碳纳米管的化学修饰研究进展

介绍了近年来碳纳米管化学修饰(共价修饰和非共价修饰)方面的最新进展。参考文献47篇。     

无相移滤波技术用于分析化学信号处理

把无相移滤波技术引入了分析化学信号处理领域。其方法为：先将输入序列按顺序滤波，然后将所得结果逆转后反向通过滤波器，再将所得结果逆转后输出。通过对色谱信号的实验研究表明，与普通的数字滤波方法相比较，无相移滤波不但具有普通数字滤波的优点，而且不会产生滤波前后的相位偏移，具有良好的应用前景，尤其对于需要准确计算保留时间的场合，用此预处理方法非常适合。     

La2Zr2O7催化剂结构相变对甲烷氧化偶联反应性能的影响

采用共沉淀法并通过改变焙烧温度制备了一系列具有不同晶相结构的La₂Zr₂O₇催化剂，在微型固定床反应器上评价其甲烷氧化偶联反应性能，并利用XRD、Raman、CO₂-TPD、XPS等表征手段，探究催化剂的物相结构、表面碱性以及表面氧物种的变化规律。结果表明，随着焙烧温度从700℃逐渐升高到1200℃，La₂Zr₂O₇催化剂结晶度不断提高，晶相发生明显变化，从无定形结构逐渐向缺陷萤石结构过渡，最终转变成烧绿石结构。焙烧温度提高促使La₂Zr₂O₇晶相转变过程中，催化剂表面的碱性强度减弱，中等碱性位数量以及具有催化活性的表面氧物种O₂^2-和O₂^-的相对含量不断减少，致使催化剂的CH₄转化率和C₂₊选择性不断降低。其中，无定形LZO-CP-700催化剂表现出最佳的甲烷氧化偶联反应性能。     

Synthesis, Crystal Structure and Electrochemical Properties of One-dimensional Chain Coordination Polymer [Co(Ⅱ)(C6H5CH=CHCOOH)2(4,4''-bipy)(H2O)5]n

A one-dimensional chain coordination polymer [Co(Ⅱ)(C6H5CH=CHCOOH)2(4,4'-bipy)(H2O)5]n has been synthesized with cinnamylic acid, 4,4'-bipy and cobaltous chloride as raw materials. Crystal data for this complex: monoclinic, space group P21/c, a - 1.1481(3), b =1.1230(2), c = 1.1759(3) nm, β = 97.054(4)°, V = 1.5046(6) nm3, Mr= 617.50, Dc = 1.363 g/cm3, Z= 2, μ(MoKα) = 0.627 mm-1, F(000) = 646, S = 1.062, R 0.0443 and wR = 0.1178. The crystal structure shows that two neighboring cobalt(Ⅱ) ions are linked together by one 4,4'-bipy, and the whole complex molecule adopts a one-dimensional chain structure. Each cobalt(Ⅱ) ion is coordinated with two nitrogen atoms from two 4,4'-bipy molecules and four oxygen atoms from four water molecules, giving a distorted octahedral coordination geometry. The electrochemical properties were analyzed by combining with the crystal structure.     

PEMFC阴极中氧扩散和电化学反应模型研究—I．TFFA模型及其数值计算

将薄膜浸渍聚集体（TFFA）模型用于描述质子交换膜燃料电池（PEMFC）阴极中氧的扩散和反应过程，其中包括氧气在气体扩散层和反应层气体通道中的扩散，氧气在反应层薄膜中的溶解和扩散，氧在反应层浸渍聚休体中的扩散和反应以及电子和离子的传导，并根据PEMFC阴极的结构特点给出TFFA模型的数值解法。     

纳米晶型MnCo2O4的微波加热法制备及其电催化性能

以Co和Mn的醋酸盐为原料,采用共沉淀法制得草酸盐前驱物,加入一定量微波吸波剂乙炔黑后,用微波进行热处理制得复合氧化物MnCo2O4.X射线衍射和扫描电镜结果表明,产物为纳米晶型,结晶良好,纯度较高,粒径为10~20nm且分布均匀.在室温下、空气气氛中,以6mol/L的KOH溶液为电解液测试了由MnCo2O4制备的空气扩散电极对氧还原反应的催化效果.极化曲线显示,在-0.2V(vsHg/HgO)电位下,氧还原反应电流密度达96mA/cm2.为显示微波加热法的优越性,用马弗炉煅烧制备了MnCo2O4,并对两种热处理方法所得产物的物化性能进行了比较.     

Study of migration of active components of phosphorescent oxygen sensors for food packaging applications

A study of migration of the active components of oxygen sensors into food is presented. Six types of sensors, based on different oxygen sensitive dyes (two metalloporphyrins and one ruthenium dye), polymers (polystyrene and polysulfone) and support materials, were exposed to a number of standard ‘food simulants’ recommended by FDA/EU guidelines and then assayed for migration or sensor components and changes in oxygen calibration. Both metalloporphyrin sensor dyes leached only in olive oil and in 95% ethanol (used as a positive control), at maximum levels of 19.22 μg/dm² for PtOEPK and 113.96 μg/dm² for PtTFPP. The RuDPP dye showed maximum leaching in 95% ethanol (25.19 μg/dm²) while also migrating in an acidic aqueous simulant. Planar supports such as polyester tended to enhance the stability of the sensor. Migration of the styrene monomer from the polystyrene encapsulation medium was concluded to be low enough to be insignificant. Migration of sensor components was shown to correlate with the changes in sensor response to oxygen. Based on these results, sensor combinations were ranked on the basis of their resistance to leaching and their general stability, safety and suitability for use on a large scale in packaged foods and related food applications was proven.     

Properties of ITO films prepared by reactive magnetron sputtering

Indium tin oxide (ITO) thin films were deposited by mid frequency pulsed dual magnetron sputtering using a metallic alloy target with 10 wt.% tin in an atmosphere of argon and oxygen. The aim of the work was to study the interdependence of structural, electrical and optical properties of ITO films deposited in the reactive and transition target mode, respectively. The deposition rate in the transition mode exceeds the deposition rate in the reactive mode by a factor of six, a maximum value of 100 nm·m min⁻¹ could be achieved. This corresponds to a static deposition rate of 200 nm min⁻¹. The lowest electrical resistivity of 1.1·10⁻³ Ω cm was measured at samples deposited in the high oxygen flow range in the transition mode. The samples show a good transparency in the visible range corresponding to extinction coefficients being below 10⁻². X-ray diffraction was used to characterise crystalline structure as well as film stress. ITO films prepared in the transition mode show a slightly preferred orientation in (211) direction, whereas films deposited in the reactive mode are strongly (222) oriented. Compared to undoped In₂O₃ all samples have an enlarged lattice. The lattice strain perpendicular to the surface is about 0.8% and 2.0% for films grown in the transition and the reactive mode, respectively. Deposition in the transition mode introduces a biaxial film stress in the range of −300 MPa, while stress in reactive mode samples is −1500 MPa.     

Thermal and structure analysis of FeSO4·H2O-BaO2 mixtures

Investigations on the thermal decomposition of FeSO₄·H₂O-BaO₂ mixtures were carried out under isothermal conditions by using simultaneously solid electrolyte cell (EMF-method). Evoked interactions producing oxygen in the temperature range 553-673 K were established by means of a solid electrolyte oxygen analyzer. Based on Mössbauer spectroscopy data and X-ray analysis it was proved that these reactions were associated with the release of oxygen from barium peroxide, oxidation of ferrosulphate-monohydrate to FeOHSO₄, and formation of barium ferrites such as BaFe₂O₄ and BaFe₁₂O₁₉.