Crystal structure and magnetic properties of two new cobalt selenite halides: Co5(SeO3)4X2 (X=Cl, Br)

Two new isostructural cobalt selenite halides Co₅(SeO₃)₄Cl₂ and Co₅(SeO₃)₄Br₂ have been synthesized. They crystallize in the triclinic system space group P−1 with the following lattice parameters for Co₅(SeO₃)₄Cl₂: a=6.4935(8) Å, b=7.7288(8) Å, c=7.7443(10) Å, α=66.051(11)°, β=73.610(11)°, γ=81.268(9)°, and Z=1. The crystal structures were solved from single-crystal X-ray data, R1=3.73 and 4.03 for Co₅(SeO₃)₄Cl₂ and Co₅(SeO₃)₄Br₂, respectively. The new compounds are isostructural to Ni₅(SeO₃)₄Br₂.Magnetic susceptibility measurements on oriented single-crystalline samples show anisotropic response in a broad temperature range. The anisotropic susceptibility is quantitatively interpreted within the zero-field splitting schemes for Co²⁺ and Ni²⁺ ions. Sharp low-temperature susceptibility features, at T_N=18 and 20 K for Co₅(SeO₃)₄Cl₂ and Co₅(SeO₃)₄Br₂, respectively, are ascribed to antiferromagnetic ordering in a minority magnetic subsystem. In isostructural Ni₅(SeO₃)₄Br₂ magnetically ordered subsystem represents a majority fraction (T_N=46 K). Nevertheless, anisotropic susceptibility of Ni₅(SeO₃)₄Br₂ is dominated at low temperatures by a minority fraction, subject to single-ion anisotropy effects and increasing population of S_z=0 (singlet) ground state of octahedrally coordinated Ni²⁺.     

Thermomagnetic hysteresis and electrical transport in amorphous films

We report resistivity and magnetization measurements on an amorphous Ni₇₄Mn₂₄Pt₂ thin film in the temperature range of 3–300 K. Two significant features are apparent in both the magnetic susceptibility and electrical resistivity. A low-temperature (low-T) anomaly is observed at about 40 K, where a cusp appears in the resistivity, while a concomitant step-like increase in zero-field-cooled (ZFC) magnetization (M) appears with increasing temperature. The low-T anomaly is attributed to a crossover from a pure re-entrant spin-glass within individual domains to a mixed ferro-spin-glass regime at lower temperatures. By contrast, the high-temperature (high-T) anomaly, signaled by the appearance of hysteresis below 250 K, corresponds to the freezing of transverse spins in individual domains acting independently. Between the low-T and high-T anomalies a small but discernable magnetic hysteresis is observed for warming vs. cooling in the field-cooled (FC) case. This behavior clearly indicates the presence of domain structure in the sample, while the disappearance of this hysteresis at lower temperatures indicates the complete freezing of the spin orientation of these domains. According to these results, we have divided the magnetic state of this sample into three regions: at temperatures above 250 K, the sample behaves like a soft ferromagnet, exhibiting M vs. H loops with very small hysteresis (less than 5 Oe). As the temperature is lowered into the intermediate region (the range 40–250 K), spins become frozen randomly and progressively within the individual domains. These domains behave independently, rather than as a cooperative behavior of the sample. Weak irreversibility sets in, indicating the onset of transverse spin freezing within the domains. At temperatures below 40 K, the M vs. H loops exhibit larger hysteresis, for both the ZFC and FC cases, as in a pure spin-glass. We have also demonstrated giant noise in the resistivity at temperatures just below 250 K. Such noise can originate from fluctuations of the domains near the film surface because of competing effective bulk and surface anisotropy fields. The large observed amplitude may be explained by means of a large ferromagnetic anisotropy in the resistivity due to the large spin–orbit effect seen in NiMn systems. Finally, the low-T peak in the resistivity has been analyzed using Fisher and Langer's expression based on the Friedel Model proposed for critical transitions in transition metals (s–d systems). The fitted results are in satisfactory agreement with the predictions of this model.     

