Fluorinated Copolymer-Oxide Hybrids

A fluorinated copolymer/metal oxide hybrid is fabricated by refluxing a high hydroxyl content fluorinated copolymer with tetraethoxysilane. The resulting organic-inorganic hybrids are transparent throughout the entire compositional range if processed with HCl as a catalyst. They exhibit a continuous variation in hardness, hydrophobicity, and abrasion resistance, intermediary between the properties of the pure polymer and that of a silica gel. The catalyst has a strong influence over the microstructure of the hybrid. ²⁹Si MAS-NMR indicates the presence of highly condensed silica clusters within the structure of the hybrid. If a Nd(III) alkoxide is used instead of TEOS, a Nd ³⁺-doped fluoropolymer is obtained. These results indicate that when a fluorinated copolymer contains groups amenable to hydrolysis and condensation, cross-linking with a metal alkoxide is possible, leading to an interesting families of hybrids.     

Wide‐angle X‐ray diffraction and differential scanning calorimetry study of the crystallization of poly(ethylene naphthalate), poly(butylene naphthalate), and their copolymers

The crystallization behavior of a series of poly(ethylene‐co‐butylene naphthalate) (PEBN) random copolymers was studied. Wide‐angle X‐ray diffraction (WAXD) patterns showed that the crystallization of these copolymers could occur over the entire range of compositions. This resulted in the formation of poly(ethylene naphthalate) or poly(butylene naphthalate) crystals, depending on the composition of the copolymers. Sharp diffraction peaks were observed, except for 50/50 PEBN. Eutectic behavior was also observed. This showed isodimorphic cocrystallization of the PEBN copolymers. The variation of the enthalpy of fusion of the copolymers with the composition was estimated. The isothermal and nonisothermal crystallization kinetics were studied. The crystallization rates were found to decrease as the comonomer unit content increased. The tensile properties were also measured and were found to decrease as the butylene naphthalate content of the copolymers increased. For initially amorphous specimens, orientation was proved by WAXD patterns after drawing, but no crystalline reflections were observed. However, the fast crystallization of drawn specimens occurred when they were heated above the glass‐transition temperature. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 843–860, 2004     

Structure of a poly(2,5‐benzimidazole)/phosphoric acid complex

As‐cast films of poly(2,5‐benzimidazole) exhibit uniplanar orientation in which the planes of the aromatic rings lie parallel to the film surface. Upon doping with phosphoric acid, the original crystalline order is lost, but the doped film can be stretched to produce films with uniaxial orientation. After thermal annealing at 540 °C, nine Bragg reflections are resolved in the fiber diagram, and these are indexed by an orthorhombic unit cell with the dimensions a = 18.1 Å, b = 3.5 Å, and c = 11.4 Å, containing four monomer units of two chains. The absence of odd‐order 00l reflections points to a 2₁ chain conformation, which is probably planar so that the aromatic units can be stacked along the b axis. The water and phosphoric acid contents of the crystalline structure cannot be determined exactly because of the presence of extensive amorphous regions that probably have different solvation. The best agreement between the observed and calculated intensities is for an idealized structure containing two phosphoric acids and two water molecules per unit cell. However, the phosphoric acid is probably present mainly in the form of pyrophosphoric acid and its higher oligomers. In addition, the X‐ray data are consistent with a more disordered structure containing chains with random (up and down) polarity and a lack of c‐axis registry. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 2576–2585, 2004     

Bio‐based nanocomposites from functionalized plant oils and layered silicate

Some discovery work was done on the synthesis of clay nanocomposites based on renewable plant oils. Functionalized triglycerides, such as acrylated epoxidized soybean oil, maleinized acrylated epoxidized soybean oil, and soybean oil pentaerythritol maleates, combined with styrene were used as the polymer matrix. The miscibility of these monomers and clay organomodifier was assessed by solubility parameters. The formation of nanocomposites was confirmed by both X‐ray data and transmission electron microscopy. The morphology showed a mix of intercalated and partially exfoliated sheets. The flexural modulus increased 30% at only 4 vol % clay content, but there was no significant effect on flexural strength, glass‐transition temperature, and thermal stability. Property enhancement was related to the degree of exfoliation that depends on both the polarity and flexibility of the monomers. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 1441–1450, 2004     

Extractive spectrophotometric determination of Cobalt(II) in synthetic and pharmaceutical samples using Cyanex 923.

