纳米CaMgSi2O6粉体的低温合成与微波介电性能

以硝酸锂、偏钒酸铵、硝酸钙、硝酸镁、正硅酸乙酯为原料，采用溶胶-凝胶法低温合成纳米CaMgSi₂O₆微波介质陶瓷粉体，研究了不同粒径粉体的烧结行为与微波介电性能。结果表明，通过在钙镁硅溶胶中引入锂钒烧结助剂可大大降低陶瓷粉体的晶相合成温度，干凝胶在750 ℃煅烧后可获得主晶相为CaMgSi₂O₆、分散性良好、粒径为78～98 nm的陶瓷粉体，可满足微型片式元器件用超薄陶瓷介质层的制备要求;该粉体在890 ℃烧结后获得致密结构的陶瓷，具有良好的微波介电性能:介电常数为7.68，品质因数为24 542 GHz，频率温度系数为-57.25×10^-6 ℃^-1。     

Er~(3+)铋铅锶玻璃吸收光谱和上转换光谱

制备了新型掺Er3+铋铅锶玻璃,研究了玻璃的吸收光谱和上转换光谱性质,应用Judd-Ofelt理论计算了铋铅锶玻璃的3个强度参量Ωt(t=2,4,6),分别为Ω2=3·27×10-20cm2,Ω4=1.15×10-20cm2,Ω6=0.38×10-20cm2。计算了Er3+离子的振子强度、自发辐射跃迁几率、荧光分支比和辐射寿命等光谱参数。研究了上转换发光强度随泵浦激光功率的变化,上转换荧光525,546和657nm曲线的斜率分别为1·86,1·88和1·85,表明红、绿光发射均为双光子吸收过程。     

水热法制备的荧光碳量子点

以葡萄糖为碳源,通过水热法制备了碳量子点,并通过X射线衍射（XRD）、透射电镜（TEM）、紫外-可见吸收光谱、荧光光谱和傅里叶红外光谱（FTIR）等方法对样品的结构、形貌和光学性能进行表征。结果显示：以葡萄糖为碳源制备的碳量子点近似球形,大小均匀,分散性良好,无团聚现象。其发射波长依赖于激发波长,在紫外灯下发出明亮的绿光。     

Ce3+/Eu2+共掺Ca3Si2O4N2荧光粉的光学特性

采用高温固相法制备了一种新型的白光LED用Ca3Si2O4N2∶Eu2+,Ce3+,K+荧光粉。利用X射线衍射仪对样品的物相结构进行了分析,结果表明:Ce3+和K+离子的掺杂没有改变Ca3Si2O4N2∶Eu2+荧光粉的主晶相。利用荧光光谱仪对样品的发光性能进行了测试,发现样品在355 nm激发下得到的发射光谱为峰值位于505 nm的单峰,是Eu2+离子5d-4f电子跃迁引起的。Ca3Si2O4N2∶Eu2+荧光粉通过Ce3+和K+离子的掺杂,发光明显增强。当Ce3+的摩尔分数为1%时,荧光粉的发光强度达到最大值,是单掺Eu2+离子荧光粉发光强度的168%。通过光谱重叠的方法计算Ce3+→Eu2+能量传递临界的距离为2.535 nm。     

Eu2+/Dy3+共掺SrSiO3透明微晶玻璃的光学性质

在还原气氛中采用高温熔融法制备了Eu2+-Dy3+共掺硅酸盐玻璃,热处理后得到了Eu2+-Dy3+共掺透明SrSiO3微晶玻璃。测试了样品的激发光谱和发射光谱,研究了不同Eu2+-Dy3+物质的量比下微晶玻璃发光的变化并计算了对应的色坐标。研究发现,样品发射光谱范围在400～600nm,其中400～550nm(绿光)的宽发射谱带来自Eu2+的5d→4f跃迁,而位于483nm(蓝光)和575nm(黄光)的尖峰则来自Dy3+的4F9/2→6 H15/2和4F9/2→6 H13/2跃迁;在紫外(UV)光(365nm)激发下通过调控Eu2+-Dy3+物质的量比可得到发白光的微晶玻璃,当Eu2+-Dy3+物质的量比为1∶8时,Eu2+-Dy3+共掺SrSiO3透明微晶玻璃所发白光最佳,对应的色坐标(0.268,0.356)位于CIE标准色坐标图的白光区域且最接近理想白光。结果表明,Eu2+-Dy3+共掺SrSiO3透明微晶玻璃可作为一种潜在的白光发光二极管用基质材料。     

