Preparation of Nanoelectrode Ensembles by Assembly of Nano—Silver Colloid on Gold Surface

A novel method for preparing silver nanoelectrode ensembles(SNEEs) and gold nanoelectrode ensembles (GNEEs) has been developed. Silver colloid particles were first absorbed to the gold electrode surface to form a monolayer silver colloid. N-hexadecyl nercaptan was then assembled on the electrode to form a thoil monolayer on which hydrophilic ions cannot be transfered. The SNEEs was prepared by removing thiol from silver colloid surface through applying and AC voltage with increasing frequency at 0.20V(vs.SCE). Finally,GNEEs was obtained by immersing a SNEEs into 6 mol/L HNO3 to remove the silver colloid particles. By comparison with other methods such as template method ect., this method enjoys some advantages of lower resistance, same diameter,easy preparation,controllable size and density.     

载气气氛对Co/MgMoO4催化剂CVD法高效合成碳纳米材料的影响

High yield and quality mutli-walled carbon nanotube (MWNT) bundles and carbon nanofibers were synthesized by catalytic decomposition of methane over Co/MgMoO₄ catalyst at 1 000 ℃. TEM studies showed that the products were mainly carbon nanofibers without carrier gas and were all MWNT bundles with hydrogen or nitrogen as carrier gas. Thermal gravimetric analyses (TGA) on the raw product indicated that the purity of MWNT was higher than 95wt%. The growth mechanism of carbon nanofibers and MWNTs was also discussed.     

结合电生孔技术的抗体-纳米TiO2靶向光敏杀癌细胞

报道了用免疫、电生孔和纳米TiO₂光催化组合技术进行杀伤结肠癌LoVo细胞的研究. 先把结合LoVo细胞表面CEA抗原的单克隆抗CEA抗体吸附在纳米TiO₂微粒表面, 抗体-纳米TiO₂复合微粒就会自动吸附到LoVo细胞的表面, 然后用电脉冲法使LoVo癌细胞的细胞膜上产生小孔, 促使纳米TiO₂微粒进入癌细胞内部. 最后在紫外光照射下使TiO₂纳米粒子在癌细胞内部发生光催化氧化作用, 杀伤癌细胞. 结果表明, 这种组合技术具有很高的杀癌细胞能力. 在仅含3.12 μg/mL抗体-纳米TiO₂的细胞培养液内和强度为4 mW/cm²的紫外光照射下, 可在30 min内将所有LoVo癌细胞杀死. 这种技术对LoVo癌细胞的杀伤力远高于对不表达CEA抗原的人正常TE353.sk细胞的杀伤力, 显示了组合技术杀癌细胞的高选择性. 因此, 这种组合技术有望成为治疗癌症的新方法, 值得进一步探索.     

纳米碳酸锌的制备和热分解动力学参数的测定

Nanosized zinc carbonate was prepared in the droplet of nano-reactor based on microemusion. The influences of the concentration of the surfactant and reactant on the diameter of nanoparticles were studied and the kinetic pa-rameters of thermal decomposition reaction were determined. It can be shown from experimental results， the di-ameter of the droplet in the microemulsion which have dissolved reactant zinc nitrate and sal volatile is between 4.9nm and 7.7nm， 6.2nm and 12.4nm， respectively. Nanosized zinc carbonate prepared by the method of mi-croemusion has shown good dispersion， narrow distribution and light agglomeration. The particle size of nanosized zinc carbonate is between 5nm and 40nm， and its kinetic parameters of thermal decomposition reaction-activation energy E and reaction order n are 110kJ·mol^-1 and 0.9， respectively.     

纳米氧化铜的制备及常温脱硫效能研究

采用硝酸铜为原料、氢氧化钠溶液为沉淀剂、使用体积比为1∶1的乙醇-水溶液为分散剂的直接沉淀法制备，通过改变工艺条件得到了三种纳米氧化铜产品，平均粒径分别为25.63，10.74和7.57 nm。采用TG-DTA、FIR、XRD和TEM等对纳米氧化铜进行表征。对产品的常温脱硫活性进行了穿透试验，并与已开发的其他常温精脱硫产品进行了比较，结果表明纳米氧化铜应用于H₂S脱硫，可在常温条件下具有优异的脱硫活性，对H₂S的脱除精度可以达到0.05 mg·m^-3以下。经过优选，产品在3 000 h^-1空速下穿透硫容达到25.3%，高于同类型的其他脱硫剂产品。     

ZnO粉体的两种不同制备途径

本文用沉淀法和气相沉积法两种方法制备了ZnO粉体，对所得样品用粉末X射线衍射(XRD)、透射电镜(TEM)和红外吸收光谱(IR)进行了鉴定和表征，初步探讨了气相沉积法制备的ZnO微粒的生长机理，并对所用的两种制备方法作了简要的比较。     

纳米Sb2O3的制备与性能研究

由于Sb2O3是一种性能优良的无机阻燃剂,并与卤素阻燃剂有很好的协效作用[1],1998年,全球用于阻燃的Sb2O3达80kt以上,占阻燃剂总耗量的7%[2]。但由于其本身的极性特点,加入到纤维、塑料等高分子材料中,材料的力学性能受到很大损失[3],因此对传统的微米级的Sb2O3进行超细、表面处     

CaTiO3纳米粉体溶胶-凝胶法合成、表征及介电特性

采用无机盐溶胶-凝胶法制备了CaTiO₃纳米粉体，采用TG-DTA、XRD、TEM等技术进行了表征，并探讨了CaTiO₃纳米粉体烧结特性及介电效应。结果表明，干凝胶800 ℃低温煅烧可获得粒径分布较窄、平均粒径为60～70 nm的单相CaTiO₃纳米粉。纳米CaTiO₃粉具有较大的比表面积，使作为粉体烧结驱动力的表面能剧增，促使CaTiO₃在1 200 ℃实现致密烧结，比固相法制备的微米粉烧结降低100～200 ℃，且具有较宽的烧结温区。与微米级粉体烧结体介电特性相比，纳米粉具有更高的Q_f值。纳米CaTiO₃粉制备的陶瓷在1 250 ℃烧结2 h，获得优良的介电性能：ε_r=172，Q_f=4 239 GHz，τ_f=+7.68 × 10^-4 ℃^-1。     

聚合物-金属纳米复合材料的制备与应用

综述了聚合物-金属纳米复合材料的制备方法，包括原位形成法、沉积法、离子注入法、辐射化学法、光照化学法、直接分散法、球磨法；介绍了聚合物．金属纳米复合材料的应用领域，最后展望了这种材料的发展前景。     

纳米PbSnO3的制备及其燃烧催化性能的研究

Nanocomposite PbSnO₃was synthesized by coprecipitation method , and its phase evolution process was investigated. The particle size, crystal form, and phase of samples were determined with XRD, TEM and EDS. The catalytic actiyity of sample on the thermal decomposition of RDX was investigated by DSC. The results show that nanocomposite PbSnO₃with the diameter of 9 nm can be obtained by calcining at 600 ℃ for 2 h, which crystal is cubic (pyrochlore type). The catalytic actiyity of nanocomposite PbSnO₃on the thermal decomposition of RDX is much higher than that of normal PbSnO₃. The nanocomposite PbSnO₃can decrease the peak temperature of thermal decomposition of RDX from 240.1 ℃ to 236.5 ℃, and the decomposition enthalpy ΔH of RDX increases 722 J·g^-1 （about 70%）.