A programme is developed to calculate the polarizations of the radiation emitted after electron impact excitation. The fully relativistic distorted-wave method is used in cross-section calculations. The programme is applied to He- and Li-like ions. The calculated values of line polarization are compared with other theoretical results and experimental values. For He-like U, at lower incident energy, the present polarization agrees with the other theoretical ones within 1%, while at higher energy, the differences increase up to about 10%. For He-like Fe and Ti, the present results of polarization degree for most of the lines agree with the experimental data within the experimental error bars. For the Li-like Ti line q （ls2s2p^2p3/2 to ls^22s）, the present value of the polarization agree excellently with another theoretical one, and both the values are consistent with the measured data within the experimental error bar.     

简单烯烃不对称环氧化的手性金属配合物催化剂

介绍了多类简单烯烃不对称环氧化反应的手性过渡金属配合物催化剂系统的催化效果。论述了配体结构与配合物作为环氧化反应催化剂的活性，稳定性，催化效率的关系。从配合物的电子和立体因素，几何构型与过渡态的构象和非对映异构体的能量差别探讨对不对称诱导效果的影响。同时陈述机理的研究情况。     

Zn1-xMgxZrNb2O8微波介质陶瓷的结构与性能研究

采用传统的固相反应合成法制备了Zn1-xMgx ZrNb2O8(x=0-0.4)微波介质陶瓷.研究了Mg2+的取代量x对Zn1-xMgxZrNb2O8陶瓷的烧结特性、物相组成、显微结构以及微波介电性能的影响.结果表明:Zn1-xMgxZrNb2O8陶瓷的烧结温度随着Mg2+取代量x的增加,略有提升;当x=0-0.3时,体系形成了单相的(Zn,Mg) ZrNb2O8固溶体,而当x=0.4时,体系除了形成(Zn,Mg) ZrNb2O8固溶体外,还有少量未知杂相生成;随着Mg2+的取代量的增加,Zn1-xMgxZrNb2O8陶瓷的微波介电性能呈现不同的变化规律.当x=0.2时,组分为Zn0.8Mg0.2ZrNb2O8的陶瓷在1230℃烧结4h,可获得较佳的微波介电性能:εr=27.55,Q ×f=58731 GHz,τf=-66.7×10-6/℃.     

流延法制备铌酸钾钠基无铅压电陶瓷的性能研究

通过流延成型技术,以片状K0.5Na0.5NbO3(简称为KNN)粉体为模板,结合掺杂改性后的基料粉体(K0.45Na0.55)0.98Li0.02(Nb0.77Ta0.18Sb0.05)O3-0.005BaZrO3(简称为KNNLST-BZ)流延制备出KNN基无铅压电陶瓷,研究了不同的工艺参数(烧结温度、烧结次数)对于KNNLST-BZ织构化陶瓷的电学性能、显微结构的影响.结果表明:模板含量为20wt;的KNNLST-BZ织构化陶瓷在1145℃下保温2h呈现出优异的性能:压电常数d33=204 pC/N,横向机电耦合系数k31=23;,剩余极化强度Pr=26 μC/cm2,矫顽场Ee=1.2 kV/mm.同时该织构化陶瓷在1145℃下烧结2次能得到更优的电学性能:d33 =248 pC/N,k31=32.54;,Pr=38 μC/cm2,Ec=1.2 kV/mm,介电损耗tanδ=6.38;,机械品质因数Qm=16.76,介电常数εT33/ε0=913.7,横向伸缩振动频率常数N1=2244.     

B掺杂量对TiO2纳米粉体的结构与光催化性能影响研究

采用溶胶凝胶法制备了不同量B掺杂TiO2纳米粉体,采用X射线衍射(XRD)、透射电子显微镜(TEM)、X射线光电子能谱(XPS)、傅里叶变换红外吸收光谱(FT-IR)及紫外-可见漫反射光谱(UV-Vis)等技术对催化剂进行了表征.结果表明:B部分掺入到TiO2晶格间隙中形成B-O-Ti键,部分以B2O3的形式存在,随着B掺杂量的增加,进入晶格的B比例减少;B掺杂有效抑制了TiO2由锐钛矿相向金红石相的转变,掺杂样品经650℃煅烧后仍为锐钛矿结构,随B掺杂量的增加,其晶粒变小;B掺杂使得TiO2表面羟基量显著增加,且掺杂量越大表面羟基量越多;各掺杂样品的吸收边带没有明显红移,光吸收强度较未掺杂TiO2稍弱,且随着B掺杂量的增加,光吸收能力呈递减趋势.可见光催化降解亚甲基蓝结果表明,B掺杂大大提高了TiO2的光催化活性,这与掺B后晶粒变小,表面羟基量显著增加有关;当B掺杂质量百分数为1.0;时,B/TiO2可见光催化活性最高,达93.40;.     

