甲苯甲醇侧链烷基化反应中沸石催化剂酸碱中心的作用Ⅱ．改性的X型和双组分改性的X／ZSM－5双沸石催化剂

制备了改性的ｘ型和ｘ／ＺＳＭ－５型沸石催化剂，并对其进行了评价和ＴＰＤ、ＥＳＣＡ表征，将实验结果进行了关联。结果表明，采用ＫＯＨ，Ｈ＿３ＢＯ＿３和碱土金属化合物等作为改性剂，可以调变沸石催化剂的酸碱中心，其中碱酸密度比为０．５３９的ＫＸ（Ｂ＿３）·ＫＺＳＭ－５（Ｃａ）催化剂，能显著提高甲苯、甲醇侧链烷基化制取苯乙烯反应的选择性和收率。井根据对实验结果的分析，初步探讨了甲苯、甲醇侧链烷基化反应的机理。     

Low Temperature Sol-Gel Preparation of Nanocrystalline TiO2 Thin Films

TiO₂ nanocrystalline thin films with varying degree of porosity have been prepared using a low temperature method. TiO₂ films of the anatase form have been obtained by using a polyethylene glycol (PEG) modified sol-gel method. Densification and crystallization of the films was found to result from the thermal treatment of the dip coated films in boiling water. The films have been characterized by Raman, XRD, FTIR, AFM and optical methods. Highly transparent films with transmission in excess of 85% and porosity as high as 58% are formed predominantly of anatase crystallites of dimensions of the order of 5 nm. Initial results on lithium intercalation into these films resulting in an efficient optical modulation in the visible and near infrared regions demonstrate a good potential of these films for electrochromic applications.     

催化裂化汽油脱硫添加剂USY/ZnO/Al2O3的性能评价

 在固定流化床催化裂化装置上，以减压蜡油为原料，对制备的U\r\nSY／ZnO／Al2O3催化裂化汽油脱硫添加剂的性能进行了评价．结果表明\r\n，随着添加剂添加量和剂油比的增加，生成汽油的硫含量降低．在500\r\n℃和剂油比为5的条件下，在FCC平衡催化剂中添加30％的添加剂时，汽\r\n油的硫含量可由不加添加剂时的1230μg／g降低到770μg／g左右．添\r\n加剂的添加量（10％）较低时，对催化裂化产物的分布基本没有影响；\r\n添加30％的添加剂时，焦炭的产率有所增加，但汽油收率基本不变．X\r\nRD表征结果表明，USY／ZnO／Al2O3添加剂中的ZnO对USY的晶相结构有\r\n一定的破坏作用，但随着反应与再生次数的增多，ZnO与Al2O3之间形成\r\n较为稳定的锌铝尖晶石结构，使添加剂的性能趋于稳定．     

环境友好助洗剂——4A沸石

介绍了4A沸石的结构、性质及其作为洗涤助剂等方面的应用和国内外发展状况。     

Microwave synthesis,characterization and catalytic properties of titanium-incorporated ZSM-5 zeolite

Titanium-incorporated ZSM-5 zeolites (Si/Al = 50–200 and Si/Ti = 70) were successfully synthesized in a one-step sol-gel process under microwave irradiation. The characteristics of Ti-ZSM-5 zeolites were investigated using X-ray power diffraction, UV/Vis-DRS, FT-IR spectroscopy and solid-state ²⁷Al-NMR to monitor the physico-chemical properties. Simultaneously, the acidic properties were characterized by the NH₃-TPD profile. The characterization results revealed that the Ti⁴⁺ and Al³⁺ ions were well incorporated into the framework of Ti-ZSM-5 zeolite. The prepared zeolite was moderately active but selective in the dehydration of methanol to dimethyl ether.     

不同环大小分子筛对钼基分子筛催化剂上甲烷无氧芳构化反应的影响

 钼基分子筛催化剂，由于不同分子筛的孔道大小及孔道形状不同\r\n，对甲烷芳构化反应表现出不同的催化性能．具有8元环孔道结构的小\r\n孔ERS－7分子筛没有催化活性，说明甲烷的芳构化反应离不开分子筛孔\r\n道的择形作用，较小的孔道中不能生成苯等芳烃．具有10元环孔道结构\r\n的ZSM－5，ZSM－11和ZRP－1三种分子筛具有较好的催化性能，但由于\r\n其孔道大小及孔道形状的差别在催化行为上表现出一定的差异．具有1\r\n0元环和12元环孔道结构的MCM－22分子筛，尤其对苯等轻芳烃而言，催\r\n化性能最佳．具有12元环孔道结构的JQX－1以及中孔分子筛SBA－15，\r\n虽然具有一定的催化性能，但活性较低．研究结果表明，孔道大小与苯\r\n分子动态直径相近或孔道稍大的分子筛是催化甲烷芳构化反应的良好载\r\n体，孔道过大或过小都不利于苯和萘等芳烃的生成．     

提高非贵金属临氢脱腊催化剂异构化能力的研究

通过水热条件下合成分子筛试验条件的考察,获得了合成条件和性能良好的ZSM-8分子筛。采用无定形硅铝和ZSM-8分子筛制备出复合载体型的非贵金属临氢脱腊催化剂,通过锌和钨改性组分的添加,提高现有工业催化剂的异构化能力。实验结果表明,不同复合载体、改性组分对催化性能有较大影响,但改性组分的添加次序无明显作用。与以前β沸石基催化剂性能相比,ZSM-8基催化剂不仅提高了润滑油收率,而且产品润滑油的粘度指数也明显提高。催化性能的改进可以归结为改性后催化剂异构化能力的提高。     

正庚烷在β沸石负载碳化钼催化剂上的异构化研究

利用程序升温还原法制备了β沸石负载碳化钼催化剂。XRD表征显示，利用正戊烷作为碳源得到了对异构化具有活性的βMo2C。以正庚烷为模型反应物，在连续流动固定床反应装置上考察了温度、压力、空速和氢烃比对βMo2C/β沸石催化剂临氢异构化反应性能的影响。获得了β沸石负载碳化钼催化剂上正庚烷异构化的最佳反应条件温度270℃～275℃，压力1.0MPa～1.5MPa，体积空速1.0h－1，氢烃体积比200∶1。在最佳条件下反应物转化率为82%，选择性和异构产物收率分别达到71%和58%。     

Ω型分子筛脱铝的核磁共振研究

在不同投料比（ＳｉＯ２／Ａｌ２Ｏ３＝１３．８，１９及２１）条件下，合成了三种Ω型分子筛原粉．对投料比为１３．８的原粉样品进行了四种不同方式的脱铝处理，即水热、ＳｉＣｌ４、ＥＤＴＡ和（ＮＨ４）２ＳｉＦ６处理，而形成了系列脱铝Ω型分子筛样品．对原粉及其脱铝样品进行了２９Ｓｉ和２７ＡｌＭＡＳＮＭＲ测试，确定出样品骨架硅铝比和铝在两种晶体学不等价Ｔ位上的占据比率，以探索四种脱铝方法的效果．实验结果与分析表明：在所有样品中，铝原子的占据具有择优Ｂ位的倾向；且铝在ＴＡ与ＴＢ位上的占据比率与合成条件有关；四种处理方式对Ω型分子筛的脱铝效果不尽相同．