Preparation and characterization of nanosized TiO2 powder as an inorganic adsorbent for aqueous radionuclide Co(II) ions

In this research TiO₂ sample was synthesized by a simple sol–gel method and was characterized by X-ray diffraction (XRD), Transmission electron microscopy (TEM) and Brunauer–Emmett–Teller (BET) techniques. The XRD result indicated that the obtained product was anatase titanium dioxide with high purity, the TEM image clearly showed that the particle sizes of TiO₂ nanoparticles were in the range of 30–70 nm, and the measured BET surface area of the heated TiO₂ nanoparticles was 147.14 m²/g. In this work, the prepared TiO₂ sample was used as a new adsorbent for the adsorption of radionuclide Co(II) ions from aqueous solutions, and the influence of pH, contact time, ionic strength and temperature in the presence or absence of humic acid/fulvic acid (HA/FA) were also investigated. The experimental results indicated that the adsorption of Co(II) ions onto TiO₂ was strongly pH-dependent. Based on the surface complexation, the presence of HSs enhanced the adsorption of Co(II) ions and the influence of Co(II) adsorption onto FA–TiO₂ hybrids was much stronger than that of HA–TiO₂ at pH values of 2.0–9.0. Adsorption of Co(II) ions onto TiO₂ powder was strongly dependent on ionic strength. The adsorption process mainly occured in the first contact time of 2 h and could be fitted by a pseudo-second-order rate model. The calculated thermodynamic data indicated that the adsorption of Co(II) ions onto TiO₂ was a spontaneous process and favorable at high temperatures.     

Preparation of an Mo and C co-doped TiO2 catalyst by a calcination–hydrothermal method, and degradation of rhodamine B in visible light

Mo and C co-doped TiO₂ photocatalysts were successfully prepared by a calcination–hydrothermal method. The catalysts were characterized by XRD, XPS, DRS, FTIR, and Raman spectroscopy. Results from photocatalysis showed that 1%Mo–C4/TiO₂ had excellent visible light photocatalytic activity. This may be ascribed not only to the Mo and C doping but also to synergism between the Mo and C.     

Comparative study on structure and properties of titanium/silicon mono‐ and co‐doped amorphous carbon films deposited by mid‐frequency magnetron sputtering

The titanium/silicon mono‐ and co‐doped amorphous carbon films were deposited by mid‐frequency magnetron sputtering Ti target, Si target, and Ti80S20 alloy target, respectively. The effects of doped elements on the composition, surface morphology, microstructure, and mechanical and tribological properties of the films were investigated. The results reveal that the ratio of sp³ and sp² carbon bonds of the films is regulated between 0.28 and 0.62 by a combination of Ti and Si dopant. The addition of small amounts of silicon leads to an increase in sp³ bonds and disorder degree of the sp² carbon. The co‐doped film exhibits significantly superior friction performance than the mono‐doped films. The ultra‐low friction (μ < 0.01) was achieved under a load of 2 N in ambient air with 40% RH. By comparing to the mono‐and co‐doped films, it is thought that the sp³/sp² ratio of the films may play a key role for the superlow friction. Copyright © 2013 John Wiley & Sons, Ltd.     

The effect of the change in the microscopic structures of the iron on corrosion resistance and passivated properties

The passive film of iron showed n‐type semiconductor characteristic in borate buffer solution, and its donor concentration increased slightly after tensile strain in the present study. However, comparing with solution‐annealed sample, the anodic passive film formed on tensile‐strained one was highly protective. The more dislocations on tensile‐strained sample promoted the diffusion of iron and oxygen vacancy. Moreover, more donor density (mainly oxygen vacancies) promoted the diffusion of oxygen. They all facilitated tensile‐strained sample to form Fe₂O₃ and thicker passive film on the surface. More Fe₂O₃ and thicker passive film on the surface of tensile‐strained iron could improve corrosion resistance. Copyright © 2014 John Wiley & Sons, Ltd.     

Synthesis of 5-alkyl-5-aryl-1-pyrroline N-oxides from 1-aryl-substituted nitroalkanes and acrolein via Michael addition and nitro reductive cyclization

A general method for accessing 5-alkyl-5-aryl-1-pyrroline N-oxides (AAPOs) has been established using readily available aryl bromides, nitroalkanes, and acrolein as the starting materials. The palladium-catalyzed arylation of nitroalkanes gave the 1-aryl-substituted nitroalkanes, which underwent the Et₃N-catalyzed Michael addition with acrolein at room temperature to afford the 4-aryl-4-nitroaldehydes. The latter were then subjected to the nitro reductive cyclization using Zn–HOAc in EtOH at 0 °C followed by warming the reaction mixture to room temperature for 24 h, furnishing the 5-alkyl-5-aryl-1-pyrroline N-oxides in good overall yields. Selected examples of 1,3-dipolar cycloaddition of the cyclic nitrones with methyl methacrylate were also described.     

气驱油油气混相过程的界面传质特性及其分子机制

油气混相过程的界面传质特性对气驱提高原油采收率技术非常重要。本文针对吉林某油田的实际油组分,采用分子动力学模拟研究了气驱油过程,分析了不同气体和驱替压力下油气两相的状态变化以及界面特性,获得不同驱替气体的最小混相压力(MMP)。结果表明,随着驱替气体压力的升高,气相的密度逐渐增大,油相膨胀密度降低,气相与油相的混合程度增强,油气两相界面厚度增加,界面张力随之减小。同时发现,驱替相中二氧化碳浓度越高,在同等气体压力下,油气界面更厚,油气混合程度更高。纯CO₂驱油得到的MMP远远小于纯N₂驱油,当这两种气体摩尔比为1 : 1混合时MMP介于两种纯气体之间,说明要达到同样的驱油效果二氧化碳需要的压力更小。最后,本文从分子微观作用力角度解释了驱替气体不同时影响油气混相程度的机制,通过分子平均作用势曲线发现油相分子对CO₂的吸引力要大于N₂分子,因此CO₂分子更容易与油相混合,驱替效果更明显。     

Kinetically rate-determining step modulation by metal—support interactions for CO oxidation on Pt/CeO2

Science China Chemistry - Rational design and performance promotion are eternal topics and ultimate goals in catalyst preparation. In contrast, trial—and—error is still the common...     

