Highly dispersed palladium nanoclusters incorporated in amino‐functionalized silica spheres for the selective hydrogenation of succinic acid to γ‐butyrolactone

Highly dispersed palladium nanoclusters incorporated on amino‐functionalized silica sphere surfaces (Pd/SiO₂‐NH₂) were fabricated by a simple one‐pot synthesis utilizing 3‐(2‐aminoethylamino)propyltrimethoxysilane (AAPTS) as coordinating agent. Uniform palladium nanoclusters with an average size of 1.1 nm can be obtained during the co‐condensation of tetraethyl orthosilicate and AAPTS owing to the strong interaction between palladium species and amino groups in AAPTS. The palladium particle size can be controlled by addition of AAPTS and plays a significant role in the catalytic performance. The Pd/SiO₂‐NH₂ catalyst exhibits high catalytic activity for succinic acid hydrogenation with 100% conversion and 94% selectivity towards γ‐butyrolactone using 1,4‐dioxane as solvent at 240°C and 60 bar for 4 h. Moreover, the Pd/SiO₂‐NH₂ catalyst is robust and readily reusable without loss of its catalytic activity. Copyright © 2015 John Wiley & Sons, Ltd.     

Microstructural stability and age-hardening behavior of Re-added dual two-phase Ni3Al and Ni3V intermetallic alloys

The effect of Re addition on the microstructure and hardening behaviour of the dual two-phase Ni₃Al (L1₂) and Ni₃V (D0₂₂) intermetallic alloy was investigated by scanning electron microscopy, transmission electron microscopy and Vickers hardness test. The two-phase eutectoid microstructure accompanying the Re-rich precipitates were observed in the channel region of the alloys in which Re substituted for Ni but not in those in which Re substituted for Al and V. The concomitant addition of Nb (or Ta) with Re more stabilized the two-phase eutectoid microstructure and consequently more induced the fine precipitates in the channel region. The annealing at temperatures below the eutectoid temperature was necessary to induce the fine precipitates in the channel region and thereby result in the precipitation hardening. The fine precipitation in the channel region and related hardening was attributed to the alloying feature so that Re is soluble in the A1 (fcc) phase at high temperatures and becomes less soluble in the two intermetallic phases decomposed from the A1 phase at low temperatures.     

Highly Luminescent Red Phosphorescent OLED with Interfacial Layers for Hole Transport and Electron Injection

Four kinds of red phosphorescent organic light-emitting devices were fabricated and compared to investigate the effect of interfacial layers for hole transport and electron injection. 1 nm-thick LiF in the device A and C and 1 nm-thick Cs₂CO₃ in the device B and D were deposited as an electron injection layer between the anode and the electron transport layer, and 5 nm-thick layer of dipyrazion[2,3-f:2′,2′-h]quinoxaline-2,3,6,7,10,11-hexacarbonitrile[HATCN] was inserted as a hole transport interfacial layer between the hole injection layer and the hole transport layer only in the device C and D. Under a luminance of 1000 cd/m², the power efficiencies were 7.6 lm/W and 8.5 lm/W in the device A and B, and 8.6 lm/W and 13.4 lm/W in the device C and D. The quantum efficiency of the device D was 15.8% under 1000 cd/m² which was somewhat lower than those of the device A and C, but a little higher than that of the device B. The luminance of the device D was much higher than those of the other devices at a given votage. The luminance of the device D at 7 V was 23,710 cd/m², which was 13.0, 3.4, and 4.0 times higher than those of the device A, B, and C at the same voltage, respectively.     

Surface passivation in n-type silicon and its application in silicon drift detector

Based on the surface passivation of n-type silicon in a silicon drift detector(SDD), we propose a new passivation structure of SiO2/Al2O3/SiO2 passivation stacks. Since the SiO2 formed by the nitric-acid-oxidation-of-silicon(NAOS)method has good compactness and simple process, the first layer film is formed by the NAOS method. The Al2O3 film is also introduced into the passivation stacks owing to exceptional advantages such as good interface characteristic and simple process. In addition, for requirements of thickness and deposition temperature, the third layer of the SiO2 film is deposited by plasma enhanced chemical vapor deposition(PECVD). The deposition of the SiO2 film by PECVD is a low-temperature process and has a high deposition rate, which causes little damage to the device and makes the SiO2 film very suitable for serving as the third passivation layer. The passivation approach of stacks can saturate dangling bonds at the interface between stacks and the silicon substrate, and provide positive charge to optimize the field passivation of the n-type substrate.The passivation method ultimately achieves a good combination of chemical and field passivations. Experimental results show that with the passivation structure of SiO2/Al2O3/SiO2, the final minority carrier lifetime reaches 5223 μs at injection of 5×10¹⁵ cm^-3. When it is applied to the passivation of SDD, the leakage current is reduced to the order of nA.     

