Effect of Organic Ligands Used in Sol-Gel Process on the Formation of Mullite

The preparation of mullite by the sol-gel method using organic polydentate ligands and the effect of the raw materials and organic polydentate ligands on the formation of mullite were investigated. Two series of samples were prepared using tetraethoxyorthosilicate (TEOS) and aluminum nitrate nonahydrate, or dibutoxyethylacetoacetatoaluminum (Al(OBu)₂(AcAcEt)) as the silica and alumina sources, respectively, and using ethylene glycol (EG), 1,3-propanediol (PD), 1,3-butanediol (BD), 2-methyl-2, 4-pentanediol (MPD), diethlene glycol monoethyl ether (DEME) and ethoxyethanol as the ligands. When the alumina source was aluminum nitrate nonahydrate, mullite was apt to appear in the order of EG>PD>MPD. When Al(OBu)₂(AcAcEt) was the alumina source, the tendency toward the appearance of mullite crystalline phase was EG>BD>DEME>MPD. Between the two alumina sources, aluminum nitrate nonahydrate gave mullite much easier than Al(OBu)₂(AcAcEt). These relationships were discussed from the viewpoints of the coordination ability of the ligands and the miscibility between the silica and alumina.     

Thermodynamic evaluation of a partial charge model assumptionfor the dissolved silica system

The Partial Charge Model was developed to predict the hydroxylation, polymerization, and precipitation of ions. The purpose of this study is to evaluate the Partial Charge Model for describing the polymerization of silica in aqueous solutions. The Partial Charge Model predicts the stability of ions and complexes based on the assumption that the stable species will have the same electronegativity as the mean electronegativity of the solution. The silica system was chosen for model validation because of the rare availability of self-consistent thermodynamic data on many dissolved but polymerized silicate anions, including both linear and cyclical species. The electronegativity of each species was calculated using the Partial Charge Model and the results were plotted against the stability constants for the ions. The silicate anions segregated into groups on the plot based on the number of charges per silicon atom in the polymer. Plots of the log of the stability constant versus the change in electronegativity produced a linear relationship for the silica polymers containing one negative charge per silicon atom, which resulted in an r ² of 0.9978. Thus, the Partial Charge Model successfully describes the thermodynamics of silica polymerization in aqueous solution for species that are sufficiently alike, but was not accurate for all silica species.     

Hydrogen Gas Sensing of High Electrical Conducting-P2O5-SiO2 Glasses Prepared by Sol-Gel Process

High proton-conducting P₂O₅-SiO₂ glass was applied to the electrolyte of the hydrogen concentration cell for hydrogen gas sensing. 5P₂O₅·95SiO₂ glass was prepared using the sol-gel method and its electrical conductivity and electromotive force were measured at 50°C as a function of both the ambient humidity and hydrogen gas concentration. The electrical conductivities increased with increasing humidity and reached 10^–2 S/cm at 90% relative humidity. The electromotive force of the hydrogen concentration cell, where the glass was used as a membrane, showed good Nernstian response to hydrogen pressure in the high relative humidity region.     

钒掺杂TiO2/AC负载催化剂的制备及光催化活性

以TiO2为主要成分的光催化剂的研究已日益受到人们的广泛关注[1-6]。但TiO2粉末的回收和流失问题难以解决,固定化TiO2负载催化剂的研制是解决这一问题的有效手段[2-6]。从实际应用的观点看,TiO2的光催化剂活性还有待进一步提高。研究发现,大多数过渡金属离子和少数非金属离子的     

Preparation and characterization of silicate gel glasses containing Cr2O3

The effect of thermal treatment on the structural incorporation of Cr₂O₃ in xCr₂O₃·(100 – x)SiO₂ and 5R _n O·xCr₂O₃·(95 – x)SiO₂ (where x=0.01–1 mol.% and R=Li, Na and Ca) gel glasses was studied by optical absorption spectrophotometry, DTA-TG, XRD and electron microscopy.Samples heat treated at 60°C have green color due to the presence of Cr³⁺ in octahedral coordination. The optical transmission, and color (yellow, orange or ambar), of the samples heat treated between 200 and 700°C prove that Cr³⁺ (octahedrally coordinated) and Cr⁶⁺ (tetrahedrally coordinated) are both present. Segregation of Cr₂O₃ take place at temperatures above 800°C.In reducing conditions the gel glasses were green due to the presence of a high content of Cr³⁺ ions. Samples containing Li or Na show crystalline phases at temperatures below 850°C.     

