CRYSTAL STRUCTURE AND MORPHOLOGY OF NASCENT SAMPLES OF SYMMETRIC AROMATIC POLYESTERS——Ⅱ. POLY(p-PHENYLENE 2,6-NAPHTHALATE)

Confined thin film melt polymerization (CTFMP) of naphthalene chloride/hydroquinone (NCMQ, 1/1, molar)mixtures at polymerization temperatures (T_p) below ca. 300℃ resulted in relatively thick, elongated crystals. Polymerizationof NC/HQ above 300℃ between glass yielded well-formed lamellar crystals ca. 100 A thick. Phase Ⅰ and Ⅱ [001] EDpatterns were obtained for all T_p, the relative amount of phase Ⅰ increasing with T_p. Polymerization of naphthalenedicarboxylic acid/hydroquinione diacetate 1/1 mixtures at high T_p also yielded lamellar crystals that "curled up" off of thesubstrate. When the high temperature CTFMP polymerization was conducted between mica, aggregates of lamellae on-edgedeveloped but epitaxial growth did not occur. Epitaxial growth of lamellae between mica could be obtained, however, byconfined thin film solution polymerization, with both of the latter samples yielding apparently related ED patterns from adifferent unit cell than phase Ⅰ or Ⅱ. Fiber patterns, obtained from sheared samples, indicated considerably greater crystaldisorder than in the nascent crystals. Refinement of the phase Ⅰ unit cell parameters, based on the [001] and [01 1] EDpatterns, with modeling based on Cerius~2, suggests a monoclinic phase Ⅰ unit cell with a = 7.76, b = 5.71, c = 14.99 A, α = γ= 90°, β= 99.7°, ρ = 1.47 g/cm~3, space group P12_1/al.     

Sol-Gel Particulate Float Process to Make Vitreous Silica Bodies

Particulate sol-gel technology uses larger particles than that of alkoxide-derived gels and provides larger pore sizes in the gelled object. This allows relatively rapid drying and fabrication of large rods or tubular shapes. However, the formation of more complex or flat shapes, which require extensive surface contact with a mold, is more difficult. The shrinkage during drying, with the significantly greater stress of surface friction due to adhesion, frequently leads to cracking.We have demonstrated a solution to this problem by floating the gel on the surface of a dense liquid. Dry silica panels up to 28 × 40 × 0.7 cm³ were prepared in this way. The use of patterning molds allowed the fabrication of more sophisticated shapes. These bodies were sintered to transparent vitreous silica articles of near net dimensions.     

Preparation of silane-grafted pellets: silica bound reagents in a very convenient form

High surface area silica pellets are excellent supports for the preparation of silica supported reagents and solid-phase basal linkers through reaction with (RO)₃Si(CH₂)₃FG (FG=NH₂, NHMe, Cl, NHC(O)NH₂, OC(O)CMe(CH₂), NCO, NEt₂). High loadings (0.66-2.15 mmol g⁻¹) of grafted silane materials are realised at synthetically useful loadings per pellet (ca. 0.06 mmol). Preliminary trials show that trial linker chemistry and ligand synthesis can be carried out on these materials and that these reactions can be monitored by solid state ¹³C NMR studies on individual pellets.     

FexNi100−x nanometric films deposited by laser ablation on SiO2/Si substrates

Fe_xNi_100−x nanometric films were deposited on SiO₂/Si substrates at room temperature using the pulsed laser deposition technique. The targets were Fe-Ni amorphous magnetic foils with composition Fe₅₀Ni₅₀, Fe₃₅Ni₆₅ and Fe₂₂Ni₇₈. Morphological and structural properties of the deposited films were investigated using scanning electron microscopy, Rutherford backscattering spectrometry, grazing incidence X-ray diffraction, and X-ray reflectivity. Electrical and magnetic characteristics of the films were investigated by using the four-point probe and the magneto-optic Kerr effect techniques, respectively. The film properties are strictly dependent on the Fe-Ni compositional ratio.     

