A Novel Cu-Mo／ZSM-5 Catalyst for NOx Catalytic Reduction with Ammonia

The Cu-Mo/ZSM-5 catalysts with different Cu/Mo ratios were prepared by wet impregnation method, and their catalytic performance for selective catalytic reduction of NOx was studied. The results showed that Cu-Mo/ZSM-5 is a very effective catalyst for NOx catalytic reduction with ammonia, especially when Cu/Mo molar ratio is about 1.5. It not only exhibited the extremely high catalytic activity, but also showed good stability for 02. The bulk phase structure of Cu-Mo/ZSM-5 catalysts was determined by XRD technique, and the results indicated that there is a maximum dispersion for Cu species when Cu/Mo molar ratio is 1.5, and an interaction between Cu and Mo along with HZSM-5 may be present in Cu-Mo/ZSM-5, which may possibly result in a special structure favorable for the catalytic reduction of NOx over Cu-Mo/ZSM-5 catalyst.     

PVDF／PAN共混超滤膜

ＰＶＤＦ／ＰＡＮ共混超滤膜尹秀丽＊宋艳秋（天津纺织工学院材料科学系天津３００１６０）关键词聚偏氟乙烯，聚丙烯腈，共混，超滤膜１９９６－１１－２０收稿，１９９７－０５－０７修回共混是改变高分子材料性能的重要手段，已发现用聚合物共混的方法能制得性能优异的...     

铈杂多配离子-水滑石超分子层柱材料ZnAl-Ce(PMoV)2的插层组装、表征及催化性能

以十四酸根阴离子柱撑Zn-Al水滑石Zn0.77Al0.22(OH)2.0.22C13H27COO.0.81 H2O(记为ZnAl-14A)为预撑前体,在水溶液中用离子交换法将以2∶17缺位杂多酸根离子(P2Mo16VO61)11-记为(P Mo V)为配体的稀土杂多配阴离子Ce(P2Mo16VO61)219-(记为Ce(PMoV)2)插层组装到水滑石层板间,合成了一种具有大的层间距(3.37 nm)的超分子插层材料Zn0.77Al0.23(OH)2.0.0105[Ce(P1.9Mo15.7V1.1O61)2].0.011C13H27COO.0.83H2O(记为ZnAl-Ce(PMoV)2)。用ICP,IR,XRD和DTA对产物的组成和结构进行了表征。结果表明,该产物中Ce(PMoV)2配阴离子沿其长轴垂直于层板的方向分布于水滑石层间;产物具有规整的层状结构和热稳定性;产物对乙酸与正丁醇的酯化反应,二甘醇的脱水-环化反应和H2O2氧化环己烷的反应有良好的催化性能,且易于回收重复使用。     

Aluminium(III) as a promoter of cellular oxidation

Aluminium has been known as a neurotoxic agent to experimental animals since the last century (Arch. Exp. Pharmacol. 40 (1897) 98). However, great interest arose in it bioinorganic chemistry as well biology when it was demonstrated to be the causative agent in pathologies related to the long-term dialysis treatment of uremic subjects with renal failure (Life Chem. 11 (1994) 197), and as a potential etiopathogenic cofactor for several neurodegenerative diseases. The inorganic biochemistry of aluminium is still largely to be discovered. In this review the pro-oxidative property of aluminium toward biological membrane will be presented and its implications in involvement in human pathology will be discussed in an interdisciplinary frame from the bioinorganic point of view.     

丙烷在无机膜反应器中的芳构化

研究了在固定床反应器和膜反应器中的丙烷芳构化，考察了ＨＺＳＭ－５担载的Ｇａ和Ｐｔ－Ｇａ催化剂对反应的影响。结果表明，采用无机膜反应器可以提高丙烷芳构化选择性，从而提高芳烃收率达１０％以上。在膜反应器中，低碳烷烃选择性降低，烯烃选择性增强。固定床相比，膜反应器在低温时对芳构化反应的促进作用最为显著，但是随着温度升高，其促进作用减弱。     

Synthesis of (trichloromethyl)organosilanes by catalytic decarboxylation of (trichloroacetoxy)organosilanes

