聚酰亚胺/SiO2杂化膜的制备、表征和气体渗透性能

采用溶胶凝胶法,在以TiO2为过渡层的硅藻土-莫来石陶瓷膜管基底上,制备了组分不同的聚酰亚胺/SiO2杂化膜。聚酰亚胺是利用4,4′-六氟亚异丙基邻苯二甲酸酐、2,4,6-三甲基-1,3-苯二胺和3,5-二氨基苯甲酸在溶液中进行亚胺化完成的。采用FT-IR、TG/DTA、DSC、SEM、BET和气体渗透测定对膜进行了表征和测试。结果表明,聚酰亚胺通过支链上的羧酸基和SiO2相键连织构成了具有规则孔道的空间网状结构,并且随着SiO2含量的增加孔径逐渐减小;杂化膜具有较高的热稳定性和有机无机兼容性;相对于聚酰亚胺膜,杂化膜对H2、CO2和H2O与N2相比较具有较高的分离性,SiO2含量为25(wt)%的杂化膜对H2/N2、CO2/N2和H2O/N2的分离因子分别达到55.9、31.1和42.8。     

Characterisation of raw materials for production of ceramics

The aim of this paper is to characterize some raw materials used for ceramics material production. Five samples of clay have been analyzed. It has been carried out a patterned sampling in a quarry in Rosarno (South Italy). Chemical-physical properties on clay samples are determined. Test pieces have been prepared and physical properties after firing are determined by DSC thermal analysis, XRD analysis and X-ray fluorescence. It is important to note the high amount of Fe₂O₃. The mixture principally contains quartz, illite and oligoclase. It has been observed the colour and the shape after firing: predominant colour is red. In this case the clay has been used in mixtures covered with glazes. The colour of internal clay is hidden by opaque of glazes. The analysed raw materials can be used in a slip for single fired red tiles. The A2sp clay produces best ceramics at 1000°C.     

Sm2Fe17合金的氢化-歧化过程演化

通过X射线衍射(XRD)、扫描电镜(SEM)和能谱分析(EDX)等手段重点研究了Sm2Fe17合金在氢化-歧化过程中的相组成、相的变化以及微观结构的演化规律。研究表明：在0．1MPa的H2气氛下，Sm2Fe17合金首先吸氢；400℃时合金出现部分脱氢现象；在T≥500℃逐渐开始歧化为SmHx和α—Fe，同时生成了大量的微晶或非晶组织；随着温度的升高，合金中的微晶非晶逐渐晶化，750℃时晶化完全，晶粒长大至20～100nm。通过对Sm2Fe17合金的氢化一歧化过程研究，建立了该过程的微观结构变化规律的物理模型。     

氯化钠在球形纳米氧化铈形成过程中的作用

以水合碳酸铈为原料, 以氯化钠作为助磨剂和阻聚剂, 采用机械活化法制备了球形纳米氧化铈, 用XRD法研究了水合碳酸铈与氯化钠质量比、球磨时间、煅烧温度对CeO2粉体晶粒度的影响, 用TEM对最终产物粒子进行形貌观察. 结果表明: 在碳酸铈的球磨过程及其随后的煅烧过程中, 氯化钠的存在起到了很好的助磨和阻聚作用, 所得CeO2为类球形粒子, 分散性较好, 晶粒度约为30～50 nm.     

Some aspects of diffusion: fluctuations in reaction diffusion,and geometric influences in nonuniform media

Summary We deal with two diffusion problems: Space-integrated conserved entities characterizing very fast - diffusion - controlled reactions, such as time lags, etc. are universal. They are given by relationships which do not reflect the failure of the mean field hydrodynamic equations. We present another application which does not reflect this failure, for determining the surface flux via a diffusion controlled reaction producing a colored product. Another anomalous diffusion process we considered is transport through cellular materials whose cell sizes are highly nonuniform. We have analyzed the effects of extreme nonuniformity by considering fractal-like models of cellular solids. The diffusion current through these models can exhibit anomalous time-dependencies which are not predicted by the diffusion equation. In particular, it is shown that the initial diffusion current can be characterized by a power-law dependence on the time. Furthermore, the exponent of the power law is given in terms of the distribution of cell sizes in the fractal-like cellular solid.     

Temperature programmed reduction of silica supported nickel catalysts

Nickel oxide promoted catalysts are prepared by simple precipitation, precipitation from homogeneous solution and impregnation methods and their reduction behavior is monitored with temperature programmed reduction (TPR) technique. The effect of different parameters such as metal loading, method of preparation and heat treatment temperature are also observed on the reducibility of the catalysts. It is observed that reduction temperature increases with the increase of calcination temperature. Results indicate that the interactions between nickel oxide and silica begin with the increase of calcination temperature which leads to the formation of nickel hydrosilicates and are responsible for high temperature reduction peaks.     

掺杂稀土元素对细晶BaTiO_3系统耐压及介电性能的影响

研究了稀土元素Ho2O3和Er2O3掺杂BaTiO3基瓷料,其在BaTiO3系晶粒中可抑制晶粒生长,使晶粒尺寸变小,体密度增高,呈现细晶效应,ε峰在整个温区范围内弥散,提高室温下介电常数,减小容量变化率。本系统中三价稀土氧化物Ho2O3和Er2O3等物质同时加入到BaTiO3陶瓷中后,稀土氧化物没有全部进入晶格内部发生取代,其中的一部分与其他添加剂形成一些非铁电相,提高耐压;另一部分留在晶界处,成为晶粒抑制剂,使得晶粒细小,瓷体致密,提高陶瓷的耐压。     

Siloxane-Based Nanobuilding Blocks by Reaction Between Silanediol and Trifunctional Silicon Alkoxides

The preparation of nanostructured organic-inorganic materials by assembling of nanobuilding blocks allows controlling the extent of phase interaction, which in its turn governs structure-properties relationships. We present here the synthesis of siloxane-based nanobuilding blocks prepared by reacting diphenylsilanediol with vinyltriethoxysilane and triethoxysilane. The reaction products were obtained by non-hydrolytic condensation between silanediol and ethoxide groups in inert atmosphere, in the presence of pyridine, triethylamine or butyl lithium. Different synthetic conditions were examined by means of ATR-FTIR and NMR spectroscopies, showing the formation of siloxane bonds. In the case of triethoxysilane the reaction carried out in the presence of pyridine leads to Si–H bond preservation in the final product. Air stable products with improved Si–O–Si hydrolytic stability can be obtained by removal of the base after the reaction completion. The condensation products can be described as a mixture of siloxane rings involving difunctional and trifunctional silicon units.