Cyanex 923 has been proposed as a sensitive analytical reagent for the direct extractive spectrophotometric determination of cobalt(II). Cobalt(II) forms a blue-colored complex with Cyanex 923 in the organic phase. The maximum absorbance of the complex is measured at 635 nm. Beer's law was obeyed in the range 58.9 - 589.0 microg of cobalt. The molar absorptivitiy and Sandell's sensitivity of the complex was calculated to be 6.79 x 10920 l mol(-1) cm(-1) and 0.088 microg cm(-2), respectively. The nature of the extracted species was found to be Co(SCN)2 x 2S. An excellent linearity with a correlation coefficient value of 0.999 was obtained for the Co(II)-Cyanex 923 complex. Stability and regeneration of the reagent (Cyanex 923) for reuse is the main advantage of the present method. The method was successfully applied to the determination of cobalt in synthetic mixtures and pharmaceutical samples was found to give values close to the actual ones. Standard alloy samples, such as high-speed tool BCS 484 and 485, have been tested for the determination of cobalt for the purpose of validating the present method. The results of the proposed method are comparable with atomic absorption spectrometry and were found to be in good agreement.     

Radioactive Tracer Study of the Displacement of Iodine Adatoms from Platinized Platinum Electrode by Carbon Monoxide

Radioactive tracer studies confirm the earlier electrochemical results that carbon monoxide can virtually completely displace iodine adatoms. For the first time, it is found that iodine adatoms are not displaced by carbon monoxide when iodide anions are adsorbed in the presence of an upd silver monolayer. The possible reasons for the effect observed are discussed.     

Two-Layered Poly-o-phenylenediamine/Polyaniline Composite: Electrosynthesis and Spectroelectrochemical Properties

Spectroelectrochemical properties of poly-o-phenylenediamine (PPD) and the synthesized composite of PPD and polyaniline—two chemically related polymers containing an amino-substituted benzene ring but having different conduction nature—are studied. The polyaniline synthesis on PPD-modified electrodes involves stages of the reaction initiation, the copolymer formation, and the formation of a polyaniline layer at the copolymer/solution interface.     

Adsorption of Kryptate Complexes of Alkali Metals in Electrolytes of Different Compositions and in the Presence of 1-Adamantanol

Data on the adsorption of kryptates of alkali metals on a mercury electrode are obtained for the first time by a method of the measurement of the differential capacitance as a function of potential and are compared to one another. Shown is that there takes place a deep mutual relationship between the structure of a complex and the regularities of its adsorption. An assumption is put forth about the possibility of adsorption of a free ligand in solutions of lithium kryptate, which possesses relatively low strength. The co-adsorption of sodium kryptate with 1-adamantanol, which forms a two-dimensional condensed layer, is investigated. Established is that the C vs. E curves, obtained in 1 M Na₂SO₄ at a constant activity of 1-adamantanol and a varying concentration of Kryptofix^R 222, exhibit two distinctly pronounced portions, each of which corresponds to predominant adsorption of one of the surface-active components. The region of predominant adsorption of Kryptofix^R 222 expands with its concentration.     

Some Aspects of the Implementation of Scaling Quantum Mechanical Molecular Force Fields

Some features of software implementation of the Pulay scaling procedure are considered. The advantages of the single value decomposition method for maintaining well-conditionality of the scale factor determination problem are demonstrated. The necessity of using a rational number of scale factors is shown. The possibility of obtaining transferable scale factors with the Pulay method and thus predict the vibrational spectra of related compounds is emphasized.     

Physicochemical and Acoustic Properties of Water-Based Magnetic Colloid

A velocity and absorption coefficient of sound for magnetic fluid (MF) based on water are studied in the frequency range of 12–132 MHz as a function of the concentration of dispersed phase, the uniform magnetic field, the storage time, and the temperature. The MF dispersed phase consist of magnetite Fe₃O₄ particles stabilized with sodium oleate. The parameters of sound propagation are measured within temperature interval 0–80°C. Densities of MF and sodium oleate are also measured as a function of temperature. Volume concentrations of magnetic fluid components (water, magnetite, and sodium oleate adsorbed on the surface of magnetic particles) are determined. Densities, heat capacities, coefficients of heat conductivity and thermal expansion of aggregates are estimated. Aggregate size distribution in the studied magnetic fluid is described by the log-normal function. Parameters characterizing the aggregate size distribution are determined and their interpretation is given.