Sol-gel ZrO2 coatings for chemical protection of stainless steel

ZrO₂ coatings deposited on 316 L stainless steel sheets were synthesized by sol-gel method using Zr(OC₃H₇)₄ as precursor and isopropanol, glacial acetic acid, and water as solvents for application with ultrasounds. Different solutions for dip-coating were prepared with compositions varying between 0.025 and 0.9 mol/dm³ of ZrO₂. X-ray diffraction shows that the films densified at 800°C are crystalline with a tetragonal structure. The thickness of the coatings varied from 0.35–0.75 m. The influence of the ZrO₂ coatings on the corrosion behavior of stainless steel substrates in aqueous NaCl was studied through potentiodynamic polarization curves at 1 mV/s. The values of the electrochemical parameters allow for an explanation of the role of the films in the increased resistance of steel against corrosion in moderately aggressive environments.     

Characterization of Sol-gel bioencapsulates for ester hydrolysis and synthesis

Candida rugosa lipase was entrapped in silica sol-gel particles prepared by hydrolysis of methyltrimethoxysilane and assayed by p-nitrophenyl palmitate hydrolysis, as a function of pH and temperature, giving pH optima of 7.8 (free enzyme) and 5.0–8.0 (immobilized enzyme). The optimum temperature for the immobilized enzyme (50–55°C) was 19°C higher than for the free enzyme. Thermal, operational, and storage stability were determined with n-butanol and bytyric acid, giving at 45°C a half-life 2.7 times greater for the immobilized enzyme; storage time was 21 d at room temperature. For ester synthesis, the optimum temperature was 47°C, and high esterification conversions were obtained under repeated batch cycles (half-life of 138 h).     

Condensation reaction of 3-(methacryloxypropyl)-trimethoxysilane and diisobutylsilanediol in non-hydrolytic sol-gel process

The condensation reaction of 3-methacryloxypropyl-trimethoxysilane (MPTS) and diisobutylsilanediol (DIBSD) in a non-hydrolytic sol-gel process was investigated in terms of the reaction time and the catalyst amount for fabrication of inorganic-organic hybrid materials. The degree of condensation, which was characterized by ²⁹Si NMR, ¹H NMR and Abbe refractometry, increases with increased the reaction time and greater catalyst amount. However, a the large catalyst amount breaks the methacryl group during the condensation reaction. Thus, the reaction time and the catalyst amount were optimized to synthesize the condensed methacryl oligosiloxanes.     

Effect of Glass Substrates on the Formation of Gold-Silver Colloids in Nanocomposite Thin Films

A sol-gel route to synthesize nanocomposite thin films containing phase separated metal colloids of gold (Au) and silver (Ag) was developed. Ag—Au colloids were prepared in silica films using dip coating technique. The annealing of the samples in air results in the formation of phase separated Ag and Au colloids in SiO₂ thin films, showing the surface plasmon peaks at 410 nm and 528 nm. For the synthesis of phase separated Ag and Au colloids on float glass substrates, formation of the silver colloids was found strongly dependent on the surface of the float glass. On the tin rich surface formation of both gold and silver colloids took place, whereas, on the tin poor surface the formation of only gold colloids was observed. The surface dependence of the formation of silver colloids was attributed to the presence of tin as Sn²⁺ state on the glass surface, which oxidizes into Sn⁴⁺ during heat treatment, reducing Ag⁺ into silver colloids.     

V2O5/TiO2 Catalytic Xerogels Raman and EPR Studies

Raman spectroscopy and Electron Paramagnetic Resonance (EPR) studies were performed on a series of V₂O₅/TiO₂ catalysts prepared by a modified sol-gel method in order to identify the vanadium species. Two species of surface vanadium were identified by Raman measurements, monomeric vanadyls and polymeric vanadates. Monomeric vanadyls are characterized by a narrow Raman band at 1030 cm^–1 and polymeric vanadates by two broad bands in the region from 900 to 960 cm^–1 and 770 to 850 cm^–1. The Raman spectra do not exhibit characteristic peaks of crystalline V₂O₅. These results are in agreement with those of X-ray Diffractometry (XRD) and Fourier Transform Infrared (FT-IR) previously reported (C.B. Rodella et al., J. Sol-Gel Sci. Techn., submitted). At least three families of V⁴⁺ ions were identified by EPR investigations. The analysis of the EPR spectra suggests that isolated V⁴⁺ ions are located in sites with octahedral symmetry substituting for Ti⁴⁺ ions in the rutile structure. Magnetically interacting V⁴⁺ ions are also present as pairs or clusters giving rise to a broad and structureless EPR line. At higher concentration of V₂O₅, a partial oxidation of V⁴⁺ to V⁵⁺ is apparent from the EPR results.