Suppression of Photoinduced BBO Defects Generation on TIO2（110） by Water

We have investigated creation of variable concentrations of defects on TIO2（110）-（1×1） surface by 266 nm laser using temperature programmed desorption technique. Oxygen-vacancy defects can be easily induced by ultraviolet light, the defects concentration has a linear dependence on power density higher than 50 mW/cm2 for 90 s irradiation. No observation of O2 molecule and Ti atom desorption suggests that UV induced defects creation on TiO2（110）-（1×1） is an effective and gentle method. With pre-dosage of thin films of water, the rate of defects creation on TiO2（110）-（1×1） is slower at least by two orders of magnitude than bare TiO2（110）-（1×1） surface. Further investigations show that water can be more easily desorbed by UV light, and thus desorption of bridging oxygen is depressed.     

Ni-Ti-O混合氧化物的制备、表征及其富氧选择性催化还原NO

采用均匀共沉淀法制备了不同Ni/Ti摩尔比的Ni-Ti-O混合氧化物,考察了它们在富氧条件下丙烯选择性催化还原NO反应中的催化性能,并运用X射线衍射,N₂吸附-脱附、吡啶吸附、程序升温脱附和原位红外光谱对催化剂进行了表征.结果表明,Ni/Ti摩尔比为1的催化剂表现出最佳催化活性,430℃时NO_x转化率达68%.该催化剂具有锐钛矿结构,比表面积较高(149m²/g),有利于提高催化活性;其表面Lewis酸性位有利于硝酸盐物种的吸附,而硝酸盐物种是该反应的重要中间体.     

PP/PB-1釜内合金的升温淋洗分级及级份表征

基于反应器颗粒技术制备的聚丙烯(PP)/聚丁烯-1(PB-1)釜内合金,其结构与组成,特别是嵌段共聚物级份的组成、分布、链序列结构等受两段聚合条件的影响较大。本文采用溶剂抽提法和升温淋洗分级法,对中试合成的两种PP/PB-1釜内合金进行分级,采用示差扫描量热仪(DSC)、高温核磁碳谱(~(13)C-NMR)、高温凝胶渗透色谱仪(GPC)对各级份进行表征,明确了合金的结构、组成及丁烯-丙烯嵌段共聚物(PB-b-PP)级份链序列结构。研究两种釜内合金的组成与力学性能关系,对于聚合工艺的优化及先进聚烯烃材料的开发提供依据。     

用于气象观测的阵列式温度传感器流体动力学分析与实验研究

传统百叶箱和防辐射罩内部的温度传感器受到太阳辐射会导致其温度高于大气真实温度, 升温量可达0.8 K甚至更高. 为提高大气温度观测精度, 本文设计了一种阵列式温度传感器. 利用计算流体动力学方法分析计算该传感器在不同环境条件下的辐射升温量, 采用遗传算法对计算结果进行拟合, 获得辐射升温量修正方程. 为验证阵列式温度传感器的实际性能, 研制了强制通风温度测量平台. 将阵列式温度传感器、配有传统防辐射罩的温度传感器和强制通风温度测量平台置于相同环境下, 进行大气温度观测比对实验. 配有传统防辐射罩的温度传感器辐射升温量平均值为0.409 K; 与前者相比, 阵列式温度传感器的辐射升温量仅为0.027 K. 这种阵列式温度传感器可将辐射升温引起的误差降低约93%. 辐射升温量实验测量值与修正方程修正值之间的平均偏移量为0.0174 K, 均方根误差为0.0215 K, 该结果验证了计算流体动力学方法与遗传算法的准确性. 如果配合计算流体动力学方法与遗传算法, 温度测量精度有进一步提高的潜力.     

Coking-resistant Ni-ZrO2/A1203 catalyst for CO methanation

Highly coke-resisting ZrO2-decorated Ni/A1203 catalysts for CO methanation were prepared by a two-step process. The support was first loaded with NiO by impregnating method and then modified with ZrO2 by deposition-precipitation method （IM-DP）. Nitrogen adsorption- desorption, X-ray diffraction, scanning electron microscopy, transmission electron microscopy, thermogravimetdc analysis, H2 temperature- programmed reduction and desorption, NH3 temperature-programmed desorption, and zeta potential analysis were employed to characterize the samples. The results revealed that, compared with the catalysts with the same composition prepared by co-impregnation （CI） and sequential impregnation （SI） methods, the Ni/A1203 catalyst prepared by IM-DP showed much enhanced catalytic performance for syngas methanation under the condition of atmospheric pressure and a high weight hourly space velocity of 120000 mL.g-1 .h-1. In a 80 h life time test under the condition of 300-600 ~C and 3.0 MPa, this catalyst showed high stability and resistance to coking, and the amount of deposited carbon was only 0.4 wt%. On the contrary, the deposited carbon over the catalyst without ZrO2 reached 1.5 wt% after a 60 h life time test. The improved catalytic performance was attributed to the selective deposition of ZrO2 nanoparticles on the surface of NiO rather than A1203, which could he well controlled via changing the electrostatic interaction in the DP procedure. This unique structure could enhance the dissociation of CO2 and generate surface oxygen intermediates, thus preventing carbon deposition on the Ni particles in syngas methanation.     