Structure and magnetism of bcc(1 1 0)-like Fe films grown on Cu(0 0 1) via ion beam triangulation and spin-polarized electron capture

The structure and magnetism of thin epitaxial Fe layers grown on Cu(0 0 1) is investigated by grazing scattering of fast H and He atoms. Information on the atomic structure of the film and substrate surfaces is obtained by making use of ion beam triangulation with protons. The magnetic behavior is studied via the polarization of light emitted after capture of spin-polarized electrons into excited atomic terms during scattering of He atoms. For the formation of bcc(1 1 0)-like Fe films at higher coverages, we detect differences in structural and magnetic properties for room and low temperature growth. We suggest that the crystalline structure depends on the film morphology and that Cu impurities affect the magnetic properties.     

Magnetic properties of mechanically alloyed Co–Ti powder

An amorphous phase containing traces of non-transformed Co and Ti powders was obtained by mechanical alloying nominal compositions of Co₆₇Ti₃₃ and Co₅₀Ti₅₀ in a high-energy ball-mill. These alloys were prepared from elemental powders of Co and Ti. The heat treatment of Co₆₇Ti₃₃ at 573, 873 and 1173 K crystallized nanoparticles of Co₂Ti and Co₃Ti compounds, while the same treatments conducted on Co₅₀Ti₅₀ resulted in the formation of Co₂Ti and CoTi nanoparticles. The saturation magnetizations reached a maximum value in the amorphous state and they decreased when the temperatures of the heat treatment rose. Demagnetizing interparticle interaction effects were estimated through hysteresis loops and initial magnetization curves using the Fourier technique.     

Effect of hardness and composition gradients on Barkhausen emission in case hardened steel

The effect of gradients in hardness, structure and composition in the surface layers on magnetic Barkhausen noise (MBN) was investigated in two widely used low alloy steels. One material was case hardened by induction hardening. The other was case carburised. Similar hardness profiles were produced by the two treatments. It was found that the variation in structure and hardness through the case in the induction-hardened steel had a minor effect on the MBN profile. In contrast, the inhomogeneity in the case-carburised material showed up clearly. This took the form of a broadened or two-peak MBN profile. When the surface layer containing the case was removed by etching, the broadened profile was replaced by a profile with a single peak. It is concluded that the shape and position of the MBN profile is significantly affected when a gradient in microstructure is induced by a gradient in carbon content. On the other hand, a gradient in microstructure induced by heat treatment with a constant carbon level has much less affect on the MBN profile for the induction-hardened steel.     

Microwave synthesis of magnetic Fe3O4 nanoparticles used as a precursor of nanocomposites and ferrofluids

Methods to synthesize magnetic Fe₃O₄ nanoparticles and to modify the surface of particles are presented in the present investigation. Fe₃O₄ magnetic nanoparticles were prepared by the co-precipitation of Fe³⁺ and Fe²⁺, NH₃·H₂O was used as the precipitating agent to adjust the pH value, and the aging of Fe₃O₄ magnetic nanoparticles was accelerated by microwave (MW) irradiation. The obtained Fe₃O₄ magnetic nanoparticles were characterized by Fourier transform infrared spectroscopy (FT-IR), transmission electron microscopy (TEM), X-ray powder diffraction (XRD) and vibrating sample magnetometer (VSM). The average size of Fe₃O₄ crystallites was found to be around 8–9 nm. Thereafter, the surface of Fe₃O₄ magnetic nanoparticles was modified by stearic acid. The resultant sample was characterized by FT-IR, scanning electron microscopy (SEM), XRD, lipophilic degree (LD) and sedimentation test. The FT-IR results indicated that a covalent bond was formed by chemical reaction between the hydroxyl groups on the surface of Fe₃O₄ nanoparticles and carboxyl groups of stearic acid, which changed the polarity of Fe₃O₄ nanoparticles. The dispersion of Fe₃O₄ in organic solvent was greatly improved. Effects of reaction time, reaction temperature and concentration of stearic acid on particle surface modification were investigated. In addition, Fe₃O₄/polystyrene (PS) nanocomposite was synthesized by adding surface modified Fe₃O₄ magnetic nanoparticles into styrene monomer, followed by the radical polymerization. The obtained nanocomposite was tested by thermogravimetry (TG), differential scanning calorimetry (DSC) and XRD. Results revealed that the thermal stability of PS was not significantly changed after adding Fe₃O₄ nanoparticles. The Fe₃O₄ magnetic fluid was characterized using UV–vis spectrophotometer, Gouy magnetic balance and laser particle-size analyzer. The testing results showed that the magnetic fluid had excellent stability, and had susceptibility of 4.46×10⁻⁸ and saturated magnetization of 6.56 emu/g. In addition, the mean size d (0.99) of magnetic Fe₃O₄ nanoparticles in the fluid was 36.19 nm.     