Laser Annealing of Thin-Film Ferroelectric Heterostructures

Preliminary experiments on laser annealing of ferroelectric samples by ultraviolet radiation of a KrF laser are carried out. In principle, laser annealing allows one to reduce appreciably the duration of thermal action, minimize the size of the samples treated, and control the crystallization processes in the samples. A special focussing system was employed to provide homogeneous irradiation of the spot with dimensions of ~1×1 cm² within a broad energy range from 0.1 to 10~J per pulse. The range of energy densities leading to phase transitions in thin films is determined.     

金属UV光敏薄膜的实验研究

介绍了金属Au和Al薄膜的制备方法，研究了其UV光电发射特性，并做了寿命实验。给出了在真空中以及放在大气中光电发射衰减的情况。指出了其在大气中达到一个稳定值之后，再反复多次暴露于干燥大气时仍存在一个稳定光电发射周期的特点，可长达数月。金属薄膜有一个最佳膜层厚度，这与光电发射逸出深度、膜层结构等密切相关。近年来光电子成像器件发展非常迅速，急需光电发射均匀的面电子源，因此在微通道板的特性测试和像管的动态模拟中，Au和Al金属薄膜成为被优选的对象。     

Cu-MgF2复合纳米金属陶瓷薄膜的电导特性研究

用射频磁控共溅射法制备了Cu体积分数分别为 10 % ,15 % ,2 0 %和 3 0 %的Cu MgF2 复合金属陶瓷薄膜 .用x射线衍射、x射线光电子能谱和变温四引线技术对薄膜的微结构、组分及电导特性进行了测试分析 .微结构分析表明 :制备的Cu MgF2 复合薄膜由fcc Cu晶态纳米微粒镶嵌于主要为非晶态的MgF2 陶瓷基体中构成 ,Cu晶粒的平均晶粒尺寸随组分增加从 11 9nm增至 17 8nm .5 0— 3 0 0K温度范围内的电导测试结果表明 :当Cu体积分数qM 由 15 %增加到 2 0 %时 ,Cu MgF2 复合薄膜的电阻减小了 8个量级 ,得出制备的复合薄膜渗透阈qCM 应处于 15 %和 2 0 %之间 .qM 在 10 %和 15 %之间的薄膜呈介质导电状态 ,而在 2 0 %和 3 0 %之间的薄膜则呈金属导电状态 .从理论上讨论了复合薄膜中杂质电导和本征电导的激活能及其对电导的贡献 ,并讨论了Cu MgF2 复合纳米金属陶瓷薄膜的渗透阈 ,得到了和实验一致的结果     

60keV质子辐照对TiNi记忆合金薄膜马氏体相变的影响

 利用磁控溅射的方法在氧化后的单晶Si基片上制备了TiNi形状记忆合金薄膜，利用示差扫描量热法和原位X射线衍射研究了薄膜的马氏体相变特征。通过60keV质子注入（辐照）薄膜样品研究了H+离子对合金薄膜马氏体相变特征的影响，结果表明氢离子注入后引起了马氏体相变开始Ms和结束点Mf以及逆马氏体相变开始As和结束温度Af的下降，而对R相变开始Rs和结束温度Rf影响不大。掠入射X射线衍射表明H+离子注入后有氢化物形成。H⁺离子注入形成的氢化物是引起相变点的变化的主要因素。     

超分子有机薄膜

利用超分子有机薄膜技术能制成新的传感分子电子器件、光学器件和生物分子器件等，受到跨学科高技术研究领域的重视。本文描述了超分子有机薄膜的制备方法以及在各应用领域的研究状况。重点介绍了我们研究组在近20年工作中，利用LB膜技术，在光电器件、气体传感技术和光学非线性，特别是在生物传感技术方面的研究成果。按照生物体系提供的信息，模拟合成功能分子，建造有组织的分子组装体，以便用来研究依赖于分子排列的生物物理化学效应。     

Micromechanisms and Mechanics of Damage and Fracture in Thin Film/Substrate Systems

The purpose of this paper is to review the mechanisms and available theoretical methods for modeling the strength and failure of thin film/substrate systems