IM-5分子筛在Ni-Cu催化剂甲烷热裂解制氢反应中的作用研究

甲烷热裂解制氢并生成高附加值的纳米碳材料,被认为是极具发展前景的氢气生产途径,但高性能催化剂的研发仍存在诸多挑战.我们选择多种载体(TS-1、 IM-5、 Y、介孔SiO₂、 γ-Al₂O₃、 CNTs),采用浸渍法制备Ni-Cu负载催化剂,通过低温N2吸附-脱附、 XRD、 SEM和H₂-TPR等系列表征方法对样品进行分析,考察不同载体对催化剂甲烷裂解制氢和纳米碳材料的影响.实验结果发现,分子筛载体独特的孔道结构有利于金属颗粒的分散,能有效避免反应中界面效应导致的催化剂失活,可提高催化剂反应活性并延长反应寿命,也显著提高了其碳产率.其中以IM-5分子筛为载体的催化剂表现最佳,在反应温度为700℃时, NiCu/IM-5催化剂甲烷转化率高达80%,氢气选择性达100%,反应400 min后活性未见明显降低. NiCu/IM-5催化剂碳产率高达1 446 g_C/g_cat,是NiCu/SiO₂催化剂的5.7倍, NiCu/γ-Al     

原子层沉积构筑Pd/TiO2限域催化剂及其在1,4-丁炔二醇加氢的应用

利用ALD制备了TiO₂限域的Pd催化剂, 研究了限域空间内Pd纳米颗粒与TiO₂的界面作用对1,4-丁炔二醇(BYD)加氢性能的影响. 相比于管外负载型催化剂, 限域催化剂在催化1,4-丁炔二醇选择性加氢反应中体现出非常高的催化活性和1,4-丁烯二醇的选择性. HR-TEM、 EDX-Mapping、 XRD、 XPS和H₂-TPR表征说明, 限域体系中Pd-TiO₂的界面相互作用强于传统TiO₂表面负载型Pd催化剂, 这种强界面作用不仅能够提高BYD的加氢活性, 也可抑制半加氢产物1,4-丁烯二醇的异构化和深度加氢, 提高1,4-丁烯二醇的选择性, 而且限域结构也可阻止管内壁Pd纳米颗粒的脱落, 提高催化剂的稳定性.     

不同聚合物分散剂对Pt/SAPO-11催化剂性能的影响

采用浸渍法制备了经过不同聚合物分散剂处理的Pt/SAPO-11催化剂,并通过X射线衍射(XRD)、透射电子显微镜(TEM)、N₂吸附-脱附和NH₃程序升温脱附(TPD)等对催化剂的组织结构进行了表征。结果表明,分散剂不会破坏催化剂的结构,反而提高了其孔体积、孔径和比表面积,同时改变了沸石的酸强度和酸量,其中以聚乙烯吡咯烷酮处理的Pt/SAPO-11催化剂孔体积、孔径和酸性分布最佳。在固定床反应器上对不同分散剂处理的Pt/SAPO-11催化剂催化性能进行评价,结果表明聚乙烯吡咯烷酮处理的Pt/SAPO-11催化剂也表现出最佳的催化性能,麻风树油的加氢脱氧率高达99.45%,生物航空煤油组分收率和异构烷烃组分(C₈~C₁₆)的选择性分别达到了44.67%和56.37%。     

离子液体修饰对Cu/USY催化乙炔氢氯化反应性能的影响

为了提高Cu/USY催化剂在乙炔氢氯化反应中的催化活性,设计并成功制备了一系列离子液体修饰的分子筛负载的铜基催化剂(Cu@TPPB/USY).当铜和TPPB的百分含量均为15时,在反应温度为160℃,乙炔气体空速为120 h-1,氯化氢与乙炔的摩尔比为1.25:1的条件下,催化剂的乙炔转化率提升了1.17倍,氯乙烯选择性一直保持在98%以上.结合催化剂的傅里叶红外(FT-IR)、 N2物理吸脱附(BET)、热重分析(TG)、 X射线光电子能谱(XPS)、透射电镜(TEM)、 X射线衍射(XRD)、氢气程序升温还原(H2-TPR)和等离子体发射光谱(ICP-OES)的表征,认为TPPB的修饰不仅可以促进催化剂中Cu物种的分散,抑制其还原和流失,还能减少催化剂表面积碳、增强Cu活性物种与载体间的相互作用力,有效地提高Cu/USY催化剂的催化活性.     

