应用TGT法生长了直径为75mm的U：CaF2晶体，宏观上透明完整.应用公式K0=Cs/Cl计算了U在CaF2晶体中的分凝系数等于0.53.应用溶质分布一般公式Cs=K0C0(1-g)K0-1，计算U的浓度分布与测量值，数值符合说明晶体生长过程接近平衡状态.分析不同条件下生长的U: CaF2晶体的晶胞参数和吸收光谱，结果表明生长气氛决定U的价态及电荷补偿机理：无PbF2存在的条件下，U为+4价，晶体呈绿色；PbF2的加入起到氟化去氧作用，U倾向于以离子半径最接近于Ca2+的U3+存在，晶体呈红色.从晶体生长开始到结束的部位，U3+:CaF2晶体吸收光谱的峰位不变，峰强呈现与U浓度相同的增加趋势.U3+:CaF2晶体外层厚约5mm处呈黄色，含有U3+和U2+的混合价态离子，其原理是石墨坩埚的还原作用通过单质铅，使部分的U3+进一步还原成了U2+. 关键词： 铀 氟化钙晶体 分凝系数 晶胞参数     

Origin of the 420 nm Absorption Band and Effect of Doping Fluorine in PbWO4 Crystals

The electronic structures for three types of PbW04 (PWO) crystals, the perfect PWO, the PWO containing lead vacancy (PWO-Vpb) and fluorine doped PWO crystal (F^-：PWO), are systematically studied within the framework of density functional theory. The computational results show that the Pb 6s state situates below the valence band so that Pb^2 ions are unable to trap holes forming Pb^3 or Pb^4 to compensate for VPb^2-. The hole-trappers in PWO-Vpb are O^2- ions. Two of the longer-bond O^2- ions share a hole forming O2^3-, and four of the longer-bond oxygen ions trap two holes forming an associated color centre [O2^3--Vpb-O2^3-], which may be the origin of the 42Onto absorption band. It is also concluded that the doping of F^- would reduce the band gap and F^- ions substituting for O^2- can effectively restrict the formation of [O2^3--Vpb-O2^3-] and weaken the 42Onm absorption band and hence enhance the scintillation property of PWO.     

高效光学加工技术

为验证国产大口径KDP晶体金刚石车床（图1）的加工能力，进行了多次试验。加工的φ150mm小于0．52的铝镜面已达到与俄罗斯机床同等水平。但同时进行的一轮KDP晶体车削试验，结果并不满意，其单次透射波前畸变近4λ，原因可能是KDP晶体的装夹存在问题，导致加工效率不佳。而且加工中还产生周期性波纹，可能是由于机床压缩空气供给系统的周期性启动，造成周期性的压力波动。     

理想的胰岛素晶体

在自然界或实验室内 ,“理想化”总是一个难以实现的概念 .但最近美国休斯顿大学的P .Vekilov教授及其同事们发现 ,他们常常可以将胰岛素晶体生长成理想的晶体形式 .他们让胰岛素蛋白质在一个已有的胰岛素晶体的螺旋位错缺陷处进行生长 ,蛋白质将绕着这个缺陷发生晶化并形成一个理想晶状胰岛素 .这是因为螺旋位错常常使晶层间产生一个微小的角度偏差 .对于大多数的晶体来说 ,晶层间的相互作用能促进晶体生长时界面间的配置 ,并导致晶层阶跃发生束缚和形成一个有条纹的晶体 .除此之外 ,在溶液中输入被溶解物质也能引起晶层阶跃的约束 .胰岛…     

单光子态的产生与测量

报道了通过自发参量下转换产生单光子态的实验研究,使用中心波长425 nm的飞秒脉冲泵浦Ⅰ类非共线相位匹配的BBO晶体,在实验上得到单光子计数率为2.978×10-4,并分析了实验中的相关问题.     

γ-辐照对纯Y_2SiO_5和Eu~(3+)∶Y_2SiO_5晶体光谱性能的影响

研究了γ-辐照前后纯Y2SiO5和Eu3+掺杂的Y2SiO5晶体吸收光谱的变化,辐照后,未退火和氢气退火的纯Y2SiO5晶体在260~270 nm和320 nm波段产生了附加吸收峰,分别是由F心和O-心的吸收引起的;经过空气退火的纯YSO晶体中,由于消除了氧空位,因此辐照后没有出现色心吸收峰。在Eu3+∶Y2SiO5晶体中,不但有相同的F心和O-心吸收峰,而且还有Eu2+离子在300 nm和390 nm的吸收峰。随着辐照剂量的增加,色心附加吸收峰增强。空气退火能减少Eu3+∶Y2SiO5晶体中的色心,而氢气退火能增加色心。     

激光晶体YAG中Er3+的辐射跃迁

本文讨论和分析了激光晶体YAG中Er3+离子的激光上能级的4S3/2、4I11/2和4I13/2辐射跃迁的有关因素。     

Fabrication of Compound Lattice by Holographic Lithography

Some compound lattices in photonic crystals with large complete photonic band gaps, such as the diamond structure and the two-dimensional hexagonal compound structure, is desired for fabrication. A novel method for fabrication of compound lattices by holographic lithography is reported. The key point is phase modulation by photoelectrical control and multiple-exposure techniques. This technique introduces many advances: for instance,using the same coherent beams and without changing the position of the sample during multiple-exposure.     

Pyroelectricity and Spontaneous Polarization in [111] Oriented 0.955 Pb（Zn1/3Nb2/3）O3-0.045PbTiO3 Single Crystals

We report that the measurements of the pyroelectric current of the pre-poled [111]-oriented 0.955 Pb（Zn1/3Nb2/3） O3-0.045 PbTiO3 （PZN-4.5%PT） single crystals can shed some light on the phase transition and spontaneous polarization characters of this material in a similar way to measures of remanent polarization and dielectric properties. The pyroelectric current is measured and the corresponding spontaneous polarization is calculated as a function of temperature with various poling fields added during cooling the sample from 200℃ to room temperature. Critical electric field of 0.061 k V/cm is found to be essential to induce the intermediate ferroelectric orthorhombic phase between the ferroelectric rhombohedral and tetragonal phases. Below the critical field, the polarization increases almost linearly with the increase of poling field. At the critical field, the polarization at 30OC increases abruptly from 14μC/cm^2 for a poling field of O.06kV/cm to 29.5μC/cm^2 for a poling field of 0.061 kV/cm, and afterwards, increases slowly and saturates to 31 μC/cm^2 for poling fields beyond 0.55 kV/cm.     

高功率LDA紧密侧面抽运Nd:YLF两级双程离轴放大系统实验研究

 介绍了一台10mm口径两级双程离轴放大系统，实现了对5mm×5mm口径光束的激光放大，耦合系统采用高功率LDA紧密侧面直接抽运棒状Nd:YLF方式。分析并实验研究了在不同抽运电流、放大脉冲与放大器LDA抽运时刻的不同延时及不同注入能量条件下，放大系统及光束每次放大时放大特性的规律。实验得到：在放大系统5mm×5mm软光阑处注入1.58mJ能量时，放大系统可输出129.2mJ能量，能量提取效率达到19.5%，满足该系统的设计指标。