Negative compressibility property in hinging open-cell Kelvin structure

A new three-dimensional(3 D) cellular model based on hinging open-cell Kelvin structure is proposed for its negative compressibility property. It is shown that this model has adjustable compressibility and does exhibit negative compressibility for some certain conformations. And further study shows that the images of compressibility are symmetrical about the certain lines, which indicates that the mechanical properties of the model in the three axial directions are interchangeable and the model itself has a certain geometric symmetry. A comparison of the Kelvin model with its anisotropic form with the dodecahedron model shows that the Kelvin model has stronger negative compressibility property in all three directions.Therefore, a new and potential method to improve negative compressibility property can be derived by selecting the system type with lower symmetry and increasing the number of geometric parameters.     

Surface of Ru/Fe2O3 catalysts used in water-gas shift reaction studied by auger electron spectrometry

Summary Carbon deposits on the surface ofRu/Fe₂O₃ catalysts used in the water-gas shift reaction have been investigated by Auger Electron Spectrometry. A correlation has been found between the thickness of the carbon deposit and the catalytic activity in WGSR. The carbon deposit covers the metallic active centers and blocks their contact with reagents. The dotting of the iron oxide support with sodium has been found to reduce the amount of carbon deposit. .      

双掺(Tm3+,Tb3+)LiYF4激光器1.5 μm波长激光阈值分析

由速率方程推出了双掺（Tm^3 ,Tb^3 ）离子准四能级系统的激光阈值解析式，讨论了Tm^3 和Tb^3 离子之间的相互作用。分析了1.5μm波长附近的激光阈值和Tm^3 、Tb^3 离子的掺杂原子数分数及晶体长度的关系。结果表明，对于对应Tm^3 离子^3H4→^3F4跃迁的约1.5μm波长的激光，激活离子Tm^3 的掺杂原子数分数过大时，交叉弛豫作用将使系统阈值迅速增加。Tb^3 离子的加入，一方面能抽空激光下能级，起到降低阈值的作用；另一方面亦减少了激光上能级的寿命，使阈值升高。故Tb^3 离子有最佳掺杂原子数分数。对于Tm原子数分数为y=0.01的Tm:LiYF4晶体，Tb^3 离子的最佳掺杂原子数分数为0.002左右，同时表明，激光阈值与晶体长度有关。最佳晶体长度与Tm^3 、Tb^3 离子的掺杂原子数分数以及晶体的衍射损耗和吸收损耗有关。     

Diastereoselective Alkylation of (Diene-Aldehyde)Fe(CO)3 Complexes with Functionalized Zinc-Copper Reagents NuCu(CN)Znl

Addition of functionalized zinc-copper reagents to the title complexes proceeds in a highly diastereoselective fashion to afford dienol complexes. The relative configurations of adducts 3d were determined by single X-ray diffraction analysis.     

用短谐振腔结构优化THz电磁波参量振荡器的输出特性

以MgO：LiNbO₃为非线性光学介质，通过采用一种高性能腔反射镜实现了一种85mm短腔长的法布里-珀罗式的光学参量振荡器，产生THz电磁波的实验结果.这种短腔长THz参量振荡器比传统的160mm腔长的振荡阈值降低了22.3％；峰值能量提高了170％；频率调谐范围从0.5—2.4THz提高到0.8—3.1THz.还报道了一种基于平面金属丝网的法布里-珀罗干涉仪测量THz波线宽的实验结果. 关键词： THz电磁波 OPO 非线性光学 3')" href="#">LiNbO₃     

Ag+掺杂的立方相Y2O3:Eu纳米晶体粉末发光强度研究

采用化学自燃烧法制备了不同Ag⁺掺杂浓度的Y₂O₃:Eu纳米晶体粉末样品(［Y³⁺］∶［Eu³⁺］∶［Ag⁺］=99∶1∶X，X=0—3.5×10^-2)，以及通过退火处理得到了相应的体材料.根据X射线衍射谱确定所得纳米和体材料样品均为纯立方相.实验表明在纳米尺寸样品中随着Ag离子浓度的增加，荧光发射强度随之增加，当X=2×10^-2时达到最大值，其发光强度比X=0时提高了近50%.当Ag离子浓度继续增加，样品发光强度保持不变.在相应的体材料样品中则没有观察到此现象.通过对各样品的发射光谱，激发光谱，X射线衍射图谱，透射电镜(TEM)照片和荧光衰减曲线的研究，分析了引起纳米样品荧光强度变化的原因是由于Ag离子与表面悬键氧结合，从而使这一无辐射通道阻断，使发光中心Eu³⁺的量子效率提高；Ag⁺的引入所带来的另一个效应是使激发更为有效.这两方面原因使发光效率得到了提高.