成分和厚度的依赖

通过调整Mn的成分，系统地研究了Ni81Fe19/Ni100-xMnx双层膜的磁学性质，特别是交换偏置场(Hex)的变化.当Ni100-xMnx中Mn的原子百分比在534%到600%之间时，对于150nm的Ni81Fe19，得到了最大的交换偏置场175kA/m，同时由于Mn对Ni81Fe19层的扩散所造成的磁矩的降低小于20%；高角x射线衍射证明Ni100-xMnx的晶格常数随着Mn成分的改变而变化，Mn含量越多，其晶格常数越大；制备态Ni100-xMnx膜晶格常数与θ相NiMn膜晶格常数的接近程度与NiMn膜θ相形成的容易程度相对应.也研究了交换偏置场随着Ni１００-xMnx厚度的变化，第一次得到了当Ni100-xMnx中Mn的原子百分比为706%时，Ni81Fe19(150nm)/Ni100-xMnx(90nm)双层膜在经过240℃，5h退火后，可以有80kA/m的交换偏置场，此时铁磁层磁矩的大小几乎不变. 关键词： Ni81Fe19/Ni100-xMnx 交换偏置场     

Spectral Anomalies in the Fraunhofer Diffraction Pattern

We study the spectral characteristics theoretically and experimentally in the Fraunhofer diffraction pattern formed by the diffraction of a spatially coherent, polychromatic light through a slit. It is found that the spectrum in some diffraction directions close to the singular direction is redshifted, compared to the spectrum of the incident polychromatic light, and blueshifted in other directions, and splits into two lines at the singular direction. We show that the experimental results are consistent with the theoretical expectations.     

Two-Frequency Brillouin Fiber Laser Based on Bragg Grating Fabry-Perot Cavity

A novel and simple two-frequency Brillouin fiber laser is presented. It is based on a fiber Fabry-Perot cavity with fiber Bragg gratings as reflectors. The model of stimulated Brillouin scattering in fiber grating-based Fabry-Perot resonator is investigated. The laser allows conversion efficiency of close to 100% and suppresses the higher-order Stokes waves. The theoretical prediction is presented and the experimental demonstration is realized.     

穆斯堡尔谱法及其应用

文章简介了穆斯堡尔效应、穆斯堡尔谱的产生以及穆斯堡尔效应的应用 ,说明它不仅在理论上具有深刻的意义 ,又有着广泛的应用价值 .     

Intramolecular energy transferable (2,2‐diphenylvinyl)phenyl substituted poly(p‐phenylenevinylene) derivative with efficient photoluminescence and electroluminescence

A poly(p‐phenylenevinylene) (PPV) derivative containing a bulky (2,2‐diphenylvinyl)phenyl group in the side chain, EHDVP‐PPV, was synthesized by Gilch route. The reduced tolane‐bisbenzyl (TBB) defects, as well as the structure of the polymer, was confirmed by various spectroscopic methods. The intramolecular energy transfer from the (2,2‐diphenylvinyl)phenyl side group to the PPV backbone was studied by UV‐vis and photoluminescence (PL) of the obtained polymer and model compound. The polymer film showed maximum absorption and emission peaks at 454 and 546 nm, respectively, and high PL efficiency of 57%. A yellow electroluminescence (λ_max = 548 nm) was obtained with intensities of 6479 cd/m² when the light‐emitting diodes of ITO/PEDOT/EHDVP‐PPV/LiF/Al were fabricated. The maximum power efficiency of the devices was 0.729 lm/W with a turn‐on voltage of 3.6 V. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 5636–5646, 2004     

Proteins Entrapped in Silica Monoliths Prepared from Glyceroxysilanes

The preparation of discrete polyol based silane precursors derived from glycerol by a simple one-pot process is described. These polyol-based silanes could be hydrolyzed under mild pH conditions and upon gelation resulted in the formation of optically clear, monolithic, mesoporous silica. The hydrolysis and condensation reactions lead to cure rates that are very sensitive to ionic strength, but are almost unaffected by pH in contrast to those of alkoxysilanes derived from primary alcohols such as Si(OEt)₄. Residual glycerol in the silica monolith could be removed by washing, or could be left in the silica to reduce the magnitude of shrinkage during long term storage. The biocompatible glyceroxysilane precursors lead to materials that were able to retain the activity of entrapped enzymes over repeated cycles of use for periods of up to several months.     