Strain-induced modification of magnetic structure and new magnetic phases in rare-earth epitaxial films

Rare earths exhibit complex magnetic phase diagrams resulting from the competition between various contributions to the magnetic energy: exchange, anisotropy and magnetostriction. The epitaxy of a rare-earth film on a substrate induces (i) a clamping to the substrate and (ii) pseudomorphic strains. Both these effects are shown to lead to modifications of the magnetic properties in (0 0 1)Dy, (0 0 1)Tb and (1 1 0)Eu films. In Dy and Tb films, spectacular variations of the Curie temperature have been evidenced. Additionally, Tb films exhibit a new large wavelength magnetic modulation. In Eu films, one of the helical magnetic domains disappears at low temperature whereas the propagation vectors of the other helices are tilted. The link between structural and magnetic properties is underlined via magnetoelastic models. Moreover, molecular beam epitaxy permits the growth of Sm in a metastable dhcp phase. The magnetic structure of dhcp Sm has been elucidated for the first time. In this review, neutron scattering is shown to be a powerful technique to reveal the magnetic structures of rare-earth films.     

Magnetic hysteresis of the magnetoresistance and the critical current density in polycrystalline YBa2Cu3O7−δ–Ag superconductors

A systematic study of the magnetic hysteresis in transport properties of polycrystalline YBa₂Cu₃O_7−δ–Ag compounds has been made based on two kinds of measurements at 77 K and under applied magnetic fields up to 30 mT: critical current density J_c(B_a) and magnetoresistance R(B_a). The R(B_a) curves show a minimum in their decreasing branch occurring at B=B_min which was found to be both the excitation current I_ex and the maximum applied magnetic field B_am dependent. In addition, for a certain value of B_am>5 mT, we have observed that B_min increases with increasing I_ex and reaches a saturation value. The J_c(B_a) curves show a maximum in decreasing applied magnetic fields occurring at B=B_max. We have also found that B_max increases with increasing B_am and reaches a saturation value. The minimum in the R(B_a) and the maximum in J_c(B_a) curves were found to be related to the trapped flux within the grains. All the experimental results are discussed within the context of the flux dynamics and transport mechanisms in these high-T_c materials.     

Defect clusters in titanium-substituted spinel-related lithium ferrite

The cation distribution in spinel-related titanium-substituted lithium ferrite, Li_0.5+0.5xFe_2.5−1.5xTi_xO₄ has been explored using interatomic potential and ab initio calculations. The results suggest that the cation distribution with Ti⁴⁺ substituting for Fe³⁺ on octahedral B sites and excess Li⁺ substituting for Fe³⁺ on tetrahedral A sites is stabilised by the formation of clusters of two octahedrally coordinated Ti⁴⁺ ions and one tetrahedrally coordinated Li⁺ ion linked through a common oxygen.