Study of the spontaneous formation of organic layers on carbon and metal surfaces from diazonium salts

This study investigates the spontaneous grafting of different para-substituted phenyl groups on carbon and metallic surfaces from diazonium salts solutions. Glassy carbon, nickel, zinc and iron plates were allowed to react with an acetonitrile solution of aryldiazonium tetrafluoroborate salt by simple dipping. The surfaces were characterized before and after their immersion by XPS and AFM to evidence the formation of a coating on the different materials. The results are indicative of the presence of substituted phenyl groups on all the investigated surfaces. This study also aims at correlating grafting efficiency with metal reactivities and diazonium salt electronic properties by means of AFM and FT-IRRAS. For this purpose, zinc and nickel were chosen due to their opposite reducing properties and two diazonium salts were selected with electron-donor or -withdrawing para-substituents. The results tend to indicate that redox properties of both partners (diazonium + metal) are of prime importance for grafting to occur.     

Assessment of thermal expansion coefficient of methylsilsesquioxane thin film

For the methylsilsesquioxane film whose optical birefringence is almost zero, it was recently reported that its vertical thermal expansion coefficient (CTE) was approximately one order of magnitude larger than the lateral CTE. Though the birefringence is not an absolute predictor of anisotropic behavior, the discrepancy in both the CTEs was so remarkable that it was essential to investigate whether the anisotropy was intrinsic property or not. If the effect of Poisson's ratio is considered in the calculation of the vertical CTE and when elastic modulus measured by surface acoustic wave spectroscopy is used in the assessment of the lateral CTE, both the CTEs are coincident with each other. Therefore, it can be concluded that the discrepancy in the CTEs can be attributed to a higher in‐plane polymer chain orientation but it can also arise from the misleadingly assumed modulus and Poisson's ratio. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 3109–3120, 2006     

溶胶-凝胶VO2薄膜转换特性研究

利用溶胶凝胶法在SiO2Si衬底上沉积高取向的V2O5薄膜,在压强低于2Pa,温度高于400℃的条件下,对V2O5薄膜进行真空烘烤,获得了电阻率变化3个数量级以上、弛豫宽度为62℃的VO2多晶薄膜.以X射线衍射(XRD)、扫描电子显微镜(SEM)图和电阻率转换特性等实验结果为依据,详细分析了溶胶凝胶薄膜在真空烘烤时从V2O5向VO2的转化,它经历了从VnO2n+1(n=2,3,4,6)到VO2的过程.实验证明,根据选择合适的成膜热处理条件和真空烘烤条件是实现溶胶凝胶V2O5结构向VO2结构成功转换的关键 关键词： 溶胶-凝胶法 氧化钒薄膜 VO2膜转换特性     

厚胶光刻非线性畸变的校正

利用厚胶光刻技术制作大深度微结构元件是一种有效的途径,但厚胶光刻过程中的非线性畸变对光刻面形质量的严重影响限制了该技术的应用,基于此,提出了一种对掩模透射率函数进行校正的方法。分析空间像形成及其在光刻胶内传递、曝光、显影等过程中非线性因素的影响,利用模拟退火算法对掩模透射率函数进行校正,以提高光刻面形质量,并以凹面柱透镜为例,给出了校正前后的显影轮廓模拟结果,其校正后浮雕面形的体积偏差仅为2.63%。该方法在有效改善面形质量的同时,并没有引起掩模的设计、制作难度及费用增加,这对于设计、制作高质量的微结构元件有重要意义。     

Photo-Absorption and photochemical decomposition of copper and alkaline-earth ß-diketonates as source gases of high-Tc superconducting films

For low-temperature deposition of oxide films relating to Bi-Sr-Ca-Cu-O superconductors, photo-absorption and -decomposition properties were examined with respect to copper and alkaline-earth ß-diketonates. It was confirmed that all ß-diketonates examined were promising as source materials for photochemical vapour deposition (photo-CVD) using a low-pressure mercury lamp, in view of their large light absorption coefficients at wavelength 254 nm. The light irradiation was effective for the formation of highly crystalline oxide films at temperatures below 600 °C. By combining two sources, Ca₂CuO₃ and SrCuO₂ films were prepared. Photo-CVD of c-axis oriented Bi₂Sr₂CuO_x film was achieved by the irradiation of ternary sources of Bi(C₆H₅)₃ and strontium and copper ß-diketonates at 500 °C.     