纳米复合材料CdS/TiO2制备与不同模式光催化降解多种染料

采用化学水浴沉淀法再结合溶胶-凝胶和程序升温溶剂热两步法制备了一系列不同比例的CdS/TiO2。通过XRD、XPS、SEM、UV-Vis/DRS等手段对所合成纳米复合材料的组成、结构和形貌等进行了表征。结果表明,该系列CdS/TiO2为锐钛矿TiO2和六方相CdS的混合晶相,其在可见光有较强吸收,并且随着复合材料中TiO2比例的增加,BET值明显增大。另外,所合成CdS/TiO2呈圆球形,颗粒比较均匀。紫外光催化降解甲基橙的实验结果表明,摩尔比为1:4的CdS/TiO2的活性明显高于CdS、P25以及其它不     

制备方法对Ni2P/SiO2催化剂结构及萘加氢性能的影响

采用程序升温还原法和次磷酸盐歧化法制备了Ni_2P/SiO_2催化剂,结合现代仪器分析表征技术,研究了制备方法对Ni_2P/SiO_2催化剂结构和萘加氢性能的影响。结果表明,两种方法均可制备出仅含Ni_2P活性相的Ni_2P/SiO_2催化剂,在反应温度340℃、氢气压力4 MPa、空速为20.8 h~(-1)下,程序升温还原法制备的Ni_2P/SiO_2催化剂表现出更高的萘加氢活性,这主要是因为程序还原法制备的Ni_2P/SiO_2催化剂中有更多Ni_2P物种生成,提供了较多的活性位点(CO吸附量21.6μmol/g);且催化剂表面弱酸位点多,有利于芳烃吸附。当选用程序升温还原法制备Ni_2P/SiO_2催化剂时,在保证生成纯相Ni_2P的前提下,较低的Ni/P比更有利于合成高加氢活性的Ni_2P/SiO_2催化剂。     

甲烷在Mo/HZRP-1催化剂上无氧脱氢芳构化反应Ⅰ.Mo/HZRP-1催化剂的催化性能和积炭行为

用高 硅含磷五 员环 沸 石 分子 筛（ 商 品 代号 Ｈ Ｚ Ｒ Ｐ１） 作 为 载体 ，制 备 了 Ｍｏ／ Ｈ Ｚ Ｒ Ｐ１ 催化剂． 与 Ｍｏ／ Ｈ Ｚ Ｓ Ｍ５ 相比， Ｍｏ／ Ｈ Ｚ Ｒ Ｐ１ 对 甲烷无 氧脱氢芳 构化反 应也表现 出较好的 催化 性能 ． 实验过程 中，在反 应气中添 加 Ｎ２ 作 为内标 物，给出包 括甲烷 在 Ｍｏ／ Ｈ Ｚ Ｒ Ｐ１ 上 的结焦量 、转化率 及各产物选 择性在内 的总碳 物料平衡 计算结果 ． 考 察了不同 Ｍｏ 担 载量对催 化剂性 能和 积炭 行为 的影响； 重点考察 了不同 温度焙烧 后２０ ％ Ｍｏ／ Ｈ Ｚ Ｒ Ｐ１ 催化剂 的性能和 积炭行 为． 在 反应的初 始阶段 ，６ ％ Ｍｏ／ Ｈ Ｚ Ｒ Ｐ１ 表 现出 很 高 的 活 性： 反 应 进 行 ３０ ｍｉｎ 时， 甲 烷 转 化 率 为 １１ ％ ， 芳 烃 选 择 性 达８１ ％ ， 而催化 剂的结焦 选择性 仅为１２ ％ ． Ｂ Ｅ Ｔ， Ｎ Ｈ３ Ｔ Ｐ Ｄ 和 催 化反 应等 表 征结 果表 明： Ｍｏ 物种的数量 和状态， 分子筛的 酸强度和 酸量以 及分子筛 的孔道 结构是 决定 甲烷 无氧 脱氢 芳构 化反 应性能和积 炭行为 的关键因 素．     

多阶段线性程序升温毛细管气相色谱最佳分离温度的选择

本文提出了气相色谱程序升温分离已知样品的优化指标。在此基础上考虑到色谱柱温和样品组分在色谱柱内的路径差别对保留时间和分离度的影响。提出了气相色谱最佳多阶梯线性程序升温温度曲线选择的基本原则——“移动重叠分辨图”法,并用毛细管气相色谱实验对此进行了验证,理论值与实测值能很好吻合。