SYNTHESIS AND CHARACTERIZATION OF LIQUID CRYSTALLINE MULTI-BLOCK COPOLYMERS,POLY[1,6-BIS(4-OXYBENZOYL-OXY)HEXANE TEREPHTHALATE]-b-BISPHENOL A POLYCARBONATE

A series of liquid crystalline multi-block copolymers poly [1,6-bis(4-oxybenzoyl-oxy)hexaneterephthalate]-b-bisphenol A polycarbonate (PHTH-6-b-PC) with different segment lengths were synthesizedin tetrachloroethane by solution polycondensation in which hydroxyl terminated PC and acyl chlorideterminated PHTH-6 were used. It is found that block copolymers with high molecular weight and well-defined structures were obtained. All the block copolymers exhibit a nematic liquid crystalline texture.     

聚丙烯表面接枝PNIPAAm膜Ⅱ.表面特性和温度响应性研究

通过吸水率和接触角测定研究了聚N 异丙基丙烯酰胺 (PNIPAAm)接枝膜的温度敏感特性 .尽管非交联型接枝膜和交联型接枝膜的吸水特性没有显著差别 ,但是交联组分的引入确实在一定程度上延缓了接枝膜的失水趋势 ,同时也有利于接枝膜亲水性的提高 .对接枝膜进行接触角研究发现 ,在某临界温度以下 ,接触角随时间的变化表征了探测水滴与膜表面之间的相互作用过程 .为了消除接触角测定过程中水份蒸发造成的影响 ,建立了接触角修正算法和修正经验关系式 ,并发展了一种适合于温度敏感性接枝膜LCST测定的变温实时接触角测定方法 .提出了接枝膜与水滴相互作用过程分为两个阶段的模型 ,并得到交联型PP接枝膜表面性能发生明显变化的临界接枝率为 0 6mg cm2 左右     

缩聚的溶剂体系对芳香－脂肪族共聚酰胺序列结构的影响

本文研究了以对苯二甲酰氯、对苯二胺和乙二胺三元共缩聚物为代表的芳－脂族共聚酰胺低温溶液缩聚中的溶剂、助溶剂（盐）和酸吸收剂等对共聚酰胺链序列结构参数－无规度（Ｂ）和数均序列长度（Ｌ）－的影响．     

聚对苯二甲酰对苯二胺纤维在热处理时的二次结晶

用X-射线衍射、TEM、FTIR、DSC、PPM等方法,研究了热处理前后PPTA纤维的一系列结构参数,发现该纤维聚集态结构参数随温度变化曲线在380℃左右出现拐点,晶粒尺寸长大,结晶度提高,晶区取向度增加同时晶格畸变增大。通过DSC谱图进一步确认了该纤维在热处理过程中的二次结晶,并表明它是热处理后PPTA纤维模量大幅度提高的主要原因。     

TEGDA红外激光光聚合动力学的实时FTIR研究

采用实时ＦＴＩＲ研究了二缩三乙二醇二丙烯酸酯的红外光聚合反应动力学。在红外激光照射下,引发剂１,３,３,１’,３’,３’－六甲基－１１－氯－１０,１２－亚丙基三碳菁－正丁基三苯基硼可以引发二缩三乙二醇二丙烯酸酯的光聚合反应。研究发现,随激光功率的提高,单体的聚合速度与双键转化率均有显著提高。在１７．０ｍＷ／ｃｍ＾２光强下二缩三乙二醇二丙烯酸酯在２０ｓ内双键转化率为１５％,聚合速度为８．４＊１０＾－３ｍｏｌ．Ｌ＾－１．ｓ＾－１,并且初期反应速度与激光功率为０．４７次方成正比,说明我聚合初期遵守双基终止的反应机理。由于分子链柔性的影响,同样条件下ＴＥＧＤＡ的转化率略高于一缩二乙二醇二丙烯酸酯。     

新型酯类液晶环氧预聚物的合成与表征

液晶高分子作为高分子学科的一个组成部分 ,已经取得令人瞩目的成就 ,在热塑性液晶聚合物方面已经进行卓有成效的工作 .随着高性能复合材料的发展 ,热固性液晶聚合物逐步引起人们的注意[1].液晶环氧树脂是液晶热固体研究中颇引人注目的一种 .环氧化合物根据所含液晶基元不同可以分为酯类、联苯类、α 甲基二乙烯类和亚甲胺类等[2 8],其中酯类环氧化合物多采用过氧酸部分氧化法制得[2 4],虽然其产物结构比较明确 ,但是合成步骤较多 ,难度较大 ,产率低 .考虑到工业上使用环氧化合物大多为齐聚物的混合物 ,而不是结构单一的低分子化合物 ,本文…