PVP为模板控制合成球形碳酸钙

Spherical calcium carbonate was prepared by the reaction of sodium carbonate with calcium chloride at the presence of a protein-like molecule， polyvinylpyrrolidone， as the template. The products were characterized by elemental analyses， XRD， SEM， and TG-DSC respectively. The effects of polyvinylpyrrolidone on the crystal form and morphology of the as-prepared CaCO₃ were investigated. It was found that the aggregative shape of the produced calcium carbonate crystalline could be well controlled by adjusting the concentration of the polyvinylpyrrolidone template. This may be of important meanings to the biomimetic synthesis of novel inorganic materials.     

镁离子存在下乙醇-水混合溶液中碳酸钙结晶行为的研究

通过对不同反应体系中合成样品的物相及镁含量变化规律的分析, 认为水溶液中碳酸钙的结晶遵循溶解重结晶机理, 乙醇-水溶液中则以聚集重构为主, 碳酸根阴离子的溶剂化作用对碳酸钙的沉积产生显著影响. 采用XRD, IR等手段对醇水混合溶液中合成的碳酸钙样品进行分析, 认为形成了含镁方解石及具有类白云石结构的过渡相同时存在的混合物相, 醇水溶液中含镁方解石趋于白云石化.     

层状CuyFe6-yAl2Ox催化剂的制备及其在罗丹明B降解反应中的应用

以铜铁铝水滑石为前驱体,经焙烧后得到了一系列不同组成的层状铜铁铝混合氧化物催化剂。将其应用于中性条件下高浓度罗丹明B(450 mg·L^-1)的类芬顿降解反应中,考察了催化剂中铜铁比例及焙烧温度对其降解性能的影响。实验结果表明,当铜铁物质的量之比为5∶1、焙烧温度为500℃时所得到的Cu5FeAl2Ox-500催化剂对罗丹明B的降解效率最高,能够在150 min内将罗丹明B完全降解。表征结果发现,Cu5FeAl2Ox-500催化剂中生成了新的CuFe2O4物相,而且具有较大的比表面积和介孔体积,因而有利于罗丹明B的降解。同时还发现该催化剂对多种污染物的降解均有很好的效果。     

掺C60二氧化钛微晶特性和光催化活性研究

通过热分析、X射线衍射以及光活性测试,分析了不同掺杂量、不同燃烧温度下掺杂C60二氧化钛微晶样品,研究了掺杂对二氧化钛光活性的改善情况,C60掺杂二氧化钛体系中C60的热解温度明显提前,二氧化钛的晶化温度延迟、相变受到抑制且光活性得到一定程度的提高,其微晶参数也有一定规律变化。     

制备条件对纳米掺铁二氧化钛微晶结构的影响

在溶胶-凝胶方法制备掺铁二氧化钛过程中,观察了不同的恒温水浴温度、不同的体系加水量对凝胶形成时间的影响 ,并对此提出了初步的解释. 采用 X射线衍射和 V oig t函数单峰分析方法计算了不同反应温度和不同体系含水量下得到的干凝胶粉在 500℃煅烧 3h后的晶粒度及( 101)晶面上的畸变与晶胞参数. 结合样品的透射电镜和电子衍射照片 ,分析了晶粒度与制备条件的关系,并作出了初步解释.并观察到( 101)晶面上的畸变与晶粒度有着相反的变化趋势