含纳米晶颗粒的Yb3+/Er3+共掺透明碲酸盐玻璃陶瓷的光谱性质研究

在组成为15Li2O-15Nb2O5-70TeO2-0.1Er2O3-0.4Yb2O3（%, 摩尔分数）的碲酸盐玻璃基础上, 采用两步热处理法制备了透明的含纳米晶颗粒碲酸盐玻璃陶瓷. 通过X射线衍射（XRD）测试表明, 玻璃陶瓷中的晶体颗粒组成为Yb6Te5O19.2或Er6Te5O19.2, 晶粒尺寸约为55 nm. 根据Judd-Ofelt理论计算了Er^3＋离子在基质玻璃和玻璃陶瓷中的光谱参数Ωt（t＝2, 4, 6）以及Er^3＋：4I15/2→4I13/2跃迁自发辐射几率, 根据McCumber理论计算了Er^3＋：4I13/2→4I15/2跃迁的发射截面. 测试了基质玻璃和玻璃陶瓷的拉曼光谱, 对比研究了铒离子在基质玻璃和玻璃陶瓷中1.5 μm处荧光和上转换光谱特性.     

A Transparent Thin Film with Hexagonal Mesostructure Containing Rhodamine 6G

A transparent this film was prepared by depositing the sol-gel mixture for the synthesis of MCM-41 mesoporous molecular sieve doped with rhodamine 6G(R6G) dye on glass substrates. The film of silica-surfactant-R6G materials, which was identified to possess hexagonally ordered mesostructure,was composed of nanocrystallites about 35 nm in diameter and 1-10μm in thickness. Cleanness of the substrates, concentration of the sol-gel mixture and rate of evaporation of the solvent were the key factors affecting transparency and homogeneity of the film. Moreover,optical change and lack in dye aggregation were observed to the R6G-functionalized MCM-41 thin film in contrast with that in ethanol solution.     

透明导电氧化物的原理、问题与研究分析

现代光电子产品和能源技术都大量使用透明导电氧化物(TCO)薄膜.由于太阳能电池、平板显示器、发光二极管、短波长激光器、节能玻璃窗等应用领域日益增长的需求,TCO薄膜获得了越来越广泛的应用.文章总结了TCO薄膜的功能原理、应用需求和当前的研究方向,重点分析了p型TCO薄膜研究所要解决的关键问题(其中包括掺杂非对称性,性能退化与缺陷的生成,结构和变化的关系),指出了p型TCO薄膜制备的关键因素,研究的热点问题和蕴藏的研究机会.     

银纳米晶对铒镱共掺的TeO2-WO3-La2O3微晶玻璃发光性能的影响

通过熔融退火的方法以及热处理技术制备得到含有Er₂WO₆，La₂WO₆晶体的TeO₂-WO₃-La₂O₃-Er₂O₃-Yb₂O₃微晶玻璃，该玻璃具有优异的上转换发光性能。结果表明，在含银纳米晶的碲酸盐微晶玻璃中，银纳米晶和微晶的析出情况与银纳米晶的引入方式和热处理温度有关。经过390℃下15 min的热处理后，AgCl和AgNO₃共掺的碲酸盐微晶玻璃比单掺AgCl或AgNO₃的碲酸盐微晶玻璃具有更高的发光强度。银纳米晶与微晶的引入可协同提高碲酸盐玻璃的上转换发光性。     

Highly flexible,transparent, conductive and antibacterial films made of spin-coated silver nanowires and a protective ZnO layer

We prepared highly flexible, transparent, conductive and antibacterial film by spin coating a silver nanowire suspension on a poly (ethylene terephthalate) (PET) substrate. The ZnO layer covered the conductive silver nanowire (AgNW) network to protect the metal nanowires from oxidization and enhance both wire-to-wire adhesion and wire-to-substrate adhesion. It is found that the number of AgNW coatings correlates with both the sheet resistance (R_s) and the transmittance of the AgNW/ZnO composite films. An excellent 92% optical transmittance in the visible range and a surface sheet resistance of only 9 Ω sq⁻¹ has been achieved, respectively. Even after bending 1000 times (5 mm bending radius), we found no significant change in the sheet resistance or optical transmittance. The real-time sheet resistance measured as a function of bending radius also remains stable even at the smallest measured bending radius (1 mm). The AgNW/ZnO composite films also show antibacterial effects which could be useful for the fabrication of wearable electronic devices.     

Nd:YAG陶瓷与单晶4F3/2–4I13/2跃迁的弱谱线多波长激光性能对比

报道了基于半导体激光端面抽运Nd:YAG的⁴F_3/2–⁴I_13/2 跃迁的弱谱线多波长激光输出. 实验对比了透明陶瓷与单晶材料的激光输出特性, 表明透明陶瓷和单晶材料荧光谱强度的略微差异, 导致了多波长输出时相同两个波长之间的激光强度比在两种材料中的差异. 基于两种耦合输出镜片, 激光阈值都在2 W左右. 在13.5 W的抽运功率下, 基于Nd:YAG透明陶瓷获得了输出功率4.05 W、强度比1 :2的1338与1356 nm双波长激光和输出功率3.65 W、强度比13 : 1的1356与1414 nm 双波长激光, 斜率效率分别达33.9% 和31.9%.     

A posterior error estimates for the nonlinear grating problem with transparent boundary condition

The nonlinear grating problem is modeled by Maxwell's equations with transparent boundary conditions. The nonlocal boundary operators are truncated by taking sufficiently many terms in the corresponding expansions. A finite element method with the truncation operators is developed for solving the nonlinear grating problem. The two posterior error estimates are established. The a posterior error estimate consists of two parts: finite element discretization error and the truncation error of the nonlocal boundary operators. In particular, the truncation error caused by truncation operations is exponentially decayed when the parameter N is increased. Numerical experiment is included to illustrate the efficiency of the method. © 2014 Wiley Periodicals, Inc. Numer Methods Partial Differential Eq 31: 1101–1118, 2015     

Highly transparent cerium doped gadolinium gallium aluminum garnet ceramic prepared with precursors fabricated by ultrasonic enhanced chemical co-precipitation

Cerium doped gadolinium gallium aluminum garnet (GGAG:Ce) ceramic precursors have been synthesized with an ultrasonic chemical co-precipitation method (UCC) and for comparison with a traditional chemical co-precipitation method (TCC). The effect of ultra-sonication on the morphology of powders and the transmittance of GGAG:Ce ceramics are studied. The results indicate that the UCC method can effectively improve the homogenization and sinterability of GGAG:Ce powders, which contribute to obtain high transparent GGAG ceramic with the highest transmittance of 81%.     

直流反应磁控溅射制备掺铟ZnO透明导电薄膜的研究

本文介绍了掺铟ZnO透明导电膜的制备工艺.并应用半导体物理理论分析了薄膜的导电机理,用Drude理论建立了物理模型,分析与计算了薄膜从可见到红外光波段的光学性能,结果表明,理论计算与实测值两者符合得较好.