镓(Ⅲ)-茜素氨羧络合剂在碳糊电极上的阳极吸附伏安法研究及应用

研究了镓(Ⅲ)-茜素氨羧络合剂(ALC)在碳糊电极上的阳极吸附伏安行为,并以此建立了一种高灵敏度、高选择性测定镓的吸附伏安法.在0.12 mol/L HAc-NaAc-0.24 mol/L邻苯二甲酸氢钾底液(pH 4.5)中,-0.10 V (vs.SCE) 富集90 s (或180 s),以250 mV/s扫速线性扫描至0.90 V, Ga3+-ALC在碳糊电极上产生灵敏的与ALC的峰电位相差近230 mV的吸附氧化峰,其二次导数峰电流与镓浓度在5.0×10-10～8.0×10-7 mol/L范围内呈线性关系;富集240 s检出限达3.0×10-10 mol/L(S/N=3).探讨了电极反应机理.该法用于粮食样品中镓的测定,结果满意.     

吡啶-2-甲酸镍的合成及其晶体结构

以吡啶 2 甲酸和Ni(ClO4)2·6H2O为原料反应制得配合物[Ni(C5H4NCOO)2(H2O)2]2H2O,并通过X 射线衍射法测定其晶体结构.该化合物属于单斜晶系,空间群P21/n,晶胞参数:a=0.97351(15)nm,b=0.52254(8)nm,c=1.4483(2)nm,β=90.119(3)°,V=0.7367(2)nm3,Z=2,Dc=1.690g/cm3,μ=1.362mm 1,F(000)=388,结构偏离因子R1=0.0316,wR2=0.0902,共收集到4771个强度数据,其中1700个独立衍射点,1489个(I>2σ(I))可观测点.X 射线分析表明晶体是由分子间氢键和π π弱相互作用堆积而成的二维层状结构.     

钛硅分子筛的结构表征及催化性能研究

以ＴＰＡＢｒ为模板剂，氨水等为碱源合成了钛硅分子筛ＴＳ－１，并利用ＸＲＤ，ＩＲ，元素分析，ＵＶ－ＶＩＳ，热分析等手段对合成的分子筛进行了表征，通过丙烯环氧化反应合成的ＴＳ－１催化性能。结果结果，ＴＳ－１凝胶与产品的硅钛与基本一致；随着硅钛比的降低，ＴＳ－１由单斜晶系过渡为正交晶系，在硅钛比为１２９－１６．７的范围内，随着进入骨架的钛量增加，单胞体积增大；     

微波辅助快速制备2D/1D ZnIn2S4/TiO2 S型异质结及其光催化制氢性能

The threat and global concern of energy crises have significantly increased over the last two decades. Because solar light and water are abundant on earth, photocatalytic hydrogen evolution through water splitting has been considered as a promising route to produce green energy. Therefore, semiconductor photocatalysts play a key role in transforming sunlight and water to hydrogen energy. To date, various photocatalysts have been studied. Among them, TiO₂ has been extensively investigated because of its non-toxicity, high chemical stability, controllable morphology, and high photocatalytic activity. In particular, 1D TiO₂ nanofibers (NFs) have attracted increasing attention as effective photocatalysts because of their unique 1D electron transfer pathway, high adsorption capacity, and high photoinduced electron–hole pair transfer capability. However, TiO₂ NFs are considered as an inefficient photocatalyst for the hydrogen evolution reaction (HER) because of their disadvantages such as a large band gap (~3.2 eV) and fast recombination of photoinduced electron–hole pairs. Therefore, the development of a high-performance TiO₂ NF photocatalyst is required for efficient solar light conversion. In recent years, several strategies have been explored to improve the photocatalytic activity of TiO₂ NFs, including coupling with narrow-bandgap semiconductors (such as ZnIn₂S₄). Recently, microwave (MW)-assisted synthesis has been considered as an important strategy for the preparation of photocatalyst semiconductors because of its low cost, environment-friendliness, simplicity, and high reaction rate. Herein, to overcome the above-mentioned limiting properties of TiO₂ NFs, we report a 2D/1D ZnIn₂S₄/TiO₂ S-scheme heterojunction synthesized through a microwave (MW)-assisted process. Herein, the 2D/1D ZnIn₂S₄/TiO₂ S-scheme heterojunction was constructed rapidly by using in situ 2D ZnIn₂S₄nanosheets decorated on 1D TiO₂ NFs. The loading of ZnIn₂S₄ nanoplates on the TiO₂ NFs could be easily controlled by adjusting the molar ratios of ZnIn₂S₄ precursors to TiO₂ NFs. The photocatalytic activity of the as-prepared samples for water splitting under simulated solar light irradiation was assessed. The experimental results showed that the photocatalytic performance of the ZnIn₂S₄/TiO₂ composites was significantly improved, and the obtained ZnIn₂S₄/TiO₂ composites showed increased optical absorption. Under optimal conditions, the highest HER rate of the ZT-0.5 (molar ratio of ZnIn₂S₄/TiO₂= 0.5) sample was 8774 μmol·g^-1·h^-1, which is considerably higher than those of pure TiO₂ NFs (3312 μmol·g^-1·h^-1) and ZnIn₂S₄nanoplates (3114 μmol·g^-1·h^-1) by factors of 2.7 and 2.8, respectively. Based on the experimental data and Mott-Schottky analysis, a possible mechanism for the formation of the S-scheme heterojunction between ZnIn₂S₄ and TiO₂ was proposed to interpret the enhanced HER activity of the ZnIn₂S₄/TiO₂heterojunctionphotocatalysts.      