团簇Au/CeO2的制备及其催化CO氧化反应构效关系的研究

负载型Au催化剂因其在诸多反应过程中的高催化活性而备受研究者关注.然而针对负载型催化剂中Au物种结构的有效调控,以及催化过程中真实构-效关系的探索一直充满了挑战.用CeO₂为Au物种担载基底,通过简单煅烧处理引起的CeO₂结构变化,进而实现Au/CeO₂之间界面作用力的调控.此研究发现Au纳米颗粒中Au⁰物种具备更为高效的催化室温CO氧化活性,结合多种原位表征分析,其室温条件下催化转化效率更依赖于CO吸附能力.而相比于单原子Au₁和纳米Au颗粒,所制备的团簇Au/CeO₂催化剂在较高温度(>50℃)展现出优异的催化CO氧化反应性能.随着温度升高,催化剂表界面O参与的MvK反应路径更易发生,因此具有更多表界面活性O物种和Au^δ+位点的团簇Au/CeO₂催化剂展现出最为优异的催化CO氧化性能.这些发现为高效负载型Au催化剂的制备提供了新思路并深化了对Au/CeO₂催化作用机制的理解.     

分级孔结构的Fe-N-C催化剂用于高效电催化氧还原

氧还原反应（ORR）是金属空气电池以及质子交换膜燃料电池（PEMFCs）系统重要的阴极反应,研究具有高活性与高稳定性的非贵金属催化剂具有重要意义。本研究使用了一种具有分级孔结构的MIL-101-(Al-Fe)作为金属前驱体模板,成功制备出具有分级多孔结构的Fe-N-C催化剂。电化学测试结果表明,在0.1 mol/L KOH电解液中,Fe-N-C-MIL-900催化剂表现出最优的氧还原性能（半波电位0.905 V以及5000圈CV测试后半波电位仅下降5 mV）,远高于纯碳基N-C-MIL-900催化剂（0.845 V）。通过旋转环盘电极测试发现,Fe-N-C-MIL-900催化剂ORR电子转移数为3.98,H2O2产率低于3%,表现出明显的4电子ORR路径。这一工作为制备具有高ORR活性的Fe-N-C催化剂提供了一种新的途径。     

Rh@Pt内凹立方体核壳催化剂的制备及其乙醇电氧化性能

贵金属Rh基催化剂可有效催化乙醇中C―C键断裂,有利于实现乙醇完全电氧化,但Rh催化剂对乙醇电氧化的催化活性较低。本文通过种子介导生长法制备了具有内凹立方体形貌的Rh@Pt/C核壳催化剂,考察了不同Pt壳层厚度的Rh@Pt/C核壳催化剂在碱性介质中对乙醇电氧化反应(EOR)的催化性能。其中Rh@Pt_0.25/C核壳催化剂对EOR的质量归一化电流最高为520 mA/mg,此时面积归一化电流也最高,为0.16 mA/cm²。研究表明,Rh@Pt/C核壳催化剂中Rh和Pt之间的表面应变效应和电子配体效应取决于Rh表面Pt壳层的厚度,Pt壳层厚度的改变,可调控催化剂中Rh和Pt的协同作用,从而减弱毒性中间体对催化剂表面的吸附,优化催化剂对EOR的性能。总体上,Rh表面Pt壳层为3层的Rh@Pt_0.25/C核壳催化剂表现出最优的EOR活性和稳定性,此时催化剂也兼具了较优的抗毒化能力。     

