高铁酸盐在SnO2-Sb2O3/Ti电极上的选择性电化学合成

合成了SnO2-Sb2O3/Ti电极材料.实验结果证实,在14mol/LNaOH水溶液中和完全避免析氧反应的条件下,Fe(Ⅱ)物种在该电极上进行电化学氧化并生成FeO42-.结果表明,Fe(OH)3在浓NaOH溶液中发生酸式电离,形成可溶于水的FeO2-,该离子的浓度随着碱溶液浓度变化而发生明显变化,而且它还是发生化学氧化和电化学氧化的反应物.在SnO2-Sb2O3/Ti电极上,FeO42-的电化学还原起始电位为0.38V(vs.Hg/HgO,14mol/LNaOH),FeO2-电化学氧化起始电位为0.54V.结果还表明,用电化学方法氧化Fe(Ⅱ)物种生成FeO42-是个多步骤过程.     

纳米级碳导电剂的种类对licoo2电化学性能的影响

碳纳米管;锂离子电池;正极;倍率容量;导电剂     

PREPARATION AND ELECTROCHEMICAL CHARACTERISTICS OF POLYMER ELECTROLYTE MEMBRANES BASED ON SAN/PVDF-HFP BLENDS

A copolymer of poly(acrylonitrile-co-styrene) (SAN) was synthesized via an emulsion polymerization method. Novel polymer electrolyte membranes cast from the blends of poly(vinylidene fluoride-co-hexafluoropropylene) (PVDF-HFP), SAN and fumed silica (SiO2) are microporous and can be used in polymer lithium-ion batteries. The membrane shows excellent characteristics such as high ionic conductivity and good mechanical strength when the mass ratio between SAN and PVDF-HFP and SiO2 is 3.5/31.5/5. The ionic conductivity of the membrane soaked in a liquid electrolyte of 1 mol/L LiPF6/EC/DMC/DEC is 4.9×10-3 S cm-1 at 25℃. The membrane is electrochemical stable up to 5.5 V versus Li /Li in the liquid electrolyte. The influences of SiO2 content on the porosity and mechanical strength of the membranes were studied. Polymer lithium-ion batteries based on the membranes were assembled and their performances were also studied.     

包覆Y(OH)3的球形Ni(OH)2的电化学性能

利用软嵌式粉末电极技术研究了Y(OH)3包覆对球形Ni(OH)2电化学性能的影响. 循环伏安结果表明, 在球形Ni(OH)2的氧化过程中存在Ni(Ⅲ)和Ni(Ⅳ)的两步氧化反应, 产生的Ni(Ⅳ)不稳定, 能分解产生NiOOH和氧气, 所以可将Ni(Ⅲ)→Ni(Ⅳ)看作副反应. Y(OH)3包覆层对Ni(OH)2氧化过程后期的副反应, 特别是Ni(Ⅲ)→Ni(Ⅳ)具有较好的抑制作用. 由包覆后的Ni(OH)2制成的模拟电池表现出很好的高温性能, 在1C充放电条件下, 当Y的摩尔分数为1.61%时, 在60 ℃时所对应的容量保持率可达到25 ℃的92.7％; 当Y的摩尔分数仅为0.55 %时, 在60 ℃时所对应的质量比容量也可达到241.3 mA·h/g.     

水相锌二次电池正极材料V2O5/C的电化学性能研究

采用溶胶－凝胶法合成了一种V₂O₅/C复合材料.扫描电镜（SEM）和红外光谱（FTIR）分析表明,这是一种外层V₂O₅胶体包覆内层乙炔分子的多孔复合材料.以V₂O₅/C作正极,锌片为负极,Zn(ClO₄)₂溶液为电解质组成水相锌二次电池,采用循环伏安（CV）和电化学阻抗谱（EIS）等方法研究发现:V₂O₅:C质量比为1:1时电极具有最好的电化学性能,电池开路电压达1.64 V; Zn^2＋能分别在1.01 V和1.26 V处分步嵌入V₂O₅/C结构中A、B两种位置,其嵌入电流密度峰值最高可达70 mA•g^－1,并且具有较好的循环充放电性能;在一定放电深度下,V₂O₅/C电极反应速率受Zn^2＋的扩散过程控制.     

锂离子电池正极材料LiMn2O4的合成与晶体结构（英）

Spinel LiMn₂O₄ powders were prepared using two-step synthesis method consisting of solid-state reaction method and citrate modified sol-gel method. The effects of the calcination temperature and the Li/Mn ratio of raw materials were studied on the physicochemical and electrochemical properties of the spinel LiMn₂O₄ powders, such as crystallinity, lattice constant and density. The title compound was characterized by powder X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Polycrystalline LiMn₂O₄ powers calcined at 750 ℃ were found to be composed of very uniformly-sized microcrystal with an average particle size of 300 nm. The improvement in electrochemical properties was mainly attributed to the process of re-grinding by absolute alcohol.     

吸热碳氢燃料裂解镧改性混合型催化剂的研究

制备了吸热型碳氢燃料NNJ-150和镧离子交换改性的USY、ZSM-5分子重申及混合分子筛，考察了NNJ-150在USHY、HZSM-5和两者混合物以及镧改性单分子筛和混合分子筛催化剂上的裂解反应。结果表明，ZSM-5分子筛中添加镧，对NNJ-150的单分子裂解反应有明显影响；混合分子两种分子筛之间存在协同作用，低温（500℃）下，LaUSY LaZSM-5（75：25）混合分子筛对低碳烯烃的选择性较高（41.48％），催化剂寿命较长（35min以上），能有效提高吸热型碳氢燃料NNJ-150的吸热能效。     

锂离子电池杂论

首先论述了锂离子电池的大好形势，难得的机遇和面临的挑战。 欧盟相继出台了两项与化学品相关的法令，加之原材料上涨、我国出口退税政策调整，锂电池市场出现新的机遇。面对能源短缺和环保的严峻形势，对动力电池和储能电池的呼声日益高涨。     

LiFePO4基高功率锂离子电池

LiFePO4是近年来刚刚发展起来的一种新型锂离子电池正极材料，具有安全性能好、循环寿命长、环境友好、价格便宜等优点，被认为是最有前途的新一代锂离子电池正极材料，在动力电池和高功率电池等领域将有着广阔的应用前景，所以磷酸铁锂材料和电池已成为国内外电源界研究和开发的热点。     

喷气燃料的化学组成与理化性质的定量关系研究

利用GC/MS分析了80个喷气燃料样品的烃族化学组成,将其分为直链烃、异构烃、环烷烃、芳烃、十氢萘五大类,并测定了燃料的密度、苯胺点、热值、冰点、闪点及沸程等主要理化性质.构建了喷气燃料组成和性质关系的数据库,考察了喷气燃料的烃族组成及沸程对各种性质的影响.结合Cookson等的理论,建立了八个模型方程,通过多元线性回归预测烃族化学组成与理化性质关系, 与已报道的其他方程比较,新模型的相关系数明显提高.