双-单齿芳香酰胺型配体桥联La3＋一维配位聚合物的合成与晶体结构

通过硝酸镧和双-单齿芳香酰胺型配体L {L＝1,4-双[(2'-苄胺甲酰基苯氧基)-甲基]苯}之间的反应得到了配位聚合物{[La(NO₃)₃]₂•L₃}_n, 并用X射线单晶衍射测定了配合物的晶体结构. 配合物为三斜晶系, _P1空间群, 晶胞参数a＝1.1298(2) nm, b＝1.2689(1) nm, c＝2.1030(3) nm, α＝81.189(9)°, β＝80.95(1)°, γ＝65.832(9)°, V＝2.7032(6) nm³, Z＝2, R＝0.0267, wR＝0.0679, La^3＋为9配位, 呈变形的三帽三角棱柱配位构型. 配合物通过配体的桥联作用形成一维环链相间的配位聚合结构, 由于相邻链间不存在氢键和π-π堆积作用, 所以配合物是以单链形式堆积排列.     

FFC-1离子交换纤维物理化学性能的研究

利用扫描电镜、热失重-红外、元素分析、低温氮吸附等技术和化学手段对聚羧酸基FFC-1离子交换纤维的结构与性能特点等进行了系统研究．结果表明：FFC-1离子交换纤维为含适量酰肼类交联键的聚羧酸(钠)型离子交换材料，外比表面积大和传质距离短是其反应动力学性能优异的主要原因，FFC-1纤维具有良好的化学与热稳定性。在5mol/L硫酸、硝酸、盐酸和2mol／L氢氧化钠溶液中浸泡，交换容量未见明显降低。但过氧化氢溶液对其功能基有明显破坏，CO2为FFC-1纤维在高温区间(300℃～350℃)的主要分解产物。     

溶胶-凝胶法制备还原态K-Co-Mo催化剂的合成醇性能

应用溶胶-凝胶法制备了还原态K-Co-Mo催化剂, 比较了不同的组分和不同的反应条件对合成醇性能的影响。实验结果表明，适量钾和钴助剂的添加能显著提高催化剂合成醇的性能，尤其是提高了C2+醇的选择性。此外，反应温度、压力以及空速对合成醇影响明显，升高温度可以提高催化反应中低碳醇的收率，但选择性下降；增加压力和空速可以提高低碳醇的收率和选择性，对合成低碳醇有利。在230 ℃，6.0 MPa，14 400 h－1条件下，催化剂合成低碳醇的收率为375.4 g/kg·h，选择性为70.2%，C1OH/C2+OH为0.48。     

正负离子表面活性剂在短链脂肪醇/水中沉淀-囊泡转化和双水相的形成

首次报道在短链脂肪醇/水溶剂中十二烷基硫酸钠和辛基三甲基溴化铵混合体系由沉淀转化为囊泡，并出现表面活性剂双水相的新现象，以期探索正负离子表面活性剂混合体系研究的新途径。     

芥子气模拟剂2-氯乙基乙基硫醚的光催化降解

利用连续流动微反、原位红外和GC/MS等手段考察了芥子气模拟剂2-氯乙基乙基硫醚（2-CEES）在P25 TiO2上的光催化降解反应,证实CO2和H2O是这个反应的最终产物.详细的跟踪分析表明,除了CO2和H2O外,在反应的气相混合物中可检测到C2H4、CH3CHO、CH4、CO、HCl和H2S；少量小分子的羧酸、醚和砜；微量C2H5SC2H5、C2H5S2C2H5、C2H5SC2H4Cl和CH2ClCH2Cl等中间产物;在反应后的催化剂表面可检测到C2H5S2C2H5、C2H5SC2H4OH、C4H9S2C2H5和C2H5S2C2H4OH、等物.根据这些结果提出了2-CEES光催化降解的反应机理,推断2-CEES的光催化降解涉及脱氯、C－S键断裂、有机硫化物光聚合和裂解等复杂过程最终转化为CO2和H2O.认为各种硫物种在表面的积聚引起了催化剂的缓慢失活.     

配位聚合物{[Co2(HBTC)2(H2O)6]·C4H10N2·2H2O}n的水热合成、结构表征及荧光性质

采用水热法合成了配位聚合物[Co2(HBTC)2(H2O)6]·C4H10N2·2H2O}n(H3BTC为1,3,5-均苯三羧酸,C4H10N2为哌嗪),通过X射线单晶衍射、红外光谱和荧光光谱进行表征,并用TGA研究了该配位聚合物的热稳定性.晶体属三斜晶系,P1空间群,a=1.05437(9)nm,b=1.05485(9)nm,c=0.71482(5)nm,α=102.4623(28)°,β=91.3500(42)°,γ=111.0186(29)°,V=0.72018(10)nm3,Mr=764.37,Dc=1.762g·cm-3,Z=1,μ(MoKα)=1.25mm-1,F(000)=394,R=0.0307,wR=0.0815.晶体的基本构建单元中包含2个Co()中心、2个配位的HBTC分子和6个配位的水分子.基本构建单元通过相互链接形成具有“Z”型结构的一维配位聚合链,链间通过两种不同的氢键(O—H…O和N—H…O)相互作用,进而形成具有三维骨架结构的微孔晶体,微孔大小为0.71nm×0.82nm.荧光光谱表明,常温下用λex=312nm的光激发后,配位聚合物在329nm处出现强烈的荧光发射.