A Systematic Evaluation of Polyurethane as a Conformal Coating for the Inhibition of Corrosion on Electronic Components

The corrosion of printed circuit boards can be effectively prevented with a polyurethane conformal coating. In this study, the protective performance of PU coating was investigated systematically through electrochemical measurements and simulated exposure/immersion tests. Some fungi tests were also included. All experimental results show that a polyurethane coating effectively inhibits corrosion on printed circuit boards. The optimal thickness of the coating film should be about 60 μm. Long-term exposure tests showed that this coating material could preserve the reliability of the investigated printed circuit boards for more than 400 days in a 90% relative humidity environment at 25°C.     

稀土元素在LD30铝合金真空钎焊中的作用

研究了添加La和Ce的Al-Si基钎料真空钎焊LD30铝合金接头的力学性能，微观组织形貌和EDS，并与未添加稀土元素的Al-Si基钎料真空钎焊接头进行对比。结果表明，添加稀土元素的LD30铝合金真空钎焊接头抗拉强度为288MPa，达母材抗拉强度的97．6％，明显高于未添加稀土的LD30合金真空钎焊接头。其机制在于La,Ce能够明显提高Al-Si基钎料与LD30铝合金的润湿性能，改善LD30铝合金真空钎焊接头焊缝及其基体中杂质元素的分布，促进钎料和母材中各元素的均匀扩散，从而提高真空钎焊接头的力学性能。     

镀液中Ce^3＋离子对锡镀层结构缺陷和可焊性的影响

应用荧光分析法、X光电子能谱法(XPS)及正电子湮没寿命谱法(PALS)等研究了从含硫酸铈添加剂的酸性光亮锡镀液获得的锡镀层结构缺陷与可焊性的关系。结果表明,电镀时Ce与Sn不发生共沉积,Ce~(3+)的主要作用是阻化Sn~(2+)的水解和氧化使镀液稳定,因而使锡镀层纯度提高、结构致密、表层氧含量减少,有利于提高镀层的可焊性。当Ce~(3+)浓度控制在3.5g/L左右时,可使镀层结构缺陷较少,可焊性较佳,说明结构缺陷是影响锡镀层可焊性的直接原因。     

丙烯酸酯接枝炭黑无皂水性涂料的性能研究

旋转粘度计研究了丙烯酸酯接枝炭黑无皂水性涂料的流变性能，并考察了着色涂料的冻融及贮存稳定性。接枝炭黑争散于无皂水性涂料中形成的着色涂料具有良好的综合性能。     

Printed plastic electronics and paperlike displays

Plastic electronic materials and high‐resolution printing methods may be important technologies for new classes of consumer electronic devices that are lightweight, mechanically flexible and bendable, and that can cover large areas at low cost. This article summarizes some of our recent work in this area. It focuses on the materials and patterning techniques that we used to produce plastic active‐matrix backplane circuits for a type of paperlike display. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 3327–3334, 2002     

Keggin型杂多酸在镀锌钝化中的应用

比较了H_4SiMo_(12)O_(40)、H_3PW_(12)O_(40)、H_4SiW_(12)O_(40)、H_3PMo_(12)O_(40)及铬酸盐对镀锌层钝化效果。H_3PMo_(12)O_(40)钝化的最佳条件为:H_3PMo_(12)O_(40)5g/L,pH 1.1,钝化时间35秒,温度15℃,空留时间10秒,封闭温度100℃(水)。经扫描电镜、XPS、AES、IR和Raman光谱等测定,表明在锌表面形成了一种含有P、Mo、O及Zn的耐蚀性膜。其中钼以Mo(Ⅵ)、Mo(Ⅴ)和Mo(Ⅳ)存在,P/Mo比为1:3.0。推测锌表面形成了一种形如Zn_x(PMo_3)_rO_z/ZnO/Zn的复杂钝化膜。     

SBS单组分橡胶防水涂料

探讨了SBS单组分橡胶防水涂料的组成、制备方法及其对性能的影响因素,详细地介绍了该涂料在防水工程应用上的两大独特优势:(1)优异的抗基层形变能力。这一优势,使其具备了屋面防水专用材料和特效材料的条件,解决了以往防水材料一直不能解决的“零点开裂”问题。(2)创造出多种复合防水工法,既克服和解决了卷材与涂料的各自缺点,又发挥了各自的优点,使这种复合防水层成为最有效的防水层。     

Metal Oxide Thin Films Containing Au Nano-Particles Prepared with Gas Diffusion Method

Au particles dispersed thin metal oxide films were prepared from precursor films containing HAuCl₄ with H₂S gas diffusion method. HAuCl₄ was uniformly dissolved in the films as promoted by hydroxypropyl cellulose (HPC). The mechanism of the Au particle formation was studied. It was found that HAuCl₄ was converted directly to Au metal particles upon contacting with H₂S gas. Au particles generated by this method were characterized with small particle size, sharp size distribution and high volume fraction in the films. The surface plasma resonance absorption of Au particles shifted to longer wavelength when TiO₂ component was introduced in the matrix.     

羧基丙烯酸酯涂料合成及其防雾性能研究

采用种子乳液聚合法合成了一种互穿网络型羧基丙烯酸酯类聚物乳液，研究了加料方式对羧基分布的影响，结果表明丙烯酸加入到核单体中有利于羧基分布在乳胶粒表面。在体系中引入离子键交联结构提高了乳液涂料的硬度和耐水性能，离子键交联ＰＩＬＮ型涂料具有优良的防雾性能。     

水溶性ZnO量子点制备及其光学性质

利用3-巯丙基三乙氧基硅烷对ZnO进行表面修饰后沉积SiO2, 制备出水溶性SiO2包覆ZnO的量子点. 与直接采用正硅酸乙酯沉积包覆SiO2的ZnO量子点相比, 362 nm处的激子荧光发射峰的强度提高了将近4倍. 由于表面引入了巯基官能团, 量子点的水溶性明显提高, 稳定性增强, 即使在较高的盐浓度下也不会团聚. 通过改变条件, 制备出了发光波长在420 nm的蓝色荧光量子点.