本文对ICP－AES法测定合金钢及镍基合金中的钨进行了系统的研究。试验表明，钨400.875纳米不受钼400.867纳米线干扰，亦无其它光谱干扰，测量范围在0.2-2%时相对标准偏差不大于3.7%，准确度较好。经过对不同基体及不同组分标钢的测定，有13种标钢能够很好共线，证明钨的测定非光谱干扰基本可忽略不计。本方法化学处理简单，不需分离掩蔽等手段可直接测定。     

氧化硅气凝胶的超临界制备及纳米结构

简要介绍了用溶胶－凝胶法制备新型功能材料氧化硅气凝胶的方法，着重阐述了氧化硅气凝胶的各种干燥过程对其纳米结构的影响，说明了超临界干燥工艺在保持气凝胶的纳米多孔结构方面的突出重要地位，同时，用比表面积测量，扫描电镜，小角Ｘ射线菜射等研究了这种轻质纳米多孔非晶固态材料的结构特性，介绍了这种材料的应用前景。     

纳米硅薄膜光吸收谱的研究

用恒定光电导法测量了纳米硅(其晶粒尺寸为3-5nm,晶态成分比X_c为45％—50％)薄膜在0.9—2.5eV范围的光吸收谱。分析了在不同光子能量范围可能存在的对光电导作主要贡献的几种光跃迁过程,以及随着X_c的增加,材料由非晶、微晶转变为纳米硅薄膜时光吸收谱的变化。发现纳米硅晶粒之间的界面区(平均厚度约为1nm)中载流子的跃迁及传输过程对整个范围的光吸收谱起主导作用。联系纳米硅的这种特殊结构解释了有关实验结果。 关键词：     

EXAFS研究负载型Ni／SiO2的区域结构

实验结果表明改进的实验室ＥＸＡＦＳ谱仪测试Ｎｉ箔的Ｋ吸收得到的ＥＸＡＦＳ谱与同步辐射上测量Ｎｉ箔得到的ＥＸＡＦＳ谱相近，利用实验室ＥＸＡＦＳ方法也可开展较好的结果测量研究，在ＳｉＯ２粉末载体上Ｎｉ负载量变化的ＥＸＡＦＳ结果表明，随着Ｎｉ负载量的降低，Ｎｉ的径向结构函数主配位峰的位置Ｒ＝０．２２０ｎｍ保持不变，但振幅强度逐渐降低。负载量从Ｎｉ箔到２．５％Ｎｉ／ＳｉＯ２，无序度因子σ由０．００６８ｎｍ     

Structural Phase Transformations of ZnS Nanocrystalline Under High Pressure

In-situ energy dispersive x-ray diffraction on ZnS nanocrystalline was carried out under high pressure by using a diamond anvil cell. Phase transition of wurtzite of 10nm ZnS to rocksalt occurred at 16.0GPa, which was higher than that of the bulk materials. The structures of ZnS nanocrystalline at different pressures were built by using materials studio and the bulk modulus, and the pressure derivative of ZnS nanocrystalline were derived by fitting the equation of Birch-Murnaghan. The resulting modulus was higher than that of the corresponding bulk material, which indicates that the nanomaterial has higher hardness than its bulk materials.     

Preparation and Optical Properties of SnO2／SiO2 Nanocomposite

SnO2/SiO2 nanocomposites have been prepared by the soaking-thermal-decomposing method, tin oxide nanoparticles are uniformly dispersed in the mesopores of silica. The optical absorption edge of the obtained nanocomposite presents a redshift compared with bulk tin oxide, With the increasing annealing temperature during the procedure of the sample preparation, the optical absorption edge of the sample moves to shorter wavelength (blueshift). These optical properties can be ascribed to the amorphous structure and band defects of surface layers of the tin oxide nanoparticles.     

纳米WO3的制备及其光解水析氧性能研究

用溶胶凝胶法,灼烧法合成了纳米级WO3,采用X-射线衍射、紫外可见漫反射光谱对WO3进行表征.在Fe3 为电子受体、溶液酸度pH为2.0情况下,研究了纳米级WO3在365nm紫外辐射下光解水析氧的光催化活性,并讨论了不同方法制备的催化剂活性差异的原因.结果表明,结晶程度越高、尺寸越小、比表面积越大的纳米级WO3具有更高的光分解水析氧活性,电子受体的浓度、溶液的酸度对析氧活性有明显的影响.