光纤拉曼放大器的研制及其在城域网中的应用

优化设计了色散补偿拉曼放大器,并将其应用于城域网络中,测试了系统的各项性能,包括光缆的实际衰减,发送端和接收端各点的光功率,拉曼放大器的实际增益,系统极限接受灵敏度,短期和长期误码率,应用前后线路的稳定性,以及不同拉曼放大器抽运功率下可达到的无中继传输距离.在使系统具有高稳定性的前提下,最大无中继传输距离可达到215 km,取得了较好的试验效果,并由此得出光纤拉曼放大器在长跨距的光纤传输系统中有很好的应用前景.     

Visible Upconversion Emission in Er3＋—Doped GeO2—PbO—PbF2 Glass

The upconversion fluorescence emission of Er3 -doped 60GeO2-2OPbO-2OPbF2 glass was experimentally investigated under the pump of 976-nm laser diode. The results reveal the existence of intense emission bands centred around 524, 545, and 657nm at room temperature. The green emission at 524 and 545nm is due to the 4S3/2 2 Hll/2→ 4I15/2 transition and the red emission of 657nm originates from the 4F9/2-→4I15/2 transition of Er3 . The quadratic dependence of the green and red emissions on excitation power indicates that a two-photonabsorption process occurs under the 976-nm excitation. The excited- state absorption from 4I ll/2 and the cross relaxation between two Er3 ions in the 4I ll/2 state contribute to the green emission. The red emission at 657nm is attributed to the excited-state absorption and cross relaxation processes in the 4I13/2 level as well as the 4S3/2 level nonradiative transition of Er3 .     

Effect of B2O3 on Judd—Ofelt parameters of Er^3＋—doped tellurite glasses

We have prepared Er^3 -doped borotellurite glasses using conventional melting and quenching method.The absorption spectrum analysis is performed on the basis of Judd-Ofelt theory.The effects of B2O3 on the spectroscopic parameters such as intersity parameters,line strengths of electric-dipole transitions,and sopontaneous emission probability are discussed.     

Frequency Upconversion Emission of Er^3＋-Doped Strontium-Lead-Bismuth Glasses

Er^3 -doped strontium-lead-bismuth glasses for developing potential upconversion lasers have been fabricated and characterized. Under 975 nm excitation, intense green and red emissions centred at 525, 546, and 657nm,corresponding to the transitions ^2H11/2 → ^4I15/2, ^4S3/2 → ^4I15/2, and ^4F9/2 → ^4I15/2, respectively, were observed at room temperature. The upconversion mechanisms are discussed based on the energy matching and quadratic dependence on excitation power, and the dominant mechanisms are excited state absorption and energy transfer upconversion for 525 and 546nm emissions, and energy transfer upconversion for 657nm emission.     

荧光捕获效应对Yb3+磷酸盐玻璃光谱性质的影响

测试了不同掺杂浓度和不同厚度下Yb³⁺磷酸盐玻璃的吸收光谱、荧光光谱和荧 光寿命，计算了积分吸收截面、吸收截面、受激发射截面、自发辐射寿命以及荧光有效线宽等光谱参数，讨论了荧光俘获效应对Yb³⁺磷酸盐玻璃光谱性质的影响.结果表明荧光俘 获效应随样品厚度和掺杂浓度的增加而增大.由于荧光俘获效应的存在使得测量的Yb^{3+磷酸盐玻璃荧光寿命明显长于计算的荧光寿命，在0.2mol%Yb₂O₃低掺 杂浓度下 关键词： 荧光俘获 掺镱磷酸盐玻璃 荧光光谱}