CeO2添加对Ta2O5低膨胀陶瓷结构与性能的影响

采用干压成型和高温固相反应烧结制备了CeO2改性Ta2O5低膨胀陶瓷材料.研究了CeO2加入量对制备的Ta2O5陶瓷样品的物相组成、微观结构、热膨胀性能、抗折强度和抗热震性能等的影响.结果表明,经1450℃保温2h烧成,纯Ta2O5陶瓷由β-Ta2O5组成,存在明显的开裂现象,表现出负的热膨胀系数(-1.02×10-6℃-1)和低的抗折强度(1.69 MPa).添加CeO2后,除β-Ta2O5主晶相外,还生成了六方相针状CeTa7O19晶体.适量CeO2的加入可有效抑制Ta2O5陶瓷的高温可逆相转变和消除开裂现象,形成致密的微观结构,样品呈现低的正热膨胀系数,抗折强度和抗热震性能显著提高.     

RuO2/TiO2纳米管薄膜的制备及其光电催化性能研究

采用阳极氧化法结合浸渍法在钛金属片基底上制备了TiO2负载RuO2纳米管阵列,利用场发射扫描电子显微镜(FE-SEM)、X射线衍射仪(XRD)、能谱仪(EDS)和紫外可见分光光度计对纳米管的形貌、结构和光学性能进行了表征,并研究了RuO2/TiO2纳米管阵列在紫外光和可见光下对亚甲基蓝溶液的光电催化性能.结采表明:RuO2/TiO2纳米管仍保持了纯TiO2纳米管的结构特征,部分Ru进入TiO2晶格代替了Ti的位置形成了固溶体,部分Ru以RuO2纳米粒子形式存在;RuO2/TiO2纳米管的光吸收波长发生了红移,且在整个可见光区均比纯TiO2纳米管光吸收能力强,RuO2/TiO2纳米管光电催化降解亚甲基蓝的4h降解率由纯TiO2纳米管的27;提高到79;;采用该法制备的TiO2纳米管阵列膜回收简单,反复使用20次后光电催化降解能力基本保持不变.     

定位锌结晶釉的析晶动力学分析

本文以ZnO作为定位结晶剂在1100℃下制备了ZnSiO3结晶釉,测试了其在不同析晶保温时间下釉面晶花大小,并根据结晶动力学理论,对结晶釉中ZnSiO3晶花的生长规律和结晶机理进行了分析探讨.结果表明:当析晶保温时间超过30 min,晶花的形成速率随时间增加而显著提高,并在45 min到60 min范围内达到最大值;当析晶保温时间超过90 min,晶花形成速率随时间增加而快速下降,并在析晶保温时间超过150 min后,晶花基本上不再生长,形成速率达到稳定值.采用ZnO作定位晶种的釉面结晶稳定性好,釉面晶花大小与析晶保温时间符合S型生长曲线关系,可用Logistic函数拟合,本研究为实现锌结晶釉的可控生长提供了参考.     

(1-4x)NBT-3xKBT-xBT系压电陶瓷电性能研究

采用传统固相法制备了(1-4x)NBT-3xKBT-xBT(x=0.020～0.035)体系压电陶瓷.采用XRD分析发现该体系陶瓷都能形成单一的钙钛矿型固溶体,并在0.025≤x≤0.032范围内具有三方和四方共存结构,为该体系的准同型相界.当x=0.028时,d33=162 pC/N,Qm=203.29,kp=0.234.电滞回线分析表明,(1-4x)NBT-3xKBT-xBT体系陶瓷随着KBT和BT含量的增加具有从铁电体向反铁电体转变的趋势.     

四方相区NBT-KBT无铅铁电介电弛豫与铁电相变研究

本文研究了具有四方结构的(Na1-xKx)0.5Bi0.5TiO3体系中x＝0.22,0.26和0.30陶瓷材料不同温度下的电滞回线,结合变温XRD和介电温谱分析,发现该体系四方结构的组成为反铁电体,但紧靠准同型相界的四方结构由于场诱导下引起的反铁电-铁电相变,表现出铁电体特性,材料在升温过程中由于反铁电宏畴向微畴的转变导致了介电峰的产生,且在介电温谱上表现出强烈的介电常数-频率依赖性,为弛豫铁电体特征.