Effect of N2O pretreatment on fresh and regenerated Pd-Ag/α-Al2O3 catalysts during selective hydrogenation of acetylene

N₂O pretreatment has shown to result in enhancement of the performance of fresh commercial Pd-Ag/α-Al₂O₃ catalyst during selective acetylene hydrogenation. However, it showed no effect for the used and regenerated catalysts probably due to changes int he metal arrangement on the catalyst surface after regeneration.     

植入用Co—Cr—Mo合金与Ti—6Al—4V合金的电偶腐蚀研究

组件式设计常被用地人工髋关节，钴络钼合金（Ｃｏ－Ｃｒ－Ｍｏ）与钛合金（Ｔｉ－６Ａｌ－４Ｖ）的压配最常用，本文应用电化学方法研究了静态条件下两种合金的电偶腐蚀行为，浸泡实验表明，钴络钼合金为阳极，但电偶电流与其维钝电流相近，并无明显加速度腐蚀效应，钛合金为阴极，受到保护，失重及金相观察结果显示，在４５天的浸泡实验周期内，未发现腐蚀痕迹，混合电位理论和电位处于两种合金的钝化电位区，电偶电流为合金的维钝     

Pt/Au双金属纳米粒子的制备及表征

Poly (N-vinyl-2-pyrrolidone)-protected Pt/Au bimetallic nanoparticles were obtained by reducing the mixture of HAuCl4 and H2PtCl6 with sodium borohydride. UV-vis spectra, transmission electronic microscopy and X-my diffraction reveal that the prepared bimetallic nanoparticles are of alloy structure.     

高频燃烧红外吸收光谱法测定钨钛合金中碳含量

建立高频燃烧红外吸收光谱法测定钨钛合金中碳含量的分析方法。在1980 W分析功率下,称取0.3 g样品,以2.0 g钨锡及0.5 g纯铁混合助熔,用高频红外分析仪测定碳。碳的含量在0.013%~0.050%范围内与红外吸收峰面积线性相关,相关系数为0.9993。碳的测定下限为3.6μg/g,方法检出限为1.08μg/g。该法测定结果的相对标准偏差为2.97%~4.11%(n=8),碳的加标回收率为96.2%~103.1%。该方法能够满足合金中碳含量的分析要求。     

钇对Nd-Fe-Al-Ni非晶合金热稳定性与晶化行为的影响

采用差示扫描量热法（DSC）、X射线衍射（XRD）和透射电镜（TEM）研究了Y对Nd-Fe-Al-Ni非晶合金热稳定性和晶化行为的影响。结果表明,淬火态的Nd60Fe20Al10Ni10-xYx（x=0,2）合金基本为非晶组织同时还含有少量的淬态相,Y的加入抑制了淬态相的析出。加入Y后,非晶合金的晶化开始温度和晶化峰值温度都向高温方向移动,证明其热稳定性提高。Y的加入改变了合金的晶化方式和最终晶化产物,使非晶基体中析出的晶化相更加弥散圆整细小。并且Y具有在化学上钝化氧杂质的作用,从而抑制了氧的有害作用。利用Kissinger方程获得了Nd60Fe20Al10Ni8Y2非晶合金的晶化开始和晶化峰值激活能分别为1.21和1.16 eV。     

载体γ-Al2O3和钐对非晶态NiB合金热稳定性的影响

用化学还原法制备了NiB、NiB/Al2O3和NiBSm/Al2O3三种催化剂，它们都呈非晶结构.用等离子耦合发射光谱仪(ICP)对催化剂组分进行了分析，采用差示扫描量热法（DSC）对三种催化剂进行了热稳定性分析.结果表明，载体的引入使非晶态NiB合金的体相组成中B的含量降低.将非晶态NiB合金负载到γ-Al2O3上,可以明显改善非晶态合金的热稳定性，少量Sm可以进一步提高晶化温度.晶化激活能数据亦表明了载体和Sm对非晶结构具有良好的稳定作用.载体和Sm可能通过不同的作用提高了非晶态合金的热稳定性.     

Chemical environment of copper at the surface of a CuAl2 model alloy: XPS,MEIS and TEM analyses

Air‐formed oxide on a CuAl₂ model alloy is shown to be free of copper species, with copper enriching in the alloy. With thickening of the oxide by anodizing, copper enriches further to a critical concentration at which its oxidation proceeds with incorporation of Cu(II) species into the film. Such species migrate more rapidly through the film than aluminium species. Incorporation of copper species is associated with generation of oxygen gas within the film and subsequent film rupture is due to release of the gas. Reduction of Cu(II) to Cu(I) species during XPS analysis is characterized and the accelerating role of charge neutralizing is highlighted. Copyright © 2004 John Wiley & Sons, Ltd.     

富镧混合稀土对ZL101A合金组织和机械性能的影响

研究了富镧混合稀土对ＺＬ１０１Ａ合金的铸态、固溶态、Ｔ６状态、重熔态的组织和机械性能的影响，提出了混合稀土中入量低压铸造整体车轮合理的热处理状态。     

Formation of Bi-Sb, Bi-Sn, and Bi-Sb-Sn Nanoclusters in Silica Xerogel Matrices from Mixed-Metal Oxide Precursors

Homogeneous mixed-metal oxides of the general formula (Bi/E/Si)O _x , where E represents a dopant element (E=Sb, Sn, or Sb/Sn), can be prepared using typical sol-gel processing techniques. Reduction of the in-situ Bi(III) and E ions by hydrogen affords nanocomposites of Bi-Sb, Bi-Sn, or Bi-Sb-Sn widely dispersed throughout the silica xerogel matrix. The materials prepared have high Bi-E metal loading of 52–60 wt. % containing Bi-E alloy nanoclusters of 12–15 nm average diameter. These results demonstrate a convenient method for the production of practical quantities of nanostructured bismuth alloy ceramic composites at high metal content.     

锆系Laves相储氢合金电极的性能研究

Ｚｒ（Ｖ０．２Ｍｎ０．２Ｍｏ０．０６Ｎｉ０．５４）２．４合金经ＨＦ溶液处理后，合金表面由富Ｚｒ和富Ｍｎ层转变成富Ｎｉ层，从而使电极初期活化周期明显缩短，电极表面氢吸附性能改善。表面反应电阻减小。本文探讨了上述电极表面反应机理，即表面Ｎｉ的催化、氢吸附和氢转移机理，对阻抗谱进行拟合，给出了相应的电极反应等效电路。