CoMn@NC催化5-羟甲基糠醛常压氧化为2, 5-呋喃二甲酸二甲酯

Dimethyl furan-2, 5-dicarboxylate (DMFDCA) is a valuable biomass-derived chemical that is an ideal alternative to fossil-derived terephthalic acid as a monomer for polymers. The one-step oxidation of 5-hydroxymethylfurfural (HMF) to DMFDCA is of practical significance. It not only shortens the reaction pathway but also avoids the separation process of intermediates; thus, reducing cost. In this work, non-noble bimetallic catalysts supported on N-doped porous carbon (CoMn@NC) were synthesized via a one-step co-pyrolysis procedure using different pyrolysis temperatures and proportions of metal precursors and additives. We employed the prepared CoMn@NC catalysts in the aerobic oxidation of HMF under mild reaction conditions to obtain DMFDCA. High-yield DMFDCA was obtained by screening the prepared catalysts and optimizing the reaction conditions, including the strength and amount of the base, as well as the reaction temperature. The optimized yield of DMFDCA was 85% over the Co₃Mn₂@NC-800 catalyst after 12 h at 50 ℃ using ambient-pressure oxygen. The physicochemical properties of the catalysts were determined using a variety of characterization techniques, the factors affecting the performance of each catalyst were investigated, and the relationship between the physicochemical properties and performance of the prepared catalysts was elucidated. A porous structure with a high surface area had a positive effect on mass transfer efficiency. Cobalt nanoparticles (NPs) and atomically dispersed Mn were coordinated to N-doped carbon to form M―N_x (where M = Co or Mn). Based on the Mott-Schottky effect, there was significant electron transfer between each metal and the N-doped carbon, additionally, the metal NPs supplied electrons to the carbon atoms. The electron-deficient metal site in the pyridinic N-rich carbon was beneficial for the activation of HMF and oxygen. The activation of oxygen produced reactive oxygen species (such as superoxide radical anions) to ensure high selectivity to DMFDCA through dehydrogenative oxidation of the hemiacetal intermediate and hydroxymethyl group of 5-hydroxymethyl-2-methyl-furoate. The existence of disordered and defective carbons increased the number of active sites. Subsequently, we performed a series of control experiments. Based on our current experimental results and previous studies, we propose a simple mechanism for the aerobic oxidation of HMF to DMFDCA. The catalyst was stable, its performance decreased slightly after two cycles, and it was tolerant to SCN⁻ ions and resistant against N or S poisoning. Furthermore, the use of this catalytic system can be expanded to various substituted aromatic alcohols, such as benzyl alcohols with different substituents, furfuryl alcohol, and heterocyclic alcohols. Simultaneously, the product type was further extended from methyl esters to ethyl esters with a high yield when the substrate reacted with ethanol. In conclusion, this catalytic system can be applied in the production of carboxylic esters for polymers.     

膦酚中性镍催化烯烃聚合及烯烃与极性单体共聚研究进展

烯烃与极性单体共聚制备功能化聚烯烃最为直接,但存在诸多挑战,是聚烯烃领域近20年的研究热点与难点。后过渡金属催化剂在功能化聚烯烃合成上具有优势,已经涌现出了二亚胺、水杨醛亚胺、膦磺酸镍钯经典催化体系;相比之下,膦酚镍催化体系早期关注较少。然而,近期对于膦酚镍催化体系的研究已经揭示,膦酚镍催化体系将是一个极具基础与应用前景的体系。本文总结近5年膦酚镍催化剂的结构特点,综述其在乙烯聚合、乙烯与极性单体共聚合、丙烯与极性单体共聚合方面的重要进展,并总结出膦酚镍催化剂的优势,对极性单体种类、催化剂结构设计、丙烯与极性单体立构规整共聚、聚合反应机理、功能化聚烯烃综合性能进行了展望。     

基于中空多孔金纳米/石墨烯复合纳米材料的葡萄糖氧化酶直接电化学及其生物传感研究

采用溶液相牺牲模板法制备中空多孔金纳米粒子（HPAuNPs）,并将该材料与还原氧化石墨烯（rGO）复合,用于葡萄糖氧化酶（GOx）在玻碳电极（GCE）表面的有效固定,构建GOx/HPAuNPs/rGO/GCE传感界面。利用扫描和透射电镜、X射线光电子能谱、X射线衍射谱、红外光谱及电化学等方法对材料的形貌与结构,GOx的固定化过程,以及传感器的直接电化学和电催化性能进行表征。结果表明,HPAuNPs和rGO的协同作用能有效促进GOx与电极之间的直接电子转移（DET）。基于GOx/HPAuNPs/rGO/GCE对葡萄糖的良好电催化性能,该方法有效实现了对葡萄糖的高灵敏度检测,其电流响应的线性范围为0.05～7.0 mmol/L,检出限（S/N=3）为16μmol/L。该传感器具有良好的选择性、重现性及稳定性,对实际样品血清中血糖的测定结果令人满意,回收率为98.0%～103%,相对标准偏差不大于5.0%。