A method for preparing (trichloromethyl)organosilanes by the catalytic decarboxylation of the corresponding trichloroacetoxysilanes RMe₂SiOC(O)CCl₃ (R = Me, ClCH₂, Ph, Me₃Si, and H) has been developed. The method involves heating the starting compounds without a solvent in the presence of a catalyst (quaternary ammonium salts or potassium salts with the addition of crown ethers). Tertiary amines (Et₃N, Bu₃N) catalyze this reaction only when heating is carried out in donor aprotic solvents (THF, acetonitrile) in the presence of oxygen. Thermal decomposition of (trichloroacetoxy)organosilanes, in contrast to catalytic decarboxylation, begins at a higher temperature and yields a mixture of products.Translated fromIzvestiya Akademii Nauk. Seriya Khimicheskaya, No. 1, pp. 150–153, January, 1995.     

介孔混合氧化物催化剂La-Co-Zr-O的制备与表征

 采用柠檬酸络合-有机模板剂分解法制备了(La+Co)/(La+Co+Zr)原子比为0.5的La-Co-Zr-O催化剂,并与传统的共沉淀法制备的La-Co-Zr-O催化剂进行比较. N2物理吸附结果表明,采用模板剂法制备的催化剂样品具有较大的比表面积(96.6～117.6 m2/g)和十分均匀的孔径(3.5～4.3 nm); X射线衍射、X射线光电子能谱和X射线吸收精细结构表征结果一致表明,催化剂中活性组分主要为高分散的Co3O4微晶(粒径为23～33 nm), 模板剂法制备的催化剂中所有组分的分散性均优于共沉淀法制备的催化剂. 程序升温还原实验结果表明,采用聚乙二醇辛基苯基醚与十六烷基三甲基溴化铵为混合模板剂制备的催化剂中Co3O4更容易被还原. Co-O 键的活动度与催化剂催化氧化反应的活性密切相关.     

催化褪色光度法测定痕量铁--Fe(Ⅲ)+亚甲基蓝+过氧化氢体系

研究了在硫酸介质中,微量铁(Ⅲ)催化过氧化氢氧化亚甲基蓝的褪色反应,建立了测定痕量铁方法.灵敏度为8.0×10-8g/mL,线性范围为0～1.000 0g/mL,用于自来水中铁的测定,结果与实际接近,相对标准偏差为0.67%.     

CdSe纳米线阵列的制备及其表征(英)

通过在含有SeSO₃^2-和Cd²⁺的室温水溶液中，用模板-电沉积法在纳米孔阵列阳极氧化铝膜(AAM)模板中制备了高有序性的CdSe纳米线阵列，并对其形貌、结构和组分进行了表征。扫描电子显微镜(SEM)和透射电子显微镜(TEM)结果表明，纳米线阵列中的CdSe纳米线具有相同的长度和直径，分别对应于使用的AAM模板的厚度和孔径；X-射线衍射(XRD)和X-射线能谱(EDAX)结果表明，CdSe纳米线中Cd和Se的化学组成非常接近于1∶1，其结构为立方CdSe。另外，对模板-电沉积法制备CdSe纳米线的机理进行了讨论。     

Complete Oxidation of Methane over Palladium Supported on Alumina Modified with Calcium,Lanthanum,and Cerium Ions

The activity and thermal stability of Pd/Al_2O_3 and Pd/(Al_2O_3 MO_x)(M=Ca,La,Ce) palladium catalysts in the reaction of complete oxidation of methane are presented in this study.The catalyst supports were prepared by sol-gel method and they were dried either conventionally or with supercritical carbon dioxide.Then they were impregnated with palladium nitrate solution.The catalysts with unmodified alumina had a high surface area.The activity and thermal stability of the alumina- supported catalyst was also very high.The introduction of calcium,lanthanum,or cerium oxide into alumina support caused a decrease of the surface area in the way dependent on the support precursor drying method.These modifiers decreased the activity of palladium catalysts,and they required higher temperatures for the complete oxidation of methane than unmodified Pd/Al_2O_3.The improvement of the palladium activity by lanthanum and cerium support modifier was observed only at low temperatures of the reaction.