激光拉曼光谱研究NiMoP浸渍液活性组分的结构 Ⅱ.不同有机添加剂的影响

采用激光拉曼光谱（LRS）技术对添加有乙二醇和柠檬酸的NiMoP浸渍液和用该浸渍液制备的NiMoP/Al₂O₃催化剂进行了表征,研究了乙二醇和柠檬酸含量对NiMoP浸渍液及浸渍过程中活性相组成、结构的影响。结果表明,乙二醇使NiMoP(0.063)浸渍液中H_{x\[PMo11O39\]⁽7-x)- 或Hx\[PMo9O31\]⁽3-x)-及Hx\[PMo12O40\]⁽3-x)- 杂多阴离子结构转化成Hx\[P2Mo5O23\]⁽6-x)- 结构,而柠檬酸能保持NiMoP(0.063)浸渍液中Hx\[P2Mo5O23\]⁽6-x)-、Hx\[PMo11O39\]⁽7-x)- 或Hx\[PMo9O31\]⁽3-x)-及Hx\[PMo12O40\]⁽3-x)-杂多阴离子结构共存,但导致Hx\[P2Mo5O23\]⁽6-x)-含量降低,Hx\[PMo12O40\]⁽3-x)-含量升高。相对乙二醇而言,柠檬酸有机添加剂能够更有效地阻止浸渍过程中各杂多阴离子结构在载体氧化铝孔道中的分解。}     

制备方法对Ag-Ru/CeO2氨合成催化剂性能的影响

采用共沉淀法（CP）、改性沉淀沉积法（MDP）、浸渍法（IP）制备了Ag-Ru/CeO₂催化剂,并运用N₂物理吸附、X射线衍射（XRD）、H₂程序升温还原（H₂-TPR）、N₂程序升温脱附（N₂-TPD）等技术对其进行了表征,考察了个同制备方法对Ag-Ru/CeO₂催化剂氨合成性能的影响.结果表明:不同方法制备的催化剂,银助剂对载体的还原性能和氮气的解离吸附性能的影响存在明显的差别,从而影响了催化剂的氨合成活性,其中采用浸渍法制备的催化剂氮气解离吸附最强,载体最易于还原,因此催化剂低温氨合成活性最高,在10 MPa,10000 h^-1,400℃反应条件下,出口氨浓度达到9.4%.     

Preparation of hierarchical mesoporous Zn/HZSM-5 catalyst and its application in MTG reaction

The hierarchical mesoporous Zn/ZSM-5 zeolite catalyst was prepared by NaOH treatment and Zn impregnation, and its application in the conversion of methanol to gasoline (MTG) was studied. N2 adsorption-desorption results showed that the mesopores with sizes of 2–20 nm in HZ5/0.3AT was formed by 0.3 M NaOH alkali treatment. The zeolite samples after modification were also characterized by XRF, AAS, XRD, SEM and NH3-TPD methods. Zn impregnated catalyst Zn/HZ5/0.3AT exhibited dramatic improvements in catalytic lifetime and liquid hydrocarbons yield. The selectivity of aromatic hydrocarbons was also improved after Zn impregnation. It is suggested that the mesopores of Zn/HZ5/0.3AT enhanced the synergetic effect of Zn species and acid sites and the capability to coke tolerance, which were confirmed by the results of catalytic test and TGA analysis, respectively.     

Comparison of two preparation methods of supported Li?Ni catalyst on alumina for selective oxidation of methane

Lithium-added nickel catalysts on alumina were prepared for CO₂ reforming of methane by two methods, precipitation and impregnation. Performances of the catalysts were investigated by TG, CO-adsorption and SEM analysis. The catalyst with ratio of Li/Ni=1.0 prepared by precipitation method has high nickel dispersion, catalytic activity and stability for CO₂ reforming of methane.