高温超导薄膜微波非线性研究的进展

文章介绍了高温超导薄膜微波非线性的主要特征，阐述了高温超导薄膜微波非线性产生的原因和相关的研究现状，指出了高温超导薄膜非线性研究中遇到的困难和尚未解决的问题．     

气相传输平衡法在(11-20)面蓝宝石上制备γ铝酸锂膜

为了寻找可能替代蓝宝石作为氮化镓外延的新型衬底,通过48 h的气相传输平衡,分别在1000℃、1030℃、1050℃、1070℃和1100℃制备了一层单相多晶的γ铝酸锂膜。X射线衍射和扫描电镜分别用于表征膜的物相、取向和表面形貌。结果显示,γ铝酸锂择优取向的好坏取决于气相平衡传输温度,在1050℃制备的γ铝酸锂具有高度的[100]择优取向;在γ铝酸锂(001)面上的双轴拉应力可能有助于[100]择优取向的形成;γ铝酸锂晶粒表面裂纹的方向一致性与其择优取向紧密相关。上述结果表明在合适的工艺条件下,气相传输平衡法制备的γ铝酸锂/蓝宝石可能成为一种很有前景且适合(1-100)面氮化镓生长的复合衬底。     

含氰基的酚醛树脂及其碳纤维复合材料

含氰基的酚醛树脂，具有优异的耐高温性能和高温下的机械强度，在３１５℃下性能变化甚小；不着火，发烟量低，有良好的加工成型性能。热固化过程中氰基成三嗪环而交联，没有小分子脱出，是一类具有广泛发展前景的新型热固性树脂。     

Carbon–epoxy composites based on fibers coated with nylon 6,6: hygrothermal ageing versus interlaminar shear strength

Carbon fibers were coated in situ with a thin film of polyhexamethylene adipamide by an interfacial polycondensation technique. The modified fibers were used for the preparation of epoxy-based unidirectional composites. Specimens of these materials were immersed in water until equilibrium conditions were attained. The weight gain at equilibrium was determined as a function of the immersion temperature, the fiber volume fraction and the polyamide content deposited on the fibers. Water penetration in specimens made with uncoated carbon fibers increases when the volume fraction decreases. Introduction of the polyamide interlayer initially increases the water absorption, but reduces it at higher immersion temperatures and/or higher polyamide contents. The treated specimens were subjected to the short beam test to determine the interlaminar shear strength (ILSS). The data show that the ILSS decreases with water penetration but increases when the immersion temperature increases from 40 to 70°C. The overall performance encountered is discussed in terms of the possible roles of the polyamide interphase while taking into account mechanisms concerned with matrix plasticization, interphase degradation and residual stress relaxation.     

A STUDY OF J-INTEGRAL OF THE ORTHOTROPIC COMPOSITE MATERIAL

ＡＳＴＵＤＹＯＦＪ－ＩＮＴＥＧＲＡＬＯＦＴＨＥＯＲＴＨＯＴＲＯＰＩＣＣＯＭＰＯＳＩＴＥＭＡＴＥＲＩＡＬＷａｎｇＡｉ－ｑｉｎ（王蔼勤）；ＦｅｎｇＢａｏ－ｌｉａｎ（冯宝莲）；ＹａｎｇＷｅｉ－ｙａｎｇ（杨维阳）（ＴａｉｙｕａｎＨｅａｖｙＭａｃｈｉｎｅｒｙ．...