystal after annealing, the fluorescence intensity is reduced to 75% and the emission lifetime is shortened from 1.40 to 0.44 ms.     

U：CaF2晶体的分凝特性与光谱性质

应用TGT法生长了直径为75mm的U：CaF2晶体，宏观上透明完整.应用公式K0=Cs/Cl计算了U在CaF2晶体中的分凝系数等于0.53.应用溶质分布一般公式Cs=K0C0(1-g)K0-1，计算U的浓度分布与测量值，数值符合说明晶体生长过程接近平衡状态.分析不同条件下生长的U: CaF2晶体的晶胞参数和吸收光谱，结果表明生长气氛决定U的价态及电荷补偿机理：无PbF2存在的条件下，U为+4价，晶体呈绿色；PbF2的加入起到氟化去氧作用，U倾向于以离子半径最接近于Ca2+的U3+存在，晶体呈红色.从晶体生长开始到结束的部位，U3+:CaF2晶体吸收光谱的峰位不变，峰强呈现与U浓度相同的增加趋势.U3+:CaF2晶体外层厚约5mm处呈黄色，含有U3+和U2+的混合价态离子，其原理是石墨坩埚的还原作用通过单质铅，使部分的U3+进一步还原成了U2+. 关键词： 铀 氟化钙晶体 分凝系数 晶胞参数     

温度梯度法生长的Ce:YAlO3高温闪烁晶体的光谱分析

采用温度梯度法生长了熔体掺杂Ce浓度为1at%的YAlO3晶体,对于其吸收光谱、荧光光谱和x射线激发发射谱进行了表征分析.根据吸收光谱提出了一个色心模型,从而成功的解释了为什么刚生长出的晶体为粉红色,而分别经氢气和空气在1400℃退火后均能变为无色的现象和退火以后吸收光谱发生的显著变化.温度梯度法生长的Ce:YAP在330nm处存在着一定程度的自吸收和自激发.光致激发发射谱的发射主峰在368nm,而x射线激发发射谱的主发射峰红移至391nm,这表明在x射线激发下,晶体对发射光的自吸收将会减少.另外在x射线激发发射谱上,经H2退火和空气退火后的样品其发射强度比未退火的晶体要强.     

Spectra Analysis of a Novel Ti-Doped LiAlO2 Single Crystal

LiAlO2 single crvstals doped with Ti at concentration 0.2at.% are grown by the Czochralskl technique with dimensions φ42×55mm. Ti ions in the crystal are quadrivalence proven by comparing the absorption and fluorescence spectra of pure LiAlO2 and Ti： LiAlO2. After air and Li-rich atmosphere annealing, the absorption peaks in the range of 600-800nm disappear. We conclude that 682 and 756nm absorption peaks are attributed to the VLi and Vo absorptions, respectively： The peaks at 716nm and 798nm may stem from the VLi^＋ and absorptions. The colour-centre model can be applied to explain the experimental phenomena. Ti^4＋-doping produces more lithium vacancies in the LiAlO2 crystal. The intensities of [LiO4] and the associated bonds remain unchanged, which improves the anti-hydrolyzation and thermal stability of LiAlO2 crystals.     

γ-辐照对纯Y_2SiO_5和Eu~(3+)∶Y_2SiO_5晶体光谱性能的影响

研究了γ-辐照前后纯Y2SiO5和Eu3+掺杂的Y2SiO5晶体吸收光谱的变化,辐照后,未退火和氢气退火的纯Y2SiO5晶体在260~270 nm和320 nm波段产生了附加吸收峰,分别是由F心和O-心的吸收引起的;经过空气退火的纯YSO晶体中,由于消除了氧空位,因此辐照后没有出现色心吸收峰。在Eu3+∶Y2SiO5晶体中,不但有相同的F心和O-心吸收峰,而且还有Eu2+离子在300 nm和390 nm的吸收峰。随着辐照剂量的增加,色心附加吸收峰增强。空气退火能减少Eu3+∶Y2SiO5晶体中的色心,而氢气退火能增加色心。     

紫外激光通信中PPM与Turbo联合编码调制研究

为提高紫外激光通信系统中的编码效率和频带利用率，提出采用PPM（pulse position modulation）调制和Turbo编码相结合的技术来提高效率。此方法不仅能提高频带的利用率，也能提高码间抗干扰能力、纠错能力和降低误码率，并对PPM调制模式下的Turbo码译码公式进行了推导，最后利用Matlab软件实现了该技术的仿真，仿真结果表明：在紫外激光通信中采用PPM和Turbo统一调制编码的技术能进一步降低系统的效率和误码率。     

掺Yb3+氧化镧钇透明激光陶瓷的光谱特性

采用传统陶瓷烧结工艺,在无压还原气氛下低温制备出透明性良好的掺Yb3+氧化镧钇透明激光陶瓷,测试了其在室温下的吸收光谱、发射光谱和荧光寿命.结果表明,掺Yb3+氧化镧钇透明激光陶瓷的吸收系数随着Yb3+掺杂浓度的增加而增大,最强吸收峰974nm处的吸收截面为0.90～1.12×10－20 cm2;主发射峰1 032 nm和1 075 nm处的发射截面分别为1.05×10－20 cm2和0.87×10－20 cm2; Yb3+掺杂浓度为5at.%时荧光寿命为1.38 ms,并随Yb3+掺杂浓度的增加而减小;当Yb3+掺杂浓度超过10at.%时,样品中存在严重的浓度猝灭.产生浓度猝灭的原因是高掺杂时离子间存在合作上转换和能量转移.