Composite Silica Particles Using a Mixture of Organosilane Monomers

Composite silica particles were synthesized by a two-step (acid-base) process in an aqueous solution with a mixture of organoalkoxysilane monomers. The two-step process separates the hydrolysis and condensation procedures to easily control condensation rate. In this study, the silane monomers used were phenyltrimethoxysilane (PTMS), vinyltrimethoxysilane (VTMS), methyltrimethoxysilane (MTMS), and tetraethyl-orthosilicate (TEOS). The physical properties of the resultant composite particles were investigated with the change in the molar ratio of monomers. The size of the particles increased with increasing the molar ratio of R_aSi(OR)₃/R_bSi(OR)₃ or R_aSi(OR)₃/TEOS (R_a: phenyl; R_b: vinyl, methyl).     

Synthesis and characterization of well‐defined diblock and triblock copolymers of poly(N‐isopropylacrylamide) and poly(ethylene oxide)

Well‐defined diblock and triblock copolymers composed of poly(N‐isopropylacrylamide) (PNIPAM) and poly(ethylene oxide) (PEO) were successfully synthesized through the reversible addition–fragmentation chain transfer polymerization of N‐isopropylacrylamide (NIPAM) with PEO capped with one or two dithiobenzoyl groups as a macrotransfer agent. ¹H NMR, Fourier transform infrared, and gel permeation chromatography instruments were used to characterize the block copolymers obtained. The results showed that the diblock and triblock copolymers had well‐defined structures and narrow molecular weight distributions (weight‐average molecular weight/number‐average molecular weight < 1.2), and the molecular weight of the PNIPAM block in the diblock and triblock copolymers could be controlled by the initial molar ratio of NIPAM to dithiobenzoate‐terminated PEO and the NIPAM conversion. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 4873–4881, 2004     

Exploitation of introducing of catalytic centers into layer galleries of layered silicates and related epoxy nanocomposites. I. Epoxy nanocomposites derived from montmorillonite modified with catalytic surfactant‐bearing carboxyl groups

Montmorillonite (MMT) was modified with the acidified cocamidopropyl betaine (CAB) and the resulting organo‐montmorillonite (O‐MMT) was dispersed in an epoxy/methyl tetrahydrophthalic anhydride system to form epoxy nanocomposites. The intercalation and exfoliation behavior of the epoxy nanocomposites were examined by X‐ray diffraction and transmission electron microscopy. The curing behavior and thermal property were investigated by in situ Fourier transform infrared spectroscopy and DSC, respectively. The results showed that MMT could be highly intercalated by acidified CAB, and O‐MMT could be easily dispersed in epoxy resin to form intercalated/exfoliated epoxy nanocomposites. When the O‐MMT loading was lower than 8 phr (relative to 100 phr resin), exfoliated nanocomposites were achieved. The glass‐transition temperatures (T_g's) of the exfoliated nanocomposite were 20 °C higher than that of the neat resin. At higher O‐MMT loading, partial exfoliation was achieved, and those samples possessed moderately higher T_g's as compared with the neat resin. O‐MMT showed an obviously catalytic nature toward the curing of epoxy resin. The curing rate of the epoxy compound increased with O‐MMT loading. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 1192–1198, 2004     

Synthesis and characterization of soluble polyimides containing trifluoromethyl groups in their backbone

A series of polyimides were synthesized from 2,2‐Bis(3,4‐dicarboxyphenyl)hexafluoropropane, 2,2‐bis(3‐amino‐4‐hydroxyphenyl)‐hexafluoropropane, and 4,4′‐oxydianiline by chemical imidization. The effects of the diamine ratios on the properties of the films were evaluated through the study of their thermal, electrical, and morphological properties. All the polymers exhibited better solubility in most of the organic solvents and hence were easily processable. Polyimides with more 2,2‐bis(3‐amino‐4‐hydroxyphenyl)‐hexafluoropropane exhibited better solubility and a low refractive index, which is highly desired for microelectronic applications. The dielectric constant and birefringence were strongly dependent on the fluorine content. With an increase in the fluorine substitution, both the dielectric constant and birefringence decreased. All the polymers exhibited high thermal stability (>400 °C). The absence of crystalline melting in differential scanning calorimetry and broad wide‐angle X‐ray diffraction patterns revealed the amorphous nature of the polymers, which was due to the presence of bulky CF₃ groups and hinged ether linkages of the diamine component. The residual stress values decreased with an increase in the 4,4′‐oxydianiline content, and the results were in agreement with the dielectric constant. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 4303–4312, 2004