Microwave-assisted Catalyzed Synthesis and In vitro Bioactivity Evaluation of Benzimidazoles Bearing Phenolic Hydroxyl

An efficient and facile method was introduced for the synthesis of benzimidazoles in this paper. The optimum reaction conditions were determined. A series of benzimidazoles bearing phenolic hydroxyl(2a-2t) were synthesized in moderate to excellent yields starting from differently substituted hydroxyl benzaldehyde and 4-position substituted o-phenylenediamine via nucleophilic addition in the presence of catalyst Na₂S₂O₅ under microwave irradiation condition. Herein, effects of the catalyst, molar ratio of reactants, reaction temperature and solvent were investigated. The optimal reaction condition was determined. The effect of DMF and EtOH solvent on the reaction was compared. The synthesized compounds were characterized by FTIR, HRMS, ¹H NMR and ¹³C NMR spectroscopy. Further, the bacteriostatic activities of the synthesized compounds were evaluated with ciprofloxacin and itraconazole as a positive control, respectively. Compounds 2b, 2n, 2q and 2r exhi-bited some antibacterial activity. The lowest MIC of antibacterial activity of compound 2b was 32 μg/mL. Meanwhile, the luminescence property of compound 2b was studied. The antibacterial activity of compound 2b, along with their good fluorescence performance highlighted the potential of these compounds as lead structures and owned fluorescence trace for further study towards the development of novel drugs and functional mechanisms in living organisms.     

金刚石纳米线氮空位色心的表面与尺寸效应

使用大规模自旋极化密度泛函理论计算研究了表面修饰和尺寸对金刚石纳米线(DNs)中氮空位(NV)色心的几何结构、 电子结构、 磁性和稳定性的影响. 理论上设计了几种不同的DNs, 这些DNs具有不同的表面修饰(干净、 氢化和氟化), 并且直径达数百个原子. 实验结果证明, 中性(NV⁰)和带1个负电荷(NV^-)的NV色心的电子结构不受半导体表面修饰和DNs直径大小的影响, 但NV色心的稳定性对这两个因素具有不同的响应. 此外, 研究中还发现, 由于DNs中存在圆柱形表面电偶极子层, 对DNs中掺杂的NV^-色心的稳定性, 表面改性诱导了不依赖尺寸的长程效应. 特别地, 对于n型氟化金刚石表面, 掺杂在DN中的NV^-色心可以稳定存在, 而对于p型氢化表面, NV⁰则相对更稳定. 因此, 表面修饰为控制金刚石纳米线中的NV色心的电子结构和稳定性提供了一种精确有效的调控方法.     

纳米Pd和Au催化CO2还原粒径效应的密度泛函理论计算研究

以可再生能源为能量来源,在水溶液中进行的光(电)催化CO₂还原生成高附加值化学品和燃料是解决能源危机与环境污染的有效途径之一.CO是一种简单却很重要的CO₂还原产物,它可以作为水煤气变换反应与费托合成的重要原料.具有较高CO选择性的贵金属纳米颗粒催化剂(如Au和Pd)一直受到研究者的广泛关注.一般来说,金属颗粒催化剂的催化性能与粒径大小密切相关,即所谓的粒径效应.然而在实际的理论计算研究中,由于受到计算能力的限制,催化剂模型都仅局限于简单的周期性模型或小的金属团簇模型,无法准确描述真实颗粒上复杂的反应位点的性质,导致了对催化行为的误解.因此,建立更加真实的颗粒模型对探究纳米颗粒催化剂上活性位点的性质,解释其粒径效应至关重要.本文旨在阐述Au与Pd纳米颗粒催化剂不同活性位点上CO₂还原反应与产H2副反应的竞争机制,并解释Au与Pd纳米颗粒催化剂在CO₂电还原中表现出不同粒径效应的原因.本文基于密度泛函理论,采用VASP软件,BEEF-vdW泛函进行计算.分别建立了原子数为55,147,309和561的颗粒模型和高CO^*覆盖度模型,避免了传统周期性模型的局限性,探究了金属颗粒催化剂不同反应位点上的CO选择性.结果表明,对于颗粒模型来说,(100)位点对CO的选择性优于边缘位点;但对于周期性模型来说,Au(211)对CO的选择性则优于Au(100).产生这种反差的主要原因在于Au颗粒的边缘位点对H*的吸附过强.通过对比,我们直观地展现了颗粒模型上平面位点和Edge位点与相对应的周期性模型上CO选择性的区别,突出了模型选择对揭示活性位点性质的重要性.在此基础上,通过计算理论CO法拉第效率,发现Au颗粒随着粒径的减小,CO选择性降低,与实验的趋势一致.对于Pd催化剂来说,低覆盖度模型无法正确预测活性位点的性质;而高CO覆盖度的情况下,Pd颗粒的边缘位点对COOH^*吸附能更强,这是导致边缘位点上CO选择性更高的主要原因.同样通过计算理论CO法拉第效率,发现随着粒径的减小,Pd颗粒上CO选择性升高.本文不仅成功揭示了Au与Pd颗粒催化剂上活性位点的性质,对粒径效应做出了合理解释,也强调了合理的计算